Energy-saving foamed polypropylene bead and molded part thereof

A foamed polypropylene and polypropylene technology, applied in the field of foamed polypropylene, can solve the problems of high molding energy consumption of EPP beads, low compression resistance, poor apparent quality of parts, etc., and achieve excellent cell uniformity , Promote mold expansion, excellent appearance quality effect

Inactive Publication Date: 2022-01-21
WUXI HI TEC ENVIRONMENTAL MATERIAL CO LTD
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The inherent melting characteristics of EPP beads lead to the need for high steam pressure to achieve firm sintering during steam molding. Especially compared to the molding process of EPS, the high molding energy consumption of EPP beads is an obstacle to its further development. factors for development
[0004] Chinese invention patent CN101679662A uses polypropylene materials with a melting point of 115-135°C to obtain foamed polypropylene beads with a molding pressure lower than 0.18 MPa and molded products thereof; the inventors have repeatedly verified experiments and found that the products of this technology have anti-corrosion properties. Risk defect of low compression performance (soft hand feeling)
Chinese invention patent CN112457596A has obtained energy-saving foamed beads coated with low-melting point polyolefin and high-melting point polypropylene. The molding pressure is lower than 2.2bar, but there is poor sintering in the EPS molding machine mold (molding pressure is lower than 1.6bar). and the risk of poor apparent quality of the part

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Energy-saving foamed polypropylene bead and molded part thereof
  • Energy-saving foamed polypropylene bead and molded part thereof
  • Energy-saving foamed polypropylene bead and molded part thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] The preparation method of expanded polypropylene beads is:

[0038] (1) After mixing polypropylene A, polypropylene B, polypropylene C, expansion aid, cell nucleating agent, and maleic anhydride modified polypropylene in a certain proportion, twin-screw extrusion granulation is used to obtain the core layer masterbatch ;

[0039] (2) After polyolefin D and other additives are uniformly mixed in a certain proportion, twin-screw extrusion granulation is used to obtain a cortex masterbatch;

[0040] (3) Add the core layer masterbatch and the cortex layer masterbatch to the core layer extruder and the cortex extruder of the double-single-screw co-extrusion unit respectively, and after plasticizing, the silk is granulated through the co-extrusion die at the same time to obtain the cortex layer. Composite particles in the core layer;

[0041] (4) Add the composite particles together with the dispersant and water into the autoclave, and add CO after sealing 2 , keep stirrin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of foamed polypropylene, and particularly relates to an energy-saving foamed polypropylene bead and a molded part thereof. The foamed polypropylene bead is prepared from composite particles through a high-temperature and high-pressure kettle type foaming method, and the composite particles comprise a core layer and a skin layer; the core layer is prepared from the following components in percentage by mass: 40 to 60 percent of polypropylene A, 20 to 40 percent of polypropylene B, 15 to 30 percent of polypropylene C, 0.05 to 2 percent of expanding aid, 0.05 to 0.5 percent of cell nucleating agent and 0.5 to 3 percent of maleic anhydride modified polypropylene; and the skin layer comprises the following components in percentage by mass: 90-100% of polyolefin D and 0-10% of other auxiliaries. The composite particle has a structure that the core layer is coated with the skin layer, and the skin layer matrix resin is low in melting point, easy to sinter and good in compatibility with the main base material resin used by the core layer; and the core layer resin adopts a specially selected mixture, and the expanding aid further promotes the molding expansibility, so that the EPP beads have more excellent molding expansion under the molding pressure of 1.4 bar, and the excellent apparent quality of a molded part is reflected while firm sintering is realized.

Description

technical field [0001] The invention belongs to the technical field of expanded polypropylene, and in particular relates to energy-saving expanded polypropylene beads and molded parts thereof. Background technique [0002] The expanded polypropylene beads (EPP) and its molded products produced by the kettle method have excellent resilience, better high temperature resistance (understood to be used at higher temperatures), and the production process is clean and pollution-free. It is a PU foam , EPS and EPE are ideal substitutes. At present, EPP has been widely used in the fields of thermal insulation, cushioning packaging and automobile lightweight. [0003] The inherent melting characteristics of EPP beads lead to the need for high steam pressure to achieve firm sintering during steam molding. Especially compared to the molding process of EPS, the high molding energy consumption of EPP beads is an obstacle to its further development. factors for development and promotion. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/16C08J9/34C08L23/12C08L23/08C08K3/30
CPCC08J9/16C08J9/34C08J9/0066C08J2323/12C08J2423/08C08J9/232C08J9/122C08J9/18C08J9/0095C08J9/0061C08J2423/12C08J2427/18C08J2203/06C08J9/228
Inventor 熊业志曾佳蒋璠晖朱民何若虚刘缓缓杨亮炯史亚杰宋新意
Owner WUXI HI TEC ENVIRONMENTAL MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products