Process for preparing water-soluble styrenelacrylic resins by continuous bulk polymerization

A technology of bulk polymerization and styrene, applied in the field of preparing water-soluble styrene/acrylic resin by continuous bulk polymerization

Inactive Publication Date: 2002-01-16
HANWHA CHEMICAL CORPORATION
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

All of these have not ye

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing water-soluble styrenelacrylic resins by continuous bulk polymerization
  • Process for preparing water-soluble styrenelacrylic resins by continuous bulk polymerization

Examples

Experimental program
Comparison scheme
Effect test

Embodiment I-V

[0034] Styrene monomers (styrene and α-methylstyrene) and acrylic acid monomers (acrylic acid) were charged to a continuously stirred, temperature-controlled reactor externally equipped with an oil jacket containing a cooling coil, as listed in Table 1 below. Shown to prepare water-soluble styrene / acrylic resin.

[0035] Polymerization was initiated in the presence of t-butylperoxybenzoate. The polymerization initiator is used in an amount of 3.5 parts by weight, based on the total weight of the monomer mixture. For the polymerization, 15 parts by weight of a mixed solvent of dipropylene glycol methyl ether and water having a water content of 35% by weight were used, based on 100 parts by weight of the monomer mixture. Polymerization was carried out under different temperature conditions ranging from 150 to 220°C. The polymerized resin passes through the falling strand type exhaust section, from which the volatile components are removed. At the same time, the exhaust sectio...

Embodiment VI-IX

[0043] In order to investigate the effect of the operating conditions of the vent section on the physical properties of the resin, the polymerization was carried out in the same manner as in Example IV, but under the temperature and pressure conditions of the vent section shown in Table 3 below. The results are shown in Table 3.

[0044] Example number

Embodiment X-XIII

[0050] A water-soluble styrene / acrylic resin was prepared in a manner similar to Example IV, except that the amount and water content of the mixed solvent of dipropylene glycol methyl ether and water were changed, as shown in Table 5 below.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a bulk polymerization process for preparing water-soluble styrene/acrylic resins, in which styrene and acryl monomers are polymerized in a solvent mixture of dipropylene glycol methyl ether and water in a temperature-controllable reactor equipped externally with an oil jacket containing a cooling coil therein and the resulting polymers are deprived of volatile contents in a falling-strand type devolatilizer. The water-soluble styrene/acrylic resins take industrial advantages over conventional resins because the resins, if polymerized at lower temperatures, show lower molecular weights, narrower molecular weight distributions, higher acid values and lower volatile content.

Description

technical field [0001] The invention relates to a method for preparing water-soluble styrene / acrylic resin by continuous bulk polymerization. More specifically, the present invention relates to a process for preparing low molecular weight polymers of narrow molecular weight distribution, high acid number and low volatile content by continuous bulk polymerization. technical background [0002] Most inks, paints and coatings in use today use organic solvents. This is because when inks, paints, and coatings are used, the organic materials of organic solvents evaporate, and they are now found to cause serious air pollution. In addition, organic solvents have a high potential to cause fires due to their flammability. [0003] As an alternative to avoid these problems, high solids liquid coatings based on water-soluble styrene / acrylic resins have been proposed. In fact, these high-solids liquid coatings are good in terms of not causing atmospheric pollution. Contrary to organi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F2/01C08F2/02C08F2/10C08F2/44C08F6/10C08F212/08C08F257/02
CPCC08F212/08C08F2/02
Inventor 陈永燮河炫在吴锡宪元浩渊
Owner HANWHA CHEMICAL CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap