Lubricant composition
A technology for lubricating compositions and phenolic compounds, which are applied in the directions of lubricating compositions, petroleum industry, thickeners, etc., can solve the problems of not prompting long life, insufficient development, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1、2 and comparative example 1~7
[0065] (1) In a grease preparation kettle, 1 / 2 mass of base oil, 10.2 mass % of 12-hydroxystearic acid and 1.0 mass % of calcium sulfonate were blended in the reaction vessel, and heated and dissolved while stirring.
[0066] (2) 2.7% by mass of lithium hydroxide (monohydrate) was dissolved in water, and 2.1% by mass of terephthalic acid was further dissolved. This aqueous solution was added to the grease composition of (1), followed by heating and mixing. After the temperature of the grease composition reached 205° C., it was held for 5 minutes.
[0067] (3) Next, add the remaining base oil, then cool to 80°C at 50°C / 1 hour, as shown in Table 1, add mixed aralkylated diphenylamine, amine compound 1 or amine compound 2, and phenol Phenolic compound 1, Phenolic compound 2 or Phenolic compound 3.
[0068] (4) Further, after naturally cooling to room temperature, finishing treatment (Shishang げ treatment) was performed using a 3-roller device to obtain 9 kinds of grease composi...
Embodiment 3
[0071](1) Heat and dissolve 1 mole of diphenylmethane-4.4'-diisocyanate (MDI) in 2 / 3 of the mass of the base oil to prepare raw material 1.
[0072] (2) In addition, 2 moles of octylamine were stirred and dissolved in the remaining base oil to prepare raw material 2.
[0073] (3) Next, while stirring raw material 1 vigorously at 50 to 60°C in the grease reactor, slowly add raw material 2. Heating was performed while stirring, and after the temperature of the grease composition reached 165° C., it was maintained for 1 hour.
[0074] (4) Then, aralkylated diphenylamine and phenolic compound 1 were added and mixed, and left to cool naturally to room temperature, followed by finishing treatment using a 3-roller device to obtain the grease composition of Example 3.
[0075] (5) The tests of (2) to (4) above were carried out with respect to the grease composition of Example 3. The results are shown in Table 1.
Embodiment 4
[0077] (1) In a grease preparation kettle, 1 / 2 mass of base oil and 15 mass % of lithium 12-hydroxystearate were blended in a heating kettle, and heated and mixed. After the temperature of the grease composition reached 210° C., it was maintained for 5 minutes.
[0078] (2) Next, after adding the remaining base oil, the mixture was cooled to 80° C. at 50° C. / 1 hour, and aralkylated diphenylamine and phenolic compound 1 were added and mixed.
[0079] (4) Further, after naturally cooling to room temperature, finishing treatment was performed using a 3-roller device to obtain the grease composition of Example 4.
[0080] (5) The tests of (2) to (4) above were carried out with respect to the grease composition of Example 4. The results are shown in Table 1.
[0081] [Table 1]
[0082]
[0083] In addition, for the grease compositions of Examples 1 and 2 and Comparative Examples 3 and 6, the above-mentioned bearing life was measured. The grease composition of Example 1 was 5...
PUM
Property | Measurement | Unit |
---|---|---|
flash point | aaaaa | aaaaa |
flash point | aaaaa | aaaaa |
drop melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap