Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Polycrystalline diamond drill bit matrix powder

A technology of polycrystalline diamond and matrix powder, which is used in drill bits, earth-moving drilling, drilling equipment, etc., can solve the problems of difficulty in meeting low-cost requirements, the impact of drill bit permeability, and high drill bit manufacturing costs, and achieve good wettability. , The effect of reducing carcass porosity and improving drilling speed

Active Publication Date: 2012-11-14
KINGDREAM PLC CO +1
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with the traditional matrix powder, this kind of matrix powder has greatly improved strength and toughness. However, a large amount of cast WC fine powder will affect the permeability of the drill bit, and the sintering process is prone to defects such as matrix looseness.
In addition, the bit manufacturing cost of this kind of matrix powder is relatively high, and it is difficult to meet the demand of low cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polycrystalline diamond drill bit matrix powder
  • Polycrystalline diamond drill bit matrix powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The carcass powder consists of 35% of spherical sintered WC particles with a particle size of 150-250 microns (the proportion of hollow spherical sintered WC particles is 25%), and 60% of macrocrystalline WC particles with a particle size of 50-150 microns. , Nickel powder mixed with 5%. The mechanical properties of the sintered carcass were tested according to GB3851 and GB / T1817. The results showed that the strength ratio of the carcass containing spherical sintered WC particles and macrocrystalline WC particles ) Pure cast WC powder carcass strength increased by 30%, impact toughness increased by 35%.

Embodiment 2

[0022] Carcass powder consists of 55% of spherical sintered WC particles with a particle size of 150-250 microns (the proportion of hollow spherical sintered WC particles is 25%), and 35% of macrocrystalline WC particles with a particle size of 50-150 microns. , 10% nickel powder mixed. The mechanical properties of the sintered carcass were tested according to GB3851 and GB / T1817. The results showed that the strength ratio of the carcass containing spherical sintered WC particles and macrocrystalline WC particles ) Pure cast WC powder carcass strength increased by 50%, impact toughness increased by 40%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a powder metallurgy material for manufacturing a polycrystalline diamond drill bit matrix. The powder metallurgy material comprises the components by weight percent: 30-60% of spherical sintered WC particles with the particle size of 125-500 microns, 25-60% of fine macrocrystalline WC particles with the particle size of 50-200 microns, and 5-15% of nickel powder. According to the invention, bonding phase can penetrate into the hollow spherical sintered WC particles and can be used for filling the hollow spherical sintered WC particles, so that the bonding phase and hard phase in the matrix can be better combined with each other, and the matrix has higher strength and toughness; and gaps among coarse particles can be effectively filled by the fine macrocrystalline WC particles, so that the erosion resistance and the wear resistance of the matrix can be better improved. According to the invention, the matrix material cost of a drill bit is reduced; and as the performances of the matrix are improved, the polycrystalline diamond compact (PDC) drill bit with a thinner or longer scraping knife can be designed, and the drilling rate of the PDC drill bit can be greatly increased.

Description

technical field [0001] The invention relates to a powder metallurgy material for making a polycrystalline diamond (PDC) bit matrix, in particular to a polycrystalline diamond bit matrix powder, which belongs to the technical field of petroleum drill bit materials. Background technique [0002] In oil drilling, matrix PDC drill bits are increasingly used because of their good erosion resistance. With the development of drilling technology and the increasingly complex drilling conditions, on the premise of ensuring the safety of the bit scraper, higher requirements are put forward for the drilling speed of the PDC bit. The matrix PDC bit mainly includes two parts: the bit body and the upper body connection. The lower part of the bit body is the matrix, and the polycrystalline diamond composite (knife) sheet is welded on the matrix. For the PDC bit, in addition to using polycrystalline diamond composites with better toughness and wear resistance, changing the structure of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/00C22C29/08E21B10/00
Inventor 张玉龙张烈华
Owner KINGDREAM PLC CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com