Preparation method of zinc hydroxystannate nanorod array with controllable size

A technology of zinc hydroxystannate and nanorod array, which is applied in nanotechnology, nanotechnology, nanotechnology and other directions for materials and surface science, can solve problems such as not meeting expected requirements, and achieve uniform size, low price, and shape. A neat effect

Inactive Publication Date: 2014-10-01
HARBIN ENG UNIV
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current research is far from meeting people's expectations for it, and further in-depth research is still needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of zinc hydroxystannate nanorod array with controllable size
  • Preparation method of zinc hydroxystannate nanorod array with controllable size
  • Preparation method of zinc hydroxystannate nanorod array with controllable size

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Preparation of zinc oxide. Coat the surface of the cleaned zinc sheet with a layer of butyl titanate, put it into a polytetrafluoroethylene autoclave with a concentration of 0.5 mol / liter sodium hydroxide solution, and heat it at a constant temperature of 180 degrees Celsius for 12 hours. The final zinc sheet is taken out, rinsed with absolute ethanol and deionized water in turn, and dried at 60-100 degrees Celsius for 6-12 hours;

[0028] (2) the zinc flakes obtained in the first step are put into the reaction solution mixed with raw material urea, potassium stannate and hydroalcoholic solution, the concentration of urea in the middle period is 0.1-0.5 mol / liter, and the concentration of potassium stannate The concentration is 0.01-0.05 mol / liter, and the volume of absolute ethanol in the hydroalcoholic solution is 30%;

[0029] (3) heating the above-mentioned solution at 60-70 degrees Celsius for 1-6 hours;

[0030] (4) Collect the zinc flakes obtained from the ...

Embodiment 2

[0032] (1) Preparation of zinc oxide. Coat the surface of the cleaned zinc sheet with a layer of butyl titanate, put it into a polytetrafluoroethylene autoclave with a concentration of 0.5 mol / liter sodium hydroxide solution, and heat it at a constant temperature of 180 degrees Celsius for 12 hours. The final zinc sheet is taken out, rinsed with absolute ethanol and deionized water in turn, and dried at 60-100 degrees Celsius for 6-12 hours;

[0033] (2) put the zinc sheet obtained in the first step into the reaction solution mixed with raw material urea, potassium stannate and hydroalcoholic solution, the concentration of urea in the middle period is 0.5-1.0 mol / liter, and the concentration of potassium stannate The concentration is 0.01-0.05 mol / liter, and the volume of absolute ethanol in the hydroalcoholic solution is 30%;

[0034] (3) heating the above-mentioned solution at 60-70 degrees Celsius for 1-6 hours;

[0035] (4) Collect the zinc flakes obtained from the react...

Embodiment 3

[0037] (1) Preparation of zinc oxide. Coat the surface of the cleaned zinc sheet with a layer of butyl titanate, put it into a polytetrafluoroethylene autoclave with a concentration of 0.5 mol / liter sodium hydroxide solution, and heat it at a constant temperature of 180 degrees Celsius for 12 hours. The final zinc sheet is taken out, rinsed with absolute ethanol and deionized water in turn, and dried at 60-100 degrees Celsius for 6-12 hours;

[0038] (2) the zinc flakes obtained in the first step are put into the reaction solution mixed with raw material urea, potassium stannate and hydroalcoholic solution, the concentration of urea in the middle period is 0.1-0.5 mol / liter, and the concentration of potassium stannate The concentration is 0.01-0.05 mol / liter, and the volume of absolute ethanol in the hydroalcoholic solution is 30%;

[0039] (3) heating the above-mentioned solution at 60-70 degrees Celsius for 9-12 hours;

[0040] (4) Collect the zinc flakes obtained from the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of a zinc hydroxystannate nanorod array with controllable size. The preparation method comprises the following steps: coating a layer of butyl titanate on the surface of a cleaned zinc sheet, placing into an autoclave filled with a 0.5 mol/L sodium hydroxide solution, conducting constant-temperature heating for 12 hours at 180DEG C, washing the zinc sheet sequentially with absolute ethyl alcohol and deionized water cleanly, and drying for 6-12 hours at 60-100DEG C; placing the zinc sheet into a reaction solution containing urea, potassium stannate and a water-alcohol solution, wherein the concentration of urea is 0.1-1.0 mol/L, the concentration of potassium stannate is 0.01-0.05 mol/L, and the volume of absolute ethyl alcohol in the water-alcohol solution is 30%; conducting constant-temperature heating for 1-12 hours at 60-90DEG C; and collecting the zinc sheet obtained in the reaction, washing the zinc sheet sequentially with absolute ethyl alcohol and deionized water cleanly, and drying for 10 hours at 60DEG C, thus obtaining the final product. The method has the advantages of being simple to operate, mild in experimental conditions, low in energy consumption, free from environmental pollution, capable of being applied in large-scale industrial production and the like.

Description

technical field [0001] The invention relates to a method for preparing an array of inorganic nano functional materials, in particular to a method for preparing a size-controllable zinc hydroxystannate nanorod array. Background technique [0002] Today, environmental pollution and resource shortages have become crucial issues restricting the development of the global economy. Therefore, how to solve environmental pollution and resource shortages that hinder the sustainable development of human society has become a global research topic that people are increasingly concerned about. Designing and preparing high-performance and high-efficiency catalytic, photoelectric, and gas-sensing functional materials and device technologies is the most critical and basic technical approach among all technical approaches to solving and coping with energy crisis and environmental pollution. [0003] Zinc hydroxystannate is a new flame retardant and smoke suppressant developed by the Internati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01G19/00B82Y40/00B82Y30/00
Inventor 高鹏王莹王龙强鲍迪
Owner HARBIN ENG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap