Ferritic stainless steel for use in high temperature applications and method for producing a foil of the steel

A stainless steel, ferrite technology, applied in separation methods, chemical instruments and methods, layered products, etc., can solve problems such as high temperature fatigue strength increase

Inactive Publication Date: 2005-03-23
SANDVIK INTELLECTUAL PROPERTY AB
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The trend towards thinner thicknesses for metal catalytic converter steel foils creates several issues, one being the need for better oxidation per...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ferritic stainless steel for use in high temperature applications and method for producing a foil of the steel
  • Ferritic stainless steel for use in high temperature applications and method for producing a foil of the steel
  • Ferritic stainless steel for use in high temperature applications and method for producing a foil of the steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] These objects of the invention are achieved by an alloy having the following composition (all contents in weight %):

[0023] C≤0.05

[0024] Cr 16.0-24.0%

[0025] Ni greater than 1.0-15.0%

[0026] Al 4.5-12.0%

[0027] Mo+W ≤4.0%

[0028] Mn≤1.0%

[0029] Si ≤2.0%

[0030] Zr+Hf ≤0.1%

[0031] REM≤0.1%

[0032] N≤0.05%

[0033] The rest is Fe and the usual steelmaking impurities and additives.

[0034] The Cr content should be limited to 16.0-24.0% by weight, preferably 20.0-22.0% by weight. The Ni content should be limited to greater than 1.0-15.0 wt%, preferably 2.5-15.0 wt%, most preferably 5.0-12.5 wt%. The aluminum content should be limited to 4.5-12.0% by weight, preferably 5.0-8.0% by weight, most preferably 5.0-7.0% by weight. The total content of Mo and W elements should be limited to a maximum of 4.0% by weight, preferably a maximum of 3.0% by weight. The Mn content...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Hardnessaaaaaaaaaa
Login to view more

Abstract

The present invention relates to the use of a hot workable ferritic stainless steel alloy resistant to thermal cyclic stress and oxidation at elevated temperatures and having improved mechanical properties as substrate for exhaust gas purifying applications, such as catalytic converters or heating applications and having the following composition (in weight-%): C <=0,05%, Cr 16,0-24,0%, Ni more than 1,0-15,0%, Al 4,5-12,0%, Mo+W <=4,0%, Mn <=1,0%, Si <=2,0%, Zr+Hf <=0,1%, REM <=0,1%, N <=0,05% balance Fe and normally occurring steelmaking impurities and additions.

Description

[0001] The present invention relates to a thermally operable ferritic stainless steel alloy resistant to thermal cycling stress and oxidation at high temperatures and having improved mechanical properties for use as a substrate in exhaust gas purification applications such as catalytic converters and heating applications. Background of the Invention [0002] Ferritic Fe—Cr—Al alloy foils are used today as carrier material for catalytic converters for purifying exhaust gases from internal combustion engines. The greatest advantage of this alloy lies in the formation of a thin bonded aluminum oxide film on the surface which keeps the metal stable at the service temperature of the catalytic converter and under the cyclical thermal stresses which are common operating conditions in this application. Avoid rapid oxidation. In order to form such a protective oxide, it is speculated that a minimum aluminum content of 4.5% in the alloy is necessary. [0003] It is known to improve if ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F01N3/10B01D53/86B32B15/01C22C38/00C22C38/06C22C38/44C22C38/50
CPCB32B15/012C22C38/06C22C38/44C22C38/005
Inventor 马格努斯·塞德格伦肯尼斯·戈兰松
Owner SANDVIK INTELLECTUAL PROPERTY AB
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap