Interface additive for improving interface bond strength of polyurethane pellicle and organic glass

A technology of interface treatment agent and polyurethane, which is applied in the field of manufacturing laminated glass and other transparent parts, can solve the problems of less interface treatment agent and no literature records, etc., and achieve the improvement of interface bonding strength, compatibility, and bonding strength Effect

Active Publication Date: 2010-11-24
CHINA BUILDING MATERIALS ACAD +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are relatively few reports on interface treatment agents for heterogeneous transparent materials such as organic-inorganic composite materials, and there is no literature record

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Interface additive for improving interface bond strength of polyurethane pellicle and organic glass
  • Interface additive for improving interface bond strength of polyurethane pellicle and organic glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an interface finishing agent used for improving adhesion strength of polyurethane film and organic glass interface. Transparent solution of the polyurethane is obtained by dissolving the polyurethane film in certain solvent, long molecular chains of acrylic acid polymer are obtained by polymerization of acrylic acid homologues started in the solution and graft or interpenetrating polymer network system of the two is formed by controlling the reaction condition. When in use, the network system is compatible with PU and PMMA respectively to form a transition bridge between the PU and the PMMA, thereby improving the compatibility of the two interfaces and interface adhesion strength, however, transmittance of the raw base material can not be reduced and side effect towards organic materials dose not exist. Adhesion strength of the polyurethane film and organic glass interface can be improved about 40 percent after the finishing agent is applied.

Description

An interface treatment agent for improving the bond strength of polyurethane film and plexiglass interface technical field The invention relates to an interface treatment agent for bonding heterogeneous transparent materials, which can be used for manufacturing laminated glass and other transparent parts. Background technique In the compounding process of heterogeneous transparent materials, such as the compounding of inorganic glass and organic glass (PMMA, polymethyl methacrylate), polyurethane (PU) film thermal compounding technology is now used. That is, under high temperature and high pressure, polyurethane film is used as a bonding material, and the process of spreading and infiltrating on the surface of inorganic glass and organic glass respectively occurs, and finally the two are combined into a whole. Since the linear expansion coefficients of inorganic glass and oriented organic glass differ by nearly an order of magnitude (8.6×10-6°C-1 and 7.15×10-5°C-1 respecti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J5/02C08J5/12C08L75/04
Inventor 欧迎春冯海兵蓝知惟张保军左岩马眷荣
Owner CHINA BUILDING MATERIALS ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com