A metal-based graphene oxide antibacterial coating, preparation method and application thereof

An antibacterial coating, metal-based technology, applied in the field of microbial protection, can solve the problems of improving the antibacterial properties of difficult coatings, low graphene oxide content, and inability to prepare coatings, and achieves low cost, good antibacterial effect, and reliability. Good results

Active Publication Date: 2022-05-03
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the large surface area of ​​graphene oxide, it is easy to agglomerate under the action of surface energy. The traditional electrodeposition process can only prepare a small amount of graphene oxide on the coating, and even cannot be prepared on the coating.
Due to the low content of graphene oxide on the surface of the coating obtained by the traditional electrodeposition process, it is difficult to improve the antibacterial performance of the coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A metal-based graphene oxide antibacterial coating, preparation method and application thereof
  • A metal-based graphene oxide antibacterial coating, preparation method and application thereof
  • A metal-based graphene oxide antibacterial coating, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Implementation example 1 A kind of preparation method of nickel-based graphene oxide antibacterial coating:

[0037] Such as figure 1 Shown, a kind of preparation method of graphene oxide antibacterial coating is realized through the following steps:

[0038] Step 1. Select 304 stainless steel as the cathode substrate, and wash it with acetone, absolute ethanol, and distilled water for 15 minutes in sequence, and the whole cleaning process is in a 40 kHz ultrasonic environment.

[0039] Step 2. Disperse 0.5 g of few-layer graphene oxide powder and 0.05 g of sodium lauryl sulfate in 100 mL of distilled water, and ultrasonically treat for 30 min.

[0040] Step 3. Take 4g of nickel particle powder with an average particle size of 30 μm and disperse it into 2000mL Watts nickel plating solution, and treat it with ultrasonic oscillation for 30 minutes.

[0041] Step 4. Mix the graphene oxide dispersion in step 2 with the electroplating solution obtained in step 3 at a ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The field of microbial protection of the present invention relates to an electrodeposition processing technology, specifically a method for preparing a metal-based graphene oxide antibacterial coating based on magnetic field-assisted scanning spray electrodeposition. The metal ion plating solution of graphene oxide is used as the raw material, and it is formed at one time by using the magnetic field-assisted spray electrodeposition technology; the antibacterial rate of the coating against E. The above; the antibacterial coating provided by the present invention does not need to be modified by adding an antibacterial agent, and has the reliability of the metal coating. The antibacterial coating prepared by this method has potential application space in the fields of public health and engineering protection.

Description

technical field [0001] The invention belongs to the field of microbial protection and relates to an electrodeposition processing technology, in particular to a method for preparing a metal-based graphene oxide antibacterial coating based on magnetic field-assisted scanning spray electrodeposition. Background technique [0002] In the natural environment, the existence of a large number of pathogenic bacteria has brought huge safety hazards to human survival, especially the development pattern of super-urbanization has further increased the urban population density, and put forward higher requirements for the field of public health. Therefore, an ideal long-term and reliable antibacterial coating can be used as an antibacterial surface for public facilities to ensure the safety of human public health. [0003] Electroplating layer is a common material for metal surface coating, mainly prepared by electrochemical deposition method. As a traditional antibacterial material, met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25D15/00C25D5/08C25D5/56C25D5/54C25D5/34C25D5/36
CPCC25D15/00C25D5/08C25D5/56C25D5/54C25D5/34C25D5/36C25D5/007C25D5/009
Inventor 沈理达娄桂宾陈亚钱莺娟焦晨成海霞
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap