Material formula for insulating layer of cable with low dielectric loss

A cable insulation and layer material technology, applied in the field of cable manufacturing, can solve the problems of reducing energy utilization, destroying communication, energy loss, etc., achieving the effects of reducing dielectric loss, reasonable material matching, and improving utilization

Inactive Publication Date: 2014-01-01
安徽万博电缆材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The dielectric loss heat consumes energy and may cause thermal breakdown of the dielectric, which not only causes energy loss and reduces the utilization rate of energy, but also easily causes short circuit, damages equipment and destroys communication.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Material formula for insulating layer of cable with low dielectric loss
  • Material formula for insulating layer of cable with low dielectric loss
  • Material formula for insulating layer of cable with low dielectric loss

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A low dielectric loss cable insulation material formula, the formula includes titanium dioxide, white carbon black, paraffin, stearic acid, spray carbon black, aluminum hydroxide and resin, and the mass percentage of each component is as follows:

[0022]

Embodiment 2

[0024] A low dielectric loss cable insulation material formula, the formula includes titanium dioxide, white carbon black, paraffin, stearic acid, spray carbon black, aluminum hydroxide and resin, and the mass percentage of each component is as follows:

[0025]

Embodiment 3

[0027] A low dielectric loss cable insulation material formula, the formula includes titanium dioxide, white carbon black, paraffin, stearic acid, spray carbon black, aluminum hydroxide and resin, and the mass percentage of each component is as follows:

[0028]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a material formula for an insulating layer of a cable with low dielectric loss. The formula contains the following ingredients in percentage by mass: 2-8% of titanium white, 3-10% of white carbon black, 12-16% of paraffin, 10-12% of stearic acid, 5-8% of spray carbon black, 7-14% of aluminum hydroxide and 35-45% of resin. The formula has the advantages of reasonable material proportion, low cost and the like and has the function of lowering the dielectric loss of the cable, the utilization ratio of energy is increased, and a guarantee is provided for the normal use of mechanical equipment, communication and the like.

Description

technical field [0001] The invention relates to the technical field of cable manufacturing, in particular to a low dielectric loss cable insulation layer material formula. Background technique [0002] Dielectric loss refers to the energy loss inside the insulating material due to the hysteresis effect of dielectric conductance and dielectric polarization under the action of an electric field, also called dielectric loss, or dielectric loss for short. Under the action of the alternating electric field, the complementary angle δ of the included angle (power factor angle Φ) between the current phasor and the voltage phasor flowing in the dielectric is called the dielectric loss angle. Dielectric loss and heat consumption consume energy and may cause thermal breakdown of the dielectric, which not only causes energy loss and reduces energy utilization, but also easily causes short circuits, damages equipment and disrupts communications. Therefore, in the electrical insulation t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L101/00C08L91/06C08K13/02C08K3/22C08K5/09C08K3/04C08K3/36
Inventor 范先宝
Owner 安徽万博电缆材料有限公司