Method for using phosphogypsum in mine goaf consolidated filling

A technology for cemented filling and goaf, which is applied in the field of cemented and filled phosphogypsum in goafs of mines, can solve the problems of not being able to solidify and reach compressive strength within one week, affecting mining efficiency, mining method limitations, etc. The effect of filling cycle, improving mining efficiency, and short curing time

Inactive Publication Date: 2009-05-27
TONGLING CHEM IND GRP
View PDF2 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the filling period is too long, it directly affects the mining efficiency and is limited by the mining method
Chinese patent CN101008316A discloses the phosphogypsum cementation followed by filling mining method and its pulping process. Its limitation is the same as that of the patent CN1821547A. It cannot be solidified within a week and achieve a compressive strength above 1.5MPa.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Use 1 part of cement, 1 part of water-quenched iron (steel) slag, 10 parts of phosphogypsum, and 0.4 part of lime, add water and stir to form a filling slurry with a weight concentration of 55%, and transport the filling slurry to the goaf of the mine. After a few days, it solidified into a high-strength filling body with a compressive strength of 2.31MPa.

Embodiment 2

[0011] Use 1.2 parts of cement, 1.2 parts of water-quenched iron (steel) slag, 14 parts of phosphogypsum, and 0.8 part of lime, add water and stir to form a filling slurry with a weight concentration of 65%, and transport the filling slurry to the goaf of the mine. After a few days, it solidified into a high-strength filling body with a compressive strength of 1.57MPa.

Embodiment 3

[0013] Use 0.8 parts of cement, 0.8 parts of water-quenched iron (steel) slag, 10 parts of phosphogypsum, and 0.6 parts of lime, add water and stir to form a filling slurry with a weight concentration of 60%, and transport the filling slurry to the goaf of the mine. After a few days, it solidified into a high-strength filling body with a compressive strength of 1.53MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for cemented filling of phosphogypsum in a mine goaf. The method mainly comprises the following steps: mixing the following materials in weight ratio: 0.8 to 1.2 percent of cement, 1.2 to 0.8 percent of water quenched iron (steel) slag, 10 to 14 percent of the phosphogypsum, and 0.4 to 0.8 percent of lime; adding water to the mixture and stirring the mixture to form filling slurry with the weight concentration of between 55 and 65 percent; conveying the filling slurry to the mine goaf; and curing the filling slurry to form a high-strength filling material. The method can significantly reduce the curing time of the filling slurry taking the phosphogypsum as the main raw material, is suitable for various mining techniques and the cement filling for various types of mine goafs, and has strong economic and social benefits.

Description

Technical field [0001] The invention belongs to the field of comprehensive utilization of phosphogypsum, and specifically relates to a method for cementing and filling phosphogypsum in mine goafs. Background technique [0002] Phosphogypsum is a waste residue produced in the process of producing phosphoric acid. About 5 to 6 tons of phosphogypsum are discharged for every ton of phosphoric acid produced. my country's annual phosphogypsum output is more than 20 million tons, but its comprehensive utilization rate is only about 25%. . The calcium sulfate dihydrate content in phosphogypsum is generally between 80 and 95%, which is equivalent to the first and second grade natural gypsum. Since it contains a small amount of phosphoric acid, fluosilicate, and sulfuric acid, it is usually acidic and will occupy land. Environmental pollution problems. Although in areas with industrial by-product phosphogypsum, phosphogypsum has been used to replace natural gypsum to produce gypsum b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B18/14
CPCC04B2111/00724C04B28/143Y02W30/91C04B7/00C04B18/142C04B22/064
Inventor 叶丽君施晰昕杨文斌鲁军崔巨东杜娟
Owner TONGLING CHEM IND GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products