Low-oxygen content submicron cobalt powder and cobalt oxalate precursor and manufacturing method thereof

A technology of micron cobalt powder and a manufacturing method, applied in the field of metallurgy and chemical industry, can solve the problems of low production efficiency and product quality, difficult to operate stably, poor stability, etc., and achieve the effects of easy control, easy stable control and simple reaction.

Active Publication Date: 2010-07-21
GEM CO LTD +1
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] It can be seen from the above table that the Fischer particle size and oxygen content of cobalt powder products produced by domestic enterprises are difficult to be controlled in a low range at the same time; traditional submicron cobalt powder tends to contain oxygen in finer submicron products. Increase, the finer sub-micron powder is very easy to catch fire in the reduction process, resulting in poor stability of the process. Although the process st

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-oxygen content submicron cobalt powder and cobalt oxalate precursor and manufacturing method thereof
  • Low-oxygen content submicron cobalt powder and cobalt oxalate precursor and manufacturing method thereof
  • Low-oxygen content submicron cobalt powder and cobalt oxalate precursor and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Implement CoCO 3 Wet pulp slurry, solid-liquid ratio 1:2; prepare oxalic acid solution with a concentration of 0.8mol / L, by molar ratio n CoCO 3 : n H 2 C 2 o 4 =1:2 ready to mix, preheat the solution to 25°C before the reaction, add H within 15min 2 C 2 o 4 Solution added CoCO 3 In the slurry, stir and react at constant temperature for 3 hours, separate and filter the precipitate from the solution, wash with clean water, dry at 100-150°C for 15-18 hours, grind and crush the dry powder and pass through a 100-mesh sieve to detect the obtained cobalt oxalate precursor The cobalt content in the medium is 32.96%wt, and the bulk density is 0.19g / cm 3 ,D 50 The cobalt oxalate precursor is reduced at 300-350°C to obtain cobalt powder. The Fischer particle size of the unbroken cobalt powder is 0.86 μm, and the oxygen content is 0.52%wt. The whole process is stable and not easy to catch fire.

Embodiment 2

[0041] Implement CoCO 3 Slurry of wet material, solid-liquid ratio 1:4; prepare oxalic acid solution with a concentration of 0.8mol / L, by molar ratio n CoCO 3 : n H 2 C 2 o 4 =1:1.3 Ready to mix, preheat the solution to 25°C before the reaction, add H within 15min 2 C 2 o 4 Solution added CoCO 3 In the slurry, stir and react at constant temperature for 3 hours, separate and filter the precipitate from the solution, wash with clean water, dry at 80-120°C for 15-18 hours, grind and crush the dry powder and pass through a 100-mesh sieve to detect the obtained cobalt oxalate precursor The cobalt content in the medium is 32.79%wt, and the bulk density is 0.14g / cm 3 ,D 50 The cobalt oxalate precursor is reduced at 300-350° C. to obtain cobalt powder. The Fischer particle size of the unbroken cobalt powder is 0.60 μm, and the oxygen content is 0.43% wt. The whole process is stable and not easy to catch fire.

Embodiment 3

[0043] Implement CoCO 3 Slurry of wet material, solid-liquid ratio 1:4; prepare oxalic acid solution with a concentration of 0.8mol / L, by molar ratio n CoCO 3 : n H 2 C 2 o 4 =1:1.3 Prepare to mix, preheat the solution to 25°C before the reaction, add H within 40min 2 C 2 o 4 Solution added CoCO 3 In the slurry, stir and react at constant temperature for 3 hours, separate and filter the precipitate from the solution, wash with clean water, dry at 100-150°C for 15-18 hours, grind and crush the dry powder and pass through a 100-mesh sieve to detect the obtained cobalt oxalate precursor The cobalt content in the medium is 32.67%wt, and the bulk density is 0.22g / cm 3 ,D 50 The cobalt oxalate precursor is reduced at 300-350°C to obtain cobalt powder. The Fischer particle size of the unbroken cobalt powder is 0.55 μm, and the oxygen content is 0.61%wt. The whole process is stable and not easy to catch fire.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Fisherman's particle sizeaaaaaaaaaa
D50aaaaaaaaaa
Fisherman's particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to low-oxygen content submicron cobalt powder and a manufacturing method thereof, wherein the low-oxygen content submicron cobalt powder is prepared by the steps of preparing the cobalt oxalate precursor through the solid-liquid reaction of cobalt carbonate powder and an oxalate solution and then reducing the cobalt oxalate precursor. The low-oxygen content submicron cobalt powder can keep low oxygen content in fine submicron-level products, is difficult to fire in the reduction procedure, is easy to stably run in all processes of the production process and has convenient preparation.

Description

technical field [0001] The invention relates to the field of metallurgy and chemical industry, more specifically, the invention relates to a metal powder and a manufacturing method thereof. Background technique [0002] Cobalt powder is widely used in the field of metallurgy and chemical industry, and is an important raw material for the production of metallurgical and chemical products such as battery electrodes, high hardness alloys, diamond tools, and catalyst carriers. [0003] With the advancement of technology, the market's requirements for the quality of cobalt powder have become harsh and diverse. In addition to the requirements for particle morphology, customers are increasingly asking for indicators such as particle size, oxygen content, and bulk density of cobalt powder. Special and special requirements; Among them, cobalt powder with a particle size ranging from 100nm to 1μm is called by the industry: submicron cobalt powder, and low-oxygen submicron cobalt powde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F9/24
Inventor 许开华何显达韩红涛
Owner GEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap