Polyformaldehyde composition and preparation method thereof

A polyoxymethylene composition and a technology for uniform mixing, applied in the field of polyoxymethylene composition and its preparation, can solve the problem that the tensile strength, flexural strength, flexural modulus, heat resistance and other properties are greatly reduced, and the polarity of the POM molecular chain is weak. , limiting the application of POM in the market, etc., to achieve the effect of simple preparation process, stable size and good impact resistance

Inactive Publication Date: 2008-03-19
SHENZHEN KEJU NEW MATERIAL
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the polarity of the POM molecular chain is weak, there are no side groups, and it is poorly compatible with most polymers, and there are few polymers that can toughen POM.
Most of the existing POM toughening is to blend thermoplastic polyurethane elastomer (TPU) with POM to form hydrogen bonds. The two have cer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0032] Example 1:

[0033] The weight ratio of POM 23%, ABS 74%, compatibilizer 2.2%, lubricant 0.4%, 168 0.2%, 1076 0.2% are mixed uniformly in the mixer; put the mixed raw materials into the twin screw extruder The feeding hopper is melted, extruded, pelletized, fully plasticized, melted, compounded, extruded, stretched, cooled, pelletized, dried and packaged; the processing technology is as follows: Twin-screw extruder, zone 160- 170℃, zone two 160-180℃, zone three 160-180℃, zone four 170-190℃, zone five 170-190℃, zone six 160-180℃, zone seven 160-170℃, zone eight 160-170 ℃; The number of screw revolutions is controlled at 200-500 revolutions per minute; the residence time is 2-6 minutes.

Example Embodiment

[0034] Example 2:

[0035] The weight ratio of POM 35%, ABS 60%, compatibilizer 4.2%, lubricant 0.4%, 168 0.2%, 1076 0.2% are mixed uniformly in the mixer; put the mixed raw materials into the twin-screw extruder The feeding hopper is melted, extruded, pelletized, fully plasticized, melted, compounded, extruded, stretched, cooled, pelletized, dried and packaged; the processing technology is as follows: Twin-screw extruder, zone 160- 170℃, zone two 160-180℃, zone three 160-180℃, zone four 170-190℃, zone five 170-190℃, zone six 160-180℃, zone seven 160-170℃, zone eight 160-170 ℃; The number of screw revolutions is controlled at 200-500 revolutions per minute; the residence time is 2-6 minutes.

Example Embodiment

[0036] Example 3:

[0037] The weight ratio of POM 60%, ABS 35%, compatibilizer 4.2%, lubricant 0.6%, 168 0.2%, 1076 0.2% are mixed uniformly in the mixer; put the mixed raw materials into the twin-screw extruder The feeding hopper is melted, extruded, pelletized, fully plasticized, melted, compounded, extruded, stretched, cooled, pelletized, dried and packaged; the processing technology is as follows: Twin-screw extruder, zone 160- 170℃, zone two 160-180℃, zone three 160-180℃, zone four 170-190℃, zone five 170-190℃, zone six 160-180℃, zone seven 160-170℃, zone eight 160-170 ℃; The number of screw revolutions is controlled at 200-500 revolutions per minute; the residence time is 2-6 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyoxymethylene composition and a method for preparing the same, wherein the composition includes 20-95 percent of POM, 4-80 percent of ABS, 0.1-20 percent of compatibilizer, 0.1-1.0 percent of lubricant, and 0.1-1.2 percent of antioxidant in weight proportion ( percent). Compared with conventional TPU toughening POM system, when the POM/ABS system of the invention achieves the same impact property, the mechanical comprehensive property of the invention is obviously better than the conventional TPU toughening POM system, and the heat resistance is greatly improved. The alloy material has simple preparation technology, and has advantages of dimensional stability, good appearance, high flowability, drug resistance and easy processing forming, which can be widely used to manufacture automobile, electronic and electric components. The invention improves the POM impact toughness and greatly enriches the use of polyoxymethylene in automobile, electronic and electric components through blending with the ABS material.

Description

[technical field] [0001] The invention relates to the technical field of polymer materials, in particular to a polyoxymethylene composition and a preparation method thereof. [Background technique] [0002] Polyoxymethylene (POM) molecular chains are alternately arranged by C-0 and twisted into a helical shape. The regular molecular chain conformation makes polyoxymethylene easy to crystallize, and it is easy to form large spherulites during melt processing. The high crystallinity of POM (about 60% to 80%) endows it with high hardness and rigidity. POM has the characteristics of wear resistance, good self-lubrication, and excellent fatigue resistance. Its mechanical properties are close to metal materials, and it is one of the five major engineering plastics. . POM raw materials come from a wide range of sources, and can be processed by injection molding, blow molding, extrusion molding and rotary casting. It is widely used in machinery, automobiles, electronic appliances, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L59/02C08K5/524C08L55/02C08L83/04C08K5/10
Inventor 徐东贺永李茂林
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap