4A zeolite synthesized from kaolin by low-temperature alkali fusion method

A kaolin, alkali fusion technology, applied in the direction of A-type crystalline aluminosilicate zeolite, crystalline aluminosilicate zeolite, etc., can solve the problems of high cost, complicated process and the like, and achieve low cost, simplified process flow and fast exchange speed. Effect

Inactive Publication Date: 2007-09-12
ZHEJIANG NORMAL UNIVERSITY
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a kind of abundant and easy-to-obtain kaolin for the deficiencies of high cost and cumbersome process in the existing chemical synthesis method, acidified bentonite method and kaolin high-temperature calcination method of producing 4A zeolite. Raw material, preparation method of synthetic 4A zeolite with simple production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 4A zeolite synthesized from kaolin by low-temperature alkali fusion method
  • 4A zeolite synthesized from kaolin by low-temperature alkali fusion method
  • 4A zeolite synthesized from kaolin by low-temperature alkali fusion method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Mix 25.8 g of kaolin and 24.0 g evenly, add 30 ml of water to make the mixture thick, roast at 200 ° C for 2 hours, pour it into a flask after cooling, and heat for 1 hour, 20.4 g of active aluminum oxide and 24 g of active silicon dioxide Mix evenly, add evenly within 1 hour, add 162ml of water, stir and crystallize for 1 hour. Heating on a water bath at a constant temperature of 95°C for 3 hours, suction filtration, and then drying at 110°C for 2 hours to obtain 4A zeolite product. The product has been detected by "X-ray diffraction analysis", and its content is more than 96%, and its calcium exchange rate is about 310mg CaCO 3 / g, all physical and chemical indicators have reached or exceeded the national standard.

Embodiment 2

[0027] Mix 25.8 g of kaolin and 25.6 g evenly, and add 50 ml of water to make the mixture thick, roast at 250 ° C for 2 hours, pour into a flask after cooling, mix 20.4 g of active aluminum oxide and 24 g of active silicon dioxide, Add evenly within 1 hour, add 162ml of water, stir and crystallize for 1 hour. Heating on a water bath at a constant temperature of 90°C for 4 hours, suction filtration, and drying at 105°C for 2 hours to obtain 4A zeolite product. The product has been detected by "X-ray diffraction analysis", and its content is above 98%, and its calcium exchange rate is about 327mg CaCO 3 / g, all physical and chemical indicators have reached or exceeded the national standard.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention relates to a method for preparing 4A zeolite with kaoline as the raw material aiming at providing a preparation method for composite 4A zeolite with kaoline as the raw material against the shortcomings of the present chemosynthesis method, acidified bentonite method and a kaoline high temperature calcining method including the following steps: mixing uniformly kaolin and NaOH in a certain proportion and heating them for 1-3h, adding a certain volume of active Al2O3, active SiO2 and water in the activated product to be thermal-crystalized for 0.5-4h under 80-95deg.C then to filter the product and dry it to get the 4A zeolite product.

Description

technical field [0001] The invention relates to a method for preparing 4A zeolite, in particular to a method for synthesizing 4A zeolite with kaolin as raw material. Background technique [0002] The composition of 4A zeolite is Na 12 Al 12 Si 12 o 48 27H 2 O belongs to the cubic crystal system, and the free diameter of the hole formed by its eight-ring structure is 4.12_, and the characteristic is that the Ca 2+ 、H 2 O and other small molecular substances have strong adsorption and exchange capabilities, and are the best substitutes for sodium tripolyphosphate, which has serious pollution to water bodies. Detergents with 4A zeolite as auxiliary agent have no phosphorus, no pollution, no residue, and strong decontamination ability. They are widely used in the detergent industry. At the same time, they are also widely used in petroleum cracking and adsorbent industries. At present, there are three methods for producing 4A zeolite, chemical synthesis method, acidified b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B39/02C01B39/14
Inventor 李小忠陆国华韩伟琴陈爱贞
Owner ZHEJIANG NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com