A technology of powder coatings and raw materials, applied in the direction of powder coatings, luminescent coatings, polyester coatings, etc., can solve the problems of limited application range, failure to achieve actual application effects, solvent pollution, etc., and achieve the effect of expanding the application range

Inactive Publication Date: 2011-05-11
李新春
View PDF2 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN101117522A discloses a self-luminous powder coating, which uses self-luminous powder to form a self-luminous coating. In some cases, the actual use effect cannot be achieved only by self-luminescence, which limits its scope of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] A luminous powder coating of the present invention is mainly made of the following raw material proportions by weight: 50-90 parts of film-forming agent; 10-30 parts of curing agent; 0.01-0.03 parts of defoaming agent; 0.4-1.0 parts of leveling agent 0.4-1.0 parts of titanium dioxide; 5-10 parts of glass microspheres; 8-10 parts of alkaline earth metal aluminates. The film-forming agent described in the present invention comprises one or more in epoxy resin, polyester resin, polyurethane resin, acrylic resin, fluorocarbon resin, phenolic resin, alkyd resin; Described curing agent comprises amine, One or more of polybasic hydroxy acids, imidazoles, triglycidyl isocyanurate; the leveling agent includes polyacrylate, silicon-containing acrylate, cellulose acetate butyrate, epoxy soybean oil One or more of them; the diameter of the glass microspheres is between 80-120 microns. It also includes a catalyst, the catalyst is imidazoles, which can significantly improve the film...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a noctilucent powder paint which is mainly prepared from the following raw materials in parts by weight: 50-90 parts of film forming agent, 10-30 parts of curing agent, 0.01-0.03 part of defoaming agent, 0.4-1.0 part of flatting agent, 0.4-1.0 part of titanium dioxide, 5-10 parts of glass beads and 8-10 parts of alkaline earth metal aluminate. In the invention, the formula of the paint is optimized, different additives are matched mutually, and the alkaline earth metal aluminate is used as the luminous material, thus the paint can emit light and reflect light at night, the luminous time is more than 12 hours, the luminous intensity can reach 1000mcd/m<2>, the paint can reflect light in the existence of weak light, and the application range of the paint can be expanded.

Description

technical field [0001] The invention relates to a luminous powder coating. Background technique [0002] As a solvent-free coating, powder coating is economical, environmentally friendly, efficient, and excellent in performance, and is welcomed by people. With the increasingly stringent requirements for environmental protection, powder coatings have developed rapidly due to their low pollution, high decorativeness, and good comprehensive performance, and are gradually replacing traditional solvent-based coatings. As the use of powder coatings becomes more and more extensive, various functional coatings appear one after another. Luminous powder coatings can be applied to parts that need to be warned at night without additional power supply. Through the characteristics of reflection or self-luminescence, it can achieve the role of night marking. . Chinese patent CN101117522A discloses a self-luminous powder coating, which uses self-luminous powder to form a self-luminous coa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D167/00C09D175/04C09D133/00C09D127/12C09D161/06C09D167/08C09D5/03C09D5/22
Inventor 李新春
Owner 李新春
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap