Wear, corrosion and rust resistant metal pipeline

A wear-resistant pipeline, anti-corrosion and anti-rust technology, which is applied in the direction of pipeline anti-corrosion/rust protection, pipeline protection, pipeline damage/wear prevention, etc. Effect of heat treatment cycle, low coefficient of friction and high hardness

Active Publication Date: 2015-04-15
NANTONG LITAI CHEM EQUIP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] However, anti-corrosion coatings in the prior art are usually difficult to balance water resistance, anti-fouling effect, and high temperature resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] A) Preparation of wear-resistant pipe body

[0060] 1) To obtain materials, select raw materials with the following chemical composition weight percentages:

[0061] C: 1.6%, V: 4.5%,

[0062] W: 9.1%, Mo: 7.6%,

[0063] Cr: 3.8%, RE: 0.15%,

[0064] Mn: 0.7%, Si: 0.05%,

[0065] B: 0.02%, Al: 0.2%,

[0066] Nb: 0.08%, Ni: 0.1%,

[0067] The balance is Fe and trace unavoidable impurities;

[0068] 2) Mix and heat ordinary steel scrap, micro-carbon ferrochrome, ferroniobium, ferronickel, ferrotungsten, ferromolybdenum, ferrochrome and ferromanganese, add carbon with pig iron or graphite, mix and heat to melt into molten steel, and add the molten steel after it is melted Ferrosilicon for pre-deoxidation;

[0069] 3) According to the distribution ratio of raw materials, adjust the composition in front of the furnace and raise the temperature to 1580°C, then add aluminum blocks for final deoxidation, and then leave the furnace;

[0070] 4) Put the rare earth ferrosi...

Embodiment 2

[0093] A) Preparation of wear-resistant pipe body

[0094] 1) To obtain materials, select raw materials with the following chemical composition weight percentages:

[0095] C: 2.7%, V: 6.0%,

[0096] W: 6.9%, Mo: 5.3%,

[0097] Cr: 5.4%, RE: 0.23%,

[0098] Mn: 0.6%, Si: 0.08%,

[0099] B: 0.01%, Al: 0.5%,

[0100] Nb: 1.1%, Ni: 0.2%,

[0101] The balance is Fe and trace unavoidable impurities;

[0102] 2) Mix and heat ordinary steel scrap, micro-carbon ferrochrome, ferroniobium, ferronickel, ferrotungsten, ferromolybdenum, ferrochrome and ferromanganese, add carbon with pig iron or graphite, mix and heat to melt into molten steel, and add the molten steel after it is melted Ferrosilicon for pre-deoxidation;

[0103] 3) According to the distribution ratio of raw materials, adjust the composition in front of the furnace and raise the temperature to 1600°C, then add aluminum blocks for final deoxidation, and then leave the furnace;

[0104] 4) Put the rare earth ferrosil...

Embodiment 3

[0127] A) Preparation of wear-resistant pipe body

[0128] 1) To obtain materials, select raw materials with the following chemical composition weight percentages:

[0129] C: 3.7%, V: 8.5%,

[0130] W: 3.2%, Mo: 2.4%,

[0131] Cr: 8.9%, RE: 0.4%,

[0132] Mn: 0.3%, Si: 1.0%,

[0133] B: 0.01%, Al: 0.8%,

[0134] Nb: 2.4%, Ni: 0.3%,

[0135] The balance is Fe and trace unavoidable impurities;

[0136] 2) Mix and heat ordinary steel scrap, micro-carbon ferrochrome, ferroniobium, ferronickel, ferrotungsten, ferromolybdenum, ferrochrome and ferromanganese, add carbon with pig iron or graphite, mix and heat to melt into molten steel, and add the molten steel after it is melted Ferrosilicon for pre-deoxidation;

[0137] 3) According to the distribution ratio of raw materials, adjust the composition in front of the furnace and raise the temperature to 1630°C, then add aluminum blocks for final deoxidation, and then leave the furnace;

[0138] 4) Put the rare earth ferrosilic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wear, corrosion and rust resistant metal pipeline. The metal pipeline is manufactured by manufacturing a wear-resistant pipeline body through centrifugal casting, carrying out the processes of quenching, high-temperature tempering, solid solution strengthening thermal treatment and double tempering and dispersion hardening thermal treatment, then electrostatically spraying a rust-resistant coating on the outer wall of the pipeline, and finally air-spraying a corrosion-resistant coating on the inner wall of the pipeline. The metal pipeline has higher hardness and wear resistance, and the corrosion-resistant coating of the metal pipeline has excellent water resistance, antifouling effect and high temperature resistance.

Description

technical field [0001] The invention relates to a pipeline, in particular to a metal wear-resistant, anti-corrosion and anti-rust pipeline. Background technique [0002] There are three main forms of material failure: fracture, corrosion, and wear. Although unlike the other two forms, material wear rarely causes catastrophic damage to metal workpieces, but the economic losses it causes are quite staggering. According to statistics, about 75%-80% of the failed mechanical parts are caused by metal wear. About 30%-50% of the energy supplied to the machine is consumed in the process of friction and wear. Parts wear out After that, it will not only affect the use efficiency of machinery and equipment, but also consume a lot of manpower and material resources to replace parts and repair equipment. The economic losses caused by wear and tear are about 120 billion US dollars per year in the United States and about 50 billion marks per year in Germany. According to 2005 According t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C37/10C22C38/56C22C38/54C21D1/18F16L57/06F16L58/04
Inventor 唐健发唐丽张凤琼李撰
Owner NANTONG LITAI CHEM EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com