Phase retarder, a laminate polarizing plate, a method for producing thereof, and a liquid crystal display

A technology of phase retarder and polarizing plate, which is applied in polarizing components, instruments, layered products, etc.

Inactive Publication Date: 2005-12-28
SUMITOMO CHEM CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The inventors of the present invention intensively studied to solve such problems, and found that these problems can be solved by using a special resin as a binder for a phase retarder composed of a coating layer containing an organically modified clay compound constitution, the present inventors have thus completed the present invention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phase retarder, a laminate polarizing plate, a method for producing thereof, and a liquid crystal display
  • Phase retarder, a laminate polarizing plate, a method for producing thereof, and a liquid crystal display
  • Phase retarder, a laminate polarizing plate, a method for producing thereof, and a liquid crystal display

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0131] (a) Production of coated phase retarders

[0132] Coating solutions having the following compositions were prepared.

[0133]Polyurethane resin varnish "SUB Lacquer 0866" 10%

[0134] Organic modified clay compound "Lucentite STN" 9%

[0135] Toluene 81%

[0136] The solid content concentration of the coating solution is 12%, and the solid content weight ratio of the organically modified clay composite to the polyurethane resin is 3 / 1. The prepared coating solution was coated with an applicator on a polyethylene terephthalate film having a thickness of 38 μm and subjected to release treatment (the water contact angle of the surface treated with the release agent was 110°) , followed by drying at 50° C. for 1 minute and then at 90° C. for an additional 3 minutes to obtain a phase retarder coated on the film. Measure the phase retardation value of the coating, and the measurement result is R 0 = 0.2 nm, R' = 94 nm. The haze of the phase retarder coated on the glass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
turbidityaaaaaaaaaa
Login to View More

Abstract

A phase retarder comprising a film comprising a mixture comprising an organomodified clay composite and an aliphatic diisocyanate-containing urethane resin, wherein the weight ratio of the former to the latter is greater than 2 to less than 5.

Description

technical field [0001] The present invention relates to a phase retarder and a laminated polarizing plate using the phase retarder, methods of producing both, and a liquid crystal display including the phase retarder. Background technique [0002] Liquid crystal displays have properties of low power consumption, low driving voltage, light weight, and flat panels, and have rapidly spread to devices for displaying information such as displays for portable phones, handheld terminals, computers, and televisions. Due to the development of liquid crystal element technology, various modes of liquid crystal displays have been developed, and efforts have been made to solve the problems of liquid crystal displays related to response rate, contrast ratio, and narrow viewing angle. However, liquid crystal displays still have a problem of narrow viewing angles compared with cathode ray tubes (CRTs); therefore, various efforts have been made to widen their viewing angles. [0003] As a l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B5/30G02F1/1335G02F1/13363
CPCG02B5/3083G02F1/133634B32B7/12B32B2307/42G02F1/133753