Composite Zinc Calcium Fluorophosphate Antirust Powder

A technology of composite zinc fluorophosphate and antirust powder, which is applied in anti-corrosion coatings, inorganic pigment treatment, fibrous fillers, etc., can solve problems such as environmental pollution, health hazards, low cost performance of pigments, etc., and achieve convenient use and excellent performance Effect

Inactive Publication Date: 2012-02-01
武汉市大汉科技发展有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the pollution of the environment caused by heavy metals, it is also harmful to the health of front-line production workers. These pigments are not cost-effective and do not meet the needs of the current industrial production development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Get fineness and be 95.99kg of the processed carrier of 800 purposes, compound into superfine zinc powder 3.0kg, calcium-based nano-powder 1.0kg and fluorosurfactant 0.01kg, obtain composite zinc calcium fluorophosphate antirust powder product 100kg.

Embodiment 2

[0015] Get fineness and be 95.98kg of the processed carrier of 800 purposes, compound into superfine zinc powder 2.0kg, calcium-based nano-powder 2.0kg and fluorosurfactant 0.02kg, obtain composite fluorophosphate zinc calcium antirust powder product 100kg.

Embodiment 3

[0017] Get fineness and be 94.95kg of the processed carrier of 800 purposes, compound into superfine zinc powder 3.0kg, calcium-based nano-powder 2.0kg and fluorosurfactant 0.05kg, obtain composite fluorophosphate zinc calcium antirust powder product 100kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A composite zinc-calcium fluorophosphate antirust powder, characterized in that: a mixture of zinc phosphate and calcium phosphate is the remainder, 800-1200 mesh ultra-fine zinc powder accounts for 0.3-20% of the total weight of the anti-rust powder; the nano-calcium oxide used The powder material accounts for 0.5-25% of the total weight of the antirust powder; the fluorine surfactant accounts for 0.1‰~5‰ of the total weight of the antirust powder. Its advantages are: the strongest anti-rust ability, the most stable performance, environmental protection, high cost performance, wide adaptability, suitable for all kinds of solvent-based paints, easy to use, no sedimentation, no delamination, no floating color, can prepare various kinds of paint. It can be used to make all-environmental water-based anti-rust paint with excellent performance. The salt water resistance test lasts for more than 20 days. It is suitable for steel surface, also suitable for other non-ferrous metal surface and non-metal surface anticorrosion paint.

Description

technical field [0001] The invention relates to an antirust pigment for coatings, in particular to an antirust pigment-composite zinc calcium fluorophosphate antirust powder for improving the antirust ability of the antirust paint. Background technique [0002] Anti-rust paint is an economical anti-rust material that must be used for steel components, and anti-rust paint must have anti-rust pigments with anti-rust function. Traditional antirust pigments include red lead powder, iron red powder, aluminum tripolyphosphate powder, zinc phosphate, and chromate. Some of the above antirust pigments contain heavy metals, and some do not contain heavy metals. Due to the heavy metal content, it will pollute the environment and cause harm to the health of front-line production workers. These pigments are not cost-effective and do not meet the needs of the current industrial production development. Contents of the invention [0003] The purpose of the invention is to research a comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D7/12C09C1/04C09C3/00C09D5/08
Inventor 朱志学金俊平金广泉李训生龙光斗
Owner 武汉市大汉科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products