Amino drying static varnish

An electrostatic and varnish technology, applied in coatings, polyester coatings, etc., can solve problems such as the paint film is not hard enough and the wear resistance of electrostatic varnish is not good enough.

Inactive Publication Date: 2014-09-10
袁卫林
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The current electrostatic varnish has entered a wide range of applications, but the wear resistance of electrostatic varnish is not good enough, and the paint film is not hard enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] The invention provides an amino drying electrostatic varnish, which comprises the following raw materials: 64 kg of castor oil alkyd resin, 32 kg of melamine formaldehyde resin, 3.6 kg of butanol, 0.4 kg of organic silicon oil, and the mass fraction of the organic silicon oil is 1%.

[0008] The amino-drying electrostatic varnish provided by the invention comprises mixing melamine-formaldehyde resin with a low degree of etherification, medium-oil castor oil alkyd resin and butanol, adding organic silicon oil, fully mixing, and filtering to obtain an amino-drying electrostatic varnish.

Embodiment 2

[0010] The invention provides an amino drying electrostatic varnish, which comprises the following raw materials: 68 kg of castor oil alkyd resin, 35 kg of melamine formaldehyde resin, 4 kg of butanol, 0.6 kg of organic silicon oil, and the mass fraction of the organic silicon oil is 2%.

[0011] The amino-drying electrostatic varnish provided by the invention comprises mixing melamine-formaldehyde resin with a low degree of etherification, medium-oil castor oil alkyd resin and butanol, adding organic silicon oil, fully mixing, and filtering to obtain an amino-drying electrostatic varnish.

Embodiment 3

[0013] The invention provides an amino drying electrostatic varnish, which comprises the following raw materials: 66 kg of castor oil alkyd resin, 34 kg of melamine formaldehyde resin, 3.8 kg of butanol, 0.5 kg of organic silicon oil, and the mass fraction of the organic silicon oil is 1.5%.

[0014] The amino-drying electrostatic varnish provided by the invention comprises mixing melamine-formaldehyde resin with a low degree of etherification, medium-oil castor oil alkyd resin and butanol, adding organic silicon oil, fully mixing, and filtering to obtain an amino-drying electrostatic varnish.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
friction coefficientaaaaaaaaaa
Login to view more

Abstract

The invention provides amino drying static varnish. The amino drying static varnish is prepared from the following raw materials in parts by weight: 100-120 parts of polyphenylene sulfide, 30-40 parts of polytetrafluoroethylene, 40-50 parts of polyether-polysulfone, 30-40 parts of lead fluoride, 200-250 parts of water, 20-30 parts of surface active agent and 130-150 parts of propylene glycol. The amino drying static varnish is baked for 45 minutes at the temperature of 370 DEG C, a smooth coating with good adhesive force and high hardness can be formed, and the kinetic friction coefficient is not more than 0.155.

Description

technical field [0001] The invention relates to a method for preparing a coating, in particular to an amino drying electrostatic varnish. Background technique [0002] The current electrostatic varnish has been widely used, but the wear resistance of the electrostatic varnish is not good enough, and the paint film is not hard enough. Contents of the invention [0003] The purpose of the present invention is to provide an amino drying electrostatic varnish to solve one or more problems in the prior art. [0004] According to one aspect of the present invention, an amino drying electrostatic varnish is provided, comprising the following raw materials in parts by weight: 64-68 parts of castor oil alkyd resin, 32-35 parts of melamine formaldehyde resin, 3.6-4 parts of butanol, organic 0.4-0.6 parts of silicone oil, and the mass fraction of organic silicone oil is 1%-2%. [0005] The amino-drying electrostatic varnish provided by the invention comprises mixing melamine-formal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D161/28
Inventor 袁卫林
Owner 袁卫林
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap