Water resistance vegetable composite oil phase

A composite oil phase and plant-based technology, which is applied in the field of water-resistant vegetable-based composite oil phase and its preparation, can solve the problem of low detonation sensitivity of modified ammonium oil explosives, lack of water resistance and waterproof performance, and explosive detonation sensitivity Low-level problems, to achieve the effect of facilitating industrial production and application, convenient packaging, storage and transportation, and excellent water resistance

Inactive Publication Date: 2011-09-28
谢斌
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The root cause lies in the low detonation sensitivity of modified ammonium oil explosives, which is prone to residual guns and rejected blasts.
In our research, we found that the root cause of the low detonation sensitivity of explosives is that the explosives are not resistant to water. Once there is a small amount of water in the blast hole, the detonation wave will automatically extinguish during the propagation and the cannon phenomenon will appear, which will cause the explosives to fail. Poor strength
Modified ammonium oil explosives and expanded ammonium nitrate explosives do not have water resistance and waterproof performance, which is the main reason why they cannot be widely used like emulsion explosives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] The components are: 35% of wax ointment, 17.5% of hydrogenated vegetable fatty acid, 35% of soybean oil, 5% of vegetable oil, 5% of vegetable wax, 2% of sorbitan monooleate, 0.5% of sodium lauryl sulfate %

[0048] Take the above components and prepare the water-resistant plant-based composite oil phase according to the following steps:

[0049] First heat various materials in a separate melting tank to 75°C to melt, then pump the materials into the reaction kettle sequentially through the oil pump and electronic scale according to the proportion requirements, stir and heat up to 105°C, then turn on the vacuum pump for dehydration , Filtration, molding, packaging.

[0050]Application: (1) Weigh 860kg of ammonium nitrate, 80kg of water, 53kg of the composite oil phase made in Example 1, and 1.2kg of swelling agent; (2) make an aqueous solution of ammonium nitrate and water at 110-120°C; (3) Prepare the composite oil phase and bulking agent at 100-105°C to make an oil p...

Embodiment 2

[0053] The components are: 30% minus three line wax paste, 15% hydrogenated vegetable fatty acid, 40% rapeseed oil, 5% castor oil, 8% vegetable wax, and 2% sorbitan monooleate.

[0054] Take the above components and prepare the water-resistant plant-based composite oil phase according to the following steps:

[0055] First heat various materials in a separate melting tank to 80°C to melt, then pump the materials into the reaction kettle sequentially through the oil pump and electronic scale according to the proportion requirements, stir and heat up to 100°C, then turn on the vacuum pump for dehydration , Filtration, molding, packaging.

[0056] Application: (1) take by weighing 920kg ammonium nitrate, adopt the composite oil phase 35kg that embodiment 2 makes, wood powder 45kg, modifying agent 3kg; (2) composite oil phase is melted into solution at 85~95 ℃; (3 )Crush the ammonium nitrate and mix it with the modifier and enter the modified pretreatment machine together with th...

Embodiment 3

[0059] The components are: 37% minus four line wax cream, 22.5% hydrogenated vegetable fatty acid, 30% cotton oil foot, 5% palm oil, 5% vegetable wax, 2% sorbitan monooleate, diffusing agent MF0. 5%.

[0060] Take the above components and prepare the water-resistant plant-based composite oil phase according to the following steps:

[0061] First heat various materials in a separate melting tank to 85°C to melt, then pump the materials into the reaction kettle sequentially through the oil pump and electronic scale according to the proportion requirements, stir and heat up to 110°C, then turn on the vacuum pump for dehydration , Filtration, molding, packaging.

[0062] Application: (1) Weigh 944kg ammonium nitrate, 76kg water, use Example 3 to make composite oil phase 55kg, puffing agent 1.2kg, wood flour 1kg; (2) Ammonium nitrate and water are made into aqueous phase solution at 130°C (3) making the oil phase solution with the composite oil phase and the bulking agent at 90° ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heating valueaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a water resistance vegetable composite oil phase which comprises the following components in percent by mass: 5-30 percent of hydrogenated vegetable fatty acid, 5-20 percent of vegetable wax, 20-50 percent of vegetable oil foot, 5-20 percent of vegetable oil and fat, 20-50 percent of decompressed cerate and 0.5-3 percent of surfactant. The water resistance vegetable composite oil phase is prepared by adopting the following steps of: firstly, heating various components in a single melting tank to the temperature of 75-85 DEG C and melting; and sequentially pumping the components into a reaction kettle through an oil pump according to the proportion requirement after weighted through an electronic scale, stirring, raising the temperature to 105-110 DEG C, starting avacuum pump for dewatering, filtering, forming and packaging. The invention overcomes the defect of water resistance of the modified ammonium nitrate fuel oil explosive and extruded explosives, and provides a high-quality and low-cost water resistance vegetable composite oil phase used for the modified ammonium nitrate fuel oil explosive and extruded explosives; and the explosives produced by using the composite oil phase have excellent water resistance, and especially the extruded explosives really have excellent water resistance.

Description

technical field [0001] The invention relates to a water-resistant plant matter composite oil phase applied to modified ammonium oil explosives and expanded ammonium nitrate explosives and a preparation method thereof. Background technique [0002] In recent years, my country has forced the elimination of powdered ammonium ladder explosives. Relevant research institutes have successively developed new powdery explosives such as expanded ammonium nitrate explosives and modified ammonium oil explosives by modifying ammonium nitrate and using composite oil phases. Since TNT is canceled in explosives, it is of great significance for improving the intrinsic safety of explosives production, improving production conditions and environmental quality. [0003] However, in the powdery modified ammonium oil explosive composed of ammonium nitrate, composite oil phase, and wood flour, due to the cancellation of the sensitizer simple explosive TNT, compared with the powdery ammonium ladder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C06B31/28
Inventor 谢斌
Owner 谢斌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com