Low temperature rapid phosphorization liquid for drawing wire and phosphorization process

A phosphating liquid, low temperature technology, applied in the direction of metal material coating process, etc., can solve the problem of poor surface lubrication in the welding area, and achieve the effect of good effect, low phosphating temperature and simple operation.

Inactive Publication Date: 2008-01-16
SOUTHEAST UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the defect of poor surface lubrication of the welding zone after the high-carbon wire rod butt welding operation in the prior art, the present invention provides a low-temperature rapid phosphating solution for wire drawing and a phosphating process suitable for large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low temperature rapid phosphorization liquid for drawing wire and phosphorization process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A low-temperature rapid phosphating solution for wire drawing in the metal product industry, including Zn(H 2 PO4) 2 , Zn(NO 3 ) 2 、H 3 PO 4 and H 2 O, its mass proportion is: (60~100): (15~40): (8~50): (808~912), in the present embodiment, its mass proportion can select following any one, 60 :15:50:808, 100:40:8:912, 72:28:34:846, 85:30:41:862, 90:35:45:900.

Embodiment 2

[0025] A low-temperature rapid phosphating solution for wire drawing in the metal product industry, including Zn(H 2 PO4) 2 , Zn(NO 3 ) 2 、H 3 PO 4 and H 2 O, its mass proportion is: (60~100): (15~40): (8~50): (808~912), present embodiment also comprises Ni(NO 3 ) 2 , Zn(H 2 PO4) 2 with Ni(NO 3 ) 2 The mass ratio is: (60 ~ 100): (0.5 ~ 1.0), the above-mentioned Zn (H 2 PO4) 2 , Zn(NO 3 ) 2 、H 3 PO 4 、H 2 O and Ni(NO 3 ) 2 The mass ratio can choose any of the following, 60:15:8:808:0.5, 100:40:50:912:1, 75:20:35:850:0.45, 83:33:45:860:0.28 , 95:37:43:890:0.18.

Embodiment 3

[0027] A low-temperature rapid phosphating solution for wire drawing in the metal product industry, composed of Zn(H 2 PO4) 2 , Zn(NO 3 ) 2 、H 3 PO 4 , Ni(NO 3 ) 2 , La(NO 3 ) 3 and H 2 O composition, its mass ratio is: (60~100): (15~40): (8~50): (0.5~1.0): (0.5~1.0): (808~912), in this embodiment , its mass ratio can choose any one of the following, 60:15:8:0.5:0.5:808, 100:40:50:1.0:1.0:912, 66:22:30:0.6:0.7:840, 88: 37:43:0.7:0.65:870, 94:34:46:0.82:0.91:905.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
film densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-temperature rapidly phosphatising liquid in wiredrawing of metallic production trade, which comprises Zn (H2PO4), Zn (NO3)2, H3PO4 and H2O, wherein the mass ratio is: (60-100):(15-40):(8-50):(808-912). The phosphatising art is: rubbing out the oxide skin in the surface of the welding point of the rod bundle through the fine grinding wheel, sanding it again, spraying said liquid evenly on the welding surface, weathering the remaining liquid and repeating again.

Description

technical field [0001] The invention relates to a low-temperature rapid phosphating solution and a phosphating process for surface drawing of steel wire rods in the metal product industry. Background technique [0002] Due to its deformability, zinc-based phosphating film is often used for surface lubrication treatment during machining. Traditionally, it is generally prepared by medium and high temperature soaking process, and the formed phosphating film is thick (5-15g / m 2 ) and relatively dense, with good lubricating properties. [0003] As a new generation of building materials, prestressed (PC) steel strands for high-strength concrete are widely used in modern buildings such as high-rise buildings and long-span bridges. Its general production process is that the cold-controlled hot-rolled high-carbon wire rod is processed by high-temperature surface phosphating, then continuous multi-pass wire drawing production, and then twisted and stabilized. [0004] Due to the hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/07C23C22/78
Inventor 蒋建清方峰于金董岩顾菡妍曹文奎
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com