Inorfil softening intensifier and preparation thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An inorganic fiber and reinforcing agent technology is applied in the field of inorganic fiber softening and reinforcing agent and its preparation. Strength, the effect of enhancing the binding force
Inactive Publication Date: 2011-05-18
鹤壁洁联新材料科技有限公司
View PDF0 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] However, inorganic mineral fibers are brittle, strong, and short in fiber. After beating and dispersing in the pulping process, they are more likely to break during transportation, and it is difficult to combine with plant fibers. Excessive use will reduce the strength of paper, so it is limited. its widespread use
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0013] 1) Adjustment of molecular weight of polyvinyl alcohol
[0014] First, dissolve polyvinyl alcohol 1788 and water at a mass ratio of 1:10 at 85-90°C to obtain a polyvinyl alcohol solution, and then press H in the polyvinyl alcohol solution 2 o 2 The mass ratio of polyvinyl alcohol 1788 is 1:130 by adding H 2 o 2 , then add H to the mixture 2 o 2 Potassium hydroxide with a mass of 4% was reacted at a temperature of 50° C. for 4 hours;
[0015] 2) Etherification of polyvinyl alcohol
[0016] Take the polyvinyl alcohol treated in step 1) and mix the etherification agent 3-chloro-2-hydroxypropyl-3-methylammonium chloride in a mass ratio of 1:0.4, react at 70°C for 4h, and adjust the pH= 7-8 to obtain an inorganic fiber softening enhancer.
Embodiment 2
[0018] 1) Adjustment of molecular weight of polyvinyl alcohol
[0019] First, dissolve polyvinyl alcohol 1792 and water at a mass ratio of 1:8 at 85-90°C to obtain a polyvinyl alcohol solution, and then press H in the polyvinyl alcohol solution 2 o 2 The mass ratio of polyvinyl alcohol 1792 is 1:110 by adding H 2 o 2 , then add H to the mixture 2 o 2 Potassium hydroxide with a mass of 2% was reacted at a temperature of 55° C. for 3 hours;
[0020] 2) Etherification of polyvinyl alcohol
[0021] Take the polyvinyl alcohol treated in step 1) and mix the etherifying agent glycidyltriethylammonium chloride in a mass ratio of 1:0.1, react at 50°C for 8 hours, adjust pH=7 to 8 to obtain softened inorganic fibers enhancer.
Embodiment 3
[0023] 1) Adjustment of molecular weight of polyvinyl alcohol
[0024] First, dissolve polyvinyl alcohol 1799 and water at a mass ratio of 1:12 at 85-90°C to obtain a polyvinyl alcohol solution, and then press H in the polyvinyl alcohol solution 2 o 2 Add H to the mass ratio of polyvinyl alcohol 1799 at 1:150 2 o 2 , then add H to the mixture 2 o 2 Potassium hydroxide with a mass of 5% was reacted at a temperature of 60° C. for 2 hours;
[0025] 2) Etherification of polyvinyl alcohol
[0026] Take the polyvinyl alcohol treated in step 1) and mix the etherification agent 3-chloro-2-hydroxypropyl-3-methylammonium chloride in a mass ratio of 1:0.6, react at 65°C for 5h, and adjust the pH= 7-8 to obtain an inorganic fiber softening enhancer.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to an inorganic fiber softening reinforcing agent and a preparation method thereof. The method is to lead H2O2, polyvinyl alcohol and potassium hydroxide to react for 2 to 4 hours at a temperature between 50 and 60 DEG C, adds an etherifying agent after the reaction to react for 4 to 8 hours at a temperature between 50 and 70 DEG C, and regulates the pH value of the solution to 7 to 8 so as to obtain the inorganic fiber softening reinforcing agent. The softening reinforcing agent is applicable to various inorganic fiber materials produced by physical or hot melt method, including basalt fibers, aedelforsite fibers, meerschaum fibers, gypsum fibers, flyash fibers and glass fibers. The softening reinforcing agent can improve the softness and strength of inorganic fibers, improve the defect of easy fracture of the inorganic fibers in processes of pulping, dispersing and transporting, change the charge property of the inorganic fiber surface, reinforce the bonding force of the inorganic fibers and plant fibers, and greatly improve application performance of the inorganic fibers in making paper, insulating wool boards and the like by wet method.
Description
technical field [0001] The invention belongs to the field of chemical industry, and in particular relates to an inorganic fiber softening enhancer and a preparation method thereof. Background technique [0002] With the development of my country's economy and the improvement of people's living standards, the demand for various papers is also increasing day by day. The leading raw material for papermaking in the world is wood, and my country is a country with a serious shortage of wood, so a large amount of wood pulp is imported every year to alleviate the contradiction between supply and demand. This situation forces people to seek and develop new papermaking raw materials. Inorganic mineral fiber is a new type of papermaking material between short plant fibers and traditional fillers (calcium carbonate, talcum powder), which includes various inorganic fiber materials produced by physical treatment or hot-melt methods, such as basalt fiber, Wollastonite fiber, fly ash fiber...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More 