Al-Fe-C-RE aluminium alloy, preparation method thereof and power cable

An al-fe-c-re, power cable technology, applied in the field of alloys, can solve problems such as poor fatigue resistance, quality problems, and affecting the service life of aluminum alloy materials

Active Publication Date: 2013-05-15
ANHUI JOY SENSE CABLE
View PDF4 Cites 70 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The aluminum alloy conductor materials in the prior art are relatively excellent in electrical properties, corrosion resistance and mechanical properties, etc., but are still relatively poor in fatigue resistance, which is prone to quality problems and affects the service life or band of the aluminum alloy material. Therefore, the overall performance of aluminum alloy power cables is still poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Al-Fe-C-RE aluminium alloy, preparation method thereof and power cable
  • Al-Fe-C-RE aluminium alloy, preparation method thereof and power cable
  • Al-Fe-C-RE aluminium alloy, preparation method thereof and power cable

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0078] The present invention also provides a method for preparing an Al-Fe-C-RE aluminum alloy, comprising the following steps:

[0079] a) Cast the raw materials of the following composition to obtain an aluminum alloy ingot: 0.01~1.6wt% Fe, 0.001~0.3wt% Cu, 0.001~0.3wt% Mg, 0.001~0.3wt% Co, 0.001~0.2 wt% Be, 0.001~0.3wt% Ca, 0.001~0.2wt% Zn, 0.001~0.3wt% Sr, 0.001~0.3wt% Zr, 0.002~0.25wt% Li, 0.001~0.2wt% Na, 0.002~0.25wt% K, 0.001~0.2wt% Ti, 0.001~0.15wt% V, 0.001~0.12wt% Cr, 0.001~0.12wt% Mn, 0.001~0.15wt% Ni , 0.001~0.2wt% of Ga, 0.003~0.2wt% of Ge, 0.001~0.2wt% of Rb, 0.001~0.15wt% of Nb, 0.001~0.2wt% of Mo, 0.001~0.25wt% of Tc, 0.001 ~0.15wt% Ru, 0.002~0.1wt% Rh, 0.001~0.12wt% Pd, 0.001~0.1wt% Ag, 0.002~0.13wt% Cd, 0.003~0.18wt% In, 0.001~0.08 wt% Sn, 0.001~0.3wt% Sb, 0.001~0.2wt% Cs, 0.001~0.08wt% Ba, 0.001~0.22wt% Hf, 0.002~0.16wt% Ta, 0.001~0.08wt% W, 0.002~0.18wt% Re, 0.002~0.08wt% Os, 0.001~0.15wt% Ir, 0.002~0.08wt% Pt, 0.001~0.05wt% Au, 0.002~0.15wt% Tl , 0.00...

Embodiment 1

[0092] (1) Put the aluminum ingot into the furnace, heat it to melt and keep it warm at 720°C. The melting process is completed in a sealed environment; first add Fe, Cu, Mg, Co, Be, Ca, Zn, Sr, Zr, Si , B, Li, Na, K, Ti, V, Cr, Mn, Ni, Ga, Ge, Rb, Nb, Mo, Tc, Ru, Rh, Pd, Ag, Cd, In, Sn, Sb, Cs, Ba , Hf, Ta, W, Re, Os, Ir, Pt, Au, Tl, Pb, Bi and C, after stirring evenly, add rare earth RE and stir for 20 minutes until fully stirred evenly, and keep it for 30 minutes; Carry out refining in the furnace; add refining agent to the alloy melt, stir evenly, and then keep it for 30 minutes, and operate the melt refining in a sealed environment; After being out of the furnace, after degassing and slag removal, it enters the casting machine for casting to obtain aluminum alloy ingots. The composition of the ingots is listed in Table 1;

[0093] (2) Heat up the aluminum alloy ingot obtained in step (1) at a rate of 5°C / min to 450°C, hold it for 6 hours, and then roll it into a rod;

...

Embodiment 2

[0098](1) Put the aluminum ingot into the furnace, heat it to melt and keep it warm at 740°C. The melting process is completed in a sealed environment; first add Fe, Cu, Mg, Co, Be, Ca, Zn, Sr, Zr, Si , B, Li, Na, K, Ti, V, Cr, Mn, Ni, Ga, Ge, Rb, Nb, Mo, Tc, Ru, Rh, Pd, Ag, Cd, In, Sn, Sb, Cs, Ba , Hf, Ta, W, Re, Os, Ir, Pt, Au, Tl, Pb, Bi and C, after stirring evenly, add rare earth RE and stir for 20 minutes until fully stirred evenly, and keep it for 30 minutes; Carry out refining in the furnace; add refining agent to the alloy melt, stir evenly, and then let it stand for 30 minutes, and operate the melt refining in a sealed environment; After being out of the furnace, after degassing and slag removal, it enters the casting machine for casting to obtain aluminum alloy ingots. The composition of the ingots is listed in Table 1;

[0099] (2) Heat up the aluminum alloy ingot obtained in step (1) at a rate of 3°C / min to 550°C, hold it for 16 hours and then roll it into a rod;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thermal resistanceaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention provides an Al-Fe-C-RE aluminium alloy and a preparation method thereof. The preparation method comprises the following steps of: a) casting an aluminium alloy cast ingot; b) homogenizing the aluminium alloy cast ingot and rolling the homogenized aluminium alloy cast ingot to obtain an aluminium alloy rod material; c) intermittently annealing the aluminium alloy rod material obtained in the step b); and d) aging the aluminium alloy rod material obtained in the step c), thus obtaining the aluminium alloy. The invention also provides a power cable. The aluminium alloy has better overall performances by selecting and controlling the added elements and adopting a reasonable preparation process.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to an Al-Fe-C-RE aluminum alloy, a preparation method thereof, and a power cable. Background technique [0002] Aluminum alloy is the most widely used non-ferrous metal structural material in industry, and is widely used in aviation, aerospace, automobile, machinery manufacturing, shipbuilding and chemical industry. With the rapid development of science and technology and industrial economy, the demand for aluminum alloys is increasing, and the research on aluminum alloys is also in-depth. The wide application of aluminum alloys has promoted the development of aluminum alloys in the power industry, and at the same time the development of the power industry has expanded the application fields of aluminum alloys. [0003] A power cable is a resource used to transmit and distribute electrical energy, and its basic structure consists of four parts: a core, an insulating layer, a shieldi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22F1/04C21D8/08H01B1/02H01B9/00
Inventor 林泽民
Owner ANHUI JOY SENSE CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com