Lightweight ceramisite concrete external wallboard and preparation method thereof

A ceramsite concrete and exterior wall panel technology, applied in building materials and other directions, can solve the problems of impact resistance, low flexural load, high water absorption, easy cracking, etc., and achieve large flexural load, long life, and low water absorption. Effect

Inactive Publication Date: 2010-05-12
吴跃平 +1
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of high water absorption, easy cracking, easy deformation, low impact resistance and bending load, and narrow application range of non-load-bearing exterior wall bricks used in current buildings, the present invention invents a kind of ceramsite as aggregate, Ceramsite concrete lightweight exterior wall panel with high-quality cement, sand and other auxiliary materials and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] (1) Material selection: Weigh 35kg of ceramsite, 12kg of cement, 12kg of medium sand, 0.2kg of waterproofing agent, 0.3kg of water reducing agent, and 0.5kg of antifreeze according to the proportion.

[0016] (2) Stirring: put the ingredients weighed in proportion into a mixer, add water and stir for 2-3 minutes;

[0017] (3) Manufacture: place a steel wire mesh sheet at the bottom of the mold, put the mixed concrete into the mold, vibrate with a flat vibrator to vibrate the cement slurry of the concrete, and add benzene board, rock wool, perlite and other insulation materials , and then place a steel mesh sheet on the insulation material, add concrete, and continue to vibrate with a flat vibrator to make it smooth;

[0018] (4) Demoulding: According to the ambient temperature, the cement specifications selected for construction and the demoulding operating procedures, master the appropriate demoulding time for demoulding. At 0-15 degrees, aluminate quick-hardening cem...

Embodiment 2

[0020] (1) Material selection: Weigh 40g of ceramsite, 10kg of cement, 8kg of medium sand, 0.8kg of waterproofing agent, 0.6kg of water reducing agent, and 0.6kg of antifreeze according to the proportion;

[0021] (2) Stirring: put the ingredients weighed in proportion into a mixer, add water and stir for 2-3 minutes;

[0022] (3) Manufacture: place a steel wire mesh sheet at the bottom of the mold, put the mixed concrete into the mold, vibrate with a flat vibrator to vibrate the cement slurry of the concrete, and add benzene board, rock wool, perlite and other insulation materials , and then place a steel mesh sheet on the insulation material, add concrete, and continue to vibrate with a flat vibrator to make it smooth;

[0023] (4) Demoulding: According to the ambient temperature, the cement specifications selected for construction and the demoulding operating procedures, master the appropriate demoulding time for demoulding. At 0-15 degrees, aluminate quick-hardening cemen...

Embodiment 3

[0025] (1) Material selection: Weigh 45g of ceramsite, 7.8kg of cement, 6.6kg of medium sand, 0.18kg of waterproofing agent, 0.12kg of water reducing agent, and 0.3kg of antifreeze according to the proportion;

[0026] (2) Stirring: put the ingredients weighed in proportion into a mixer, add water and stir for 2-3 minutes;

[0027] (3) Manufacture: place a steel wire mesh sheet at the bottom of the mold, put the mixed concrete into the mold, vibrate with a flat vibrator to vibrate the cement slurry of the concrete, and add benzene board, rock wool, perlite and other insulation materials , and then place a steel mesh sheet on the insulation material, add concrete, and continue to vibrate with a flat vibrator to make it smooth;

[0028] (4) Demoulding: According to the ambient temperature, the cement specifications selected for construction and the demoulding operating procedures, master the appropriate demoulding time for demoulding. At 0-15 degrees, aluminate quick-hardening ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a lightweight ceramisite concrete external wallboard and a preparation method thereof. The external wallboard is characterized by comprising the following components in percentage by weight: 58-75% of ceramisite, 13-21% of cement, 11-21% of medium sand, 0.13-0.92% of waterproof agents, 0.098-0.69% of water reducing agents and 0.065-1.15% of anti-freezing agents. The lightweight ceramisite concrete external wallboard solves the problem that the aerated cement bricks, slag and coal ash bricks, coal ash, stone and cement bricks, which are widely used in the non-bearing external walls in the buildings at present, feature high water absorption, easy cracking and dropping of plastering ceramic tiles and stones, low whole structure strength, low anti-impact and anti-kink load and the like, and is suitable for being used in the buildings.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a lightweight concrete exterior wall panel using ceramsite as an aggregate. Background technique [0002] At present, the non-load-bearing exterior walls widely used in construction mainly include steam-filled cement bricks, slag fly ash bricks, and fly ash gravel cement bricks. Gas-filled cement bricks have a high water absorption rate, and the pasted tiles and stones are easy to crack and fall off, and cannot be nailed, drilled, or threaded horizontally and vertically; slag fly ash bricks and fly ash gravel cement bricks have high water absorption rates, are easy to crack, and have low overall structural strength , impact resistance, low bending load. Contents of the invention [0003] In order to solve the problems of high water absorption, easy cracking, easy deformation, low impact resistance and bending load, and narrow application range of non-load-bearing exterior wal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04C2/04C04B28/00C04B14/02
Inventor 吴跃平焦双健
Owner 吴跃平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap