An Al-Ti-Nb intermediate alloy and process for preparing same

A master alloy, aluminum-titanium technology, applied in the field of aluminum-titanium-niobium master alloy and its preparation, can solve the problems of unsatisfactory diversification, high cost, narrow adaptability, etc., and achieve easy storage and transportation, low cost and low production cost Effect

Inactive Publication Date: 2005-06-22
张忠士
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

An existing aluminum-titanium rare earth compound master alloy smelted with titanium alloy (patent application number 94112628.5) has good oxidation resistance, but its cost is high and its adaptability is narrow (used for pure rare earth type titanium alloy smelting), which cannot meet the diversified requirements of modern titanium alloy production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The method of smelting by ignition outside the furnace is carried out according to the conventional steps, the raw materials are dried, the furnace is built, the ingredients are prepared according to the weight percentage, the materials are evenly mixed, the furnace is loaded, smelted, cooled, the furnace is started, weighing, finishing, crushing, magnetic Selection, sampling analysis, packaging.

[0017] Concrete preparation process is as follows:

[0018] 1. Drying of raw materials: drying raw materials, masonry slag and batching slag in a drying room at a temperature of 75°C (can be 75±5°C) for 24 hours (can be 24 to 72 hours);

[0019] 2. Weighing raw materials: Potassium chlorate is used as a catalyst during batching (adding weight is 2-10% of the total amount of raw materials)

[0020] Nb 2 o 5 TiO 2 Al CaF 2 KcO 3

[0021] 1kg 0.44kg 0.115kg 0.05kg 0.093kg

[0022] 3. Mixing: put the material into the V-shaped mixer, mix evenly, and the number of...

Embodiment 2～5

[0034] Embodiment 2~5. Operate according to the method of embodiment 1, see table 1 with embodiment 1 difference.

[0035] production process

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to the preparation of titanium alloy, more specifically an Al-Ti-Nb intermediate alloy for titanium alloy preparation and process for preparing the same, wherein the constituents (by weight percent) of the alloy include, Al 2-10%, Si 3-30%, and balancing Nb. The preparing process comprises, employing furnace outside ignition smelting method, operating according to routine procedures, the raw material drying temperature being 70-80 deg. C, the drying time no less than 24 hours, calculated based on 1kg of Nb2O5, the charged mixture includes, TiO2 0.25-0.66kg, Al 0.115-0.46kg, CaF2 0.05-0.10kg, KclO3 0.07-0.12 kg, the raw material shoving temperature being 30-60 deg. C. The advantages of the invention include facilitated preparation of titanium alloy, low making cost, homogeneous alloying, good oxidation resistance, easy storing, transport and fragmenting.

Description

technical field [0001] The invention relates to the preparation of titanium alloys, in particular to an aluminum-titanium-niobium (niobium-based) master alloy used for the preparation of titanium alloys and a preparation method thereof. Background technique [0002] With the continuous development of titanium alloys, it is more and more necessary for the master alloy to be directly added to titanium for smelting, which avoids the cumbersomeness of simply adding metal elements separately, and the melting point of the niobium-based master alloy is lower than the highest melting point of each metal element; The melting point of AlTiNb alloy is 2018°C, while the melting point of Nb is 2468°C, which makes the preparation and smelting process of titanium alloy stable, and avoids the phenomenon that the melting current applied fluctuates and is not easy to control due to inconsistent melting points of metal elements. An existing aluminum-titanium rare earth compound master alloy sm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/03C22C27/02
Inventor 张忠士郭淑君田福礼
Owner 张忠士
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap