A light-weight concrete exterior wall panel

A technology of lightweight concrete and exterior wall panels, applied in the field of building materials, can solve the problems of impact resistance, low bending load, high water absorption, easy deformation, etc., and achieve the effect of large bending load, low water absorption and long life

Inactive Publication Date: 2017-05-10
顾杨子
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of high water absorption, easy cracking, easy deformation, low impact resistance, low bending load, and poor anti-seismic effect of non-load-bearing exterior wall bricks currently used in buildings, the present invention invents a brick with ceramsite as aggregate , ceramsite powder as auxiliary material ceramsite concrete lightweight exterior wall panel and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] (1) Material selection: Weigh 24 kg of coarse ceramsite (φ0.5-1.0cm), 9 kg of medium ceramsite (φ0.3-0.5cm), 14 kg of ceramsite powder (below φ0.3cm), 12 kg of cement, 0.2 kg of waterproofing agent, 0.3 kg of water reducing agent, and 0.5 kg of antifreeze.

[0014] (2) Stirring: put the ingredients weighed in proportion into a mixer, add water and stir for 2-3 minutes;

[0015] (3) Manufacture: place a steel wire mesh sheet at the bottom of the mold, put the mixed concrete into the mold, vibrate with a flat vibrator, vibrate the cement slurry of the concrete, add benzene board, rock wool, perlite and other insulation materials , and then place a steel mesh sheet on the insulation material, add concrete, and continue to vibrate with a flat vibrator to make it smooth;

[0016] (4) Demolding: According to the ambient temperature, the cement specifications selected for construction and the demoulding operating procedures, master the appropriate demoulding time for demouldi...

Embodiment 2

[0018] (1) Material selection: weighing according to proportion: coarse ceramsite (φ0.5-1.0cm) 28.8 kg, medium ceramsite (φ0.3-0.5cm) 4.8 kg, ceramsite powder (below φ0.3cm) 14.4 kg , cement 10 kg, waterproofing agent 0.8 kg, water reducing agent 0.6 kg, antifreeze 0.6 kg;

[0019] (2) Stirring: put the ingredients weighed in proportion into a mixer, add water and stir for 2-3 minutes;

[0020] (3) Manufacture: place a steel wire mesh sheet at the bottom of the mold, put the mixed concrete into the mold, vibrate with a flat vibrator, vibrate the cement slurry of the concrete, add benzene board, rock wool, perlite and other insulation materials , and then place a steel mesh sheet on the insulation material, add concrete, and continue to vibrate with a flat vibrator to make it smooth;

[0021] (4) Demolding: According to the ambient temperature, the cement specifications selected for construction and the demoulding operating procedures, master the appropriate demoulding time fo...

Embodiment 3

[0023] (1) Material selection: Weigh 28 kg of coarse ceramsite (φ0.5-1.0cm), 10.2 kg of medium ceramsite (φ0.3-0.5cm), 12.8 kg of ceramsite powder (below φ0.3cm), , 8.4 kg of cement, 0.18 kg of waterproofing agent, 0.12 kg of water reducing agent, and 0.3 kg of antifreeze;

[0024] (2) Stirring: put the ingredients weighed in proportion into a mixer, add water and stir for 2-3 minutes;

[0025] (3) Manufacture: Place a steel wire mesh sheet at the bottom of the mold, put the mixed concrete into the mold, vibrate with a flat vibrator to vibrate the cement slurry of the concrete, and add insulation materials such as benzene board, rock wool, perlite, etc. , and then place a steel mesh sheet on the insulation material, add concrete, and continue to vibrate with a flat vibrator to make it smooth;

[0026] (4) Demolding: According to the ambient temperature, the cement specifications selected for construction and the demoulding operating procedures, master the appropriate demouldi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A light-weight concrete exterior wall panel is disclosed. The panel is characterized in that components of the panel include coarse ceramsite (with Phi being 0.5-1.0 cm), middle-size ceramsite (with Phi being 0.3-0.5 cm), ceramsite powder (with Phi being 0.3 cm or below), cement, a waterproof agent, a water reducer and an antifreezing agent; and the components include 34.5-43% of the coarse ceramsite (with Phi being 0.5-1.0 cm), 6.9-17.2% of the middle-size ceramsite (with Phi being 0.3-0.5 cm), 13.8-25.8% of the ceramsite powder (with Phi being 0.3 cm or below), 13-21% of the cement, 0.13-0.92% of the waterproof agent, 0.098-0.69% of the water reducer and 0.065-1.15% of the antifreezing agent. The panel overcomes a problem that aerated cement bricks, slag-fly ash bricks, fly ash-broken stone-cement bricks, and the like which are widely used in nonbearing exterior walls of buildings at present have disadvantages of high water absorption rates, liable cracking and shedding of adhered tiles and stone materials, low overall structural intensity, low shock resistance, low flexural load, and the like, and is suitable for application in buildings.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a lightweight concrete exterior wall panel using ceramsite as an aggregate and ceramsite powder as an auxiliary material. Background technique [0002] At present, the non-load-bearing exterior wall materials widely used in construction mainly include steamed cement bricks, slag fly ash bricks, fly ash gravel cement bricks, etc. Gas-filled cement bricks have a high water absorption rate, and the pasted tiles and stones are easy to crack and fall off, and cannot be nailed, drilled, or threaded horizontally and vertically; slag fly ash bricks and fly ash gravel cement bricks have high water absorption rates, are easy to crack, and have low overall structural strength , low impact resistance and low bending load. Contents of the invention [0003] In order to solve the problems of high water absorption, easy cracking, easy deformation, low impact resistance, low bending load, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B20/00C04B111/40
CPCC04B28/00C04B2111/40
Inventor 顾杨子
Owner 顾杨子
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap