Method for preparing functional wallpaper by using iron-magnesium tourmaline and palygorskite

A kind of iron-magnesium tourmaline and palygorskite technology, applied in the direction of fiber type, textile and papermaking, fiber processing, etc., can solve the problems of limited application and achieve the effect of strong water absorption

Active Publication Date: 2014-10-08
SOUTH CHINA UNIV OF TECH
View PDF6 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Titanium dioxide photocatalyst needs ultraviolet light excitation to release electrons, limiting its application in home decoration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Fe in the present embodiment ferrite 2 o 3 The content is 12% (weight percent), the MgO content is 12% (weight percent), and the average particle size is 2 microns; the average particle size of palygorskite is 2 microns.

[0025] A method for preparing functional wallpaper by using ferromagnesian tourmaline powder and palygorskite, comprising the following steps and process conditions:

[0026] (1) with 15% (weight percent) polyacrylate coating agent, 1% (weight percent) polyacrylic acid thickener, 5% (weight percent) ferrite powder, 20% (weight percent) palygorskite, 20% (weight percentage) calcium carbonate powder, 39% (weight percentage) water are mixed and stirred evenly, make coating paint;

[0027] (2) Coating the above-mentioned coating paint on the polyester fiber base cloth, and then printing and baking to obtain a functional wallpaper. The prepared wallpaper can release negative ions, and has the functions of purifying air and adjusting indoor air humidity....

Embodiment 2

[0031] The ferrite refers to Fe 2 o 3 The content is 16% (percentage by weight), the content of MgO is 16% (percentage by weight), and the average particle size is 1 micron; the average particle size of palygorskite is 1 micron.

[0032] A method for preparing functional wallpaper by using ferromagnesian tourmaline powder and palygorskite, comprising the following steps and process conditions:

[0033] (1) with 18% (weight percent) polyacrylate coating agent, 2% (weight percent) polyacrylic acid thickener, 20% (weight percent) ferrite powder, 5% (weight percent) palygorskite, 15% (weight percentage) calcium carbonate powder, 40% (weight percentage) water are mixed and stirred evenly, make coating paint;

[0034] (2) Coating the above-mentioned coating paint on the polyester fiber base cloth, and then printing and baking to obtain a functional wallpaper. The prepared wallpaper can release negative ions, and has the functions of purifying air and adjusting indoor air humidity. ...

Embodiment 3

[0037] The ferrite refers to Fe 2 o 3 The content is 14% (percentage by weight), the content of MgO is 14% (percentage by weight), and the average particle size is 1.5 microns; the average particle size of palygorskite is 1.5 microns.

[0038] A method for preparing functional wallpaper by using ferromagnesian tourmaline powder and palygorskite, comprising the following steps and process conditions:

[0039] (1) with 20% (weight percent) polyacrylate coating agent, 1.5% (weight percent) polyacrylic acid thickener, 10% (weight percent) ferrite powder, 10% (weight percent) palygorskite, 20% (weight percentage) calcium carbonate powder, 38.5% (weight percentage) water are mixed and stirred evenly, make coating paint;

[0040] (2) Coating the above-mentioned coating paint on the polyester fiber base cloth, and then printing and baking to obtain a functional wallpaper. The prepared wallpaper can release negative ions, and has the functions of purifying air and adjusting indoor a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing functional wallpaper by using iron-magnesium tourmaline and palygorskite. The method comprises the steps: mixing and stirring uniformly 15-20% of a polyacrylate coating agent, 1-2% of a polyacrylic acid thickener, 5-20% of an iron-magnesium tourmaline powder, 5-20% of the palygorskite, 10-20% of a calcium carbonate powder and 30-40% of water according to the mass percentage, and thus obtaining a coating paint; coating a polyester fiber base fabric with the coating paint, then printing and baking, and thus obtaining the functional wallpaper. The prepared wallpaper can release negative ions, and has the functions of purifying air and adjusting the indoor air humidity.

Description

technical field [0001] The invention relates to a wallpaper, in particular to a method for preparing functional wallpaper by using ferromagnesia tourmaline and palygorskite. The resin type artificial marble prepared by the method and the prepared wallpaper can release negative ions, and have the functions of purifying air and adjusting indoor air humidity. Background technique [0002] Wallpaper has various colors, rich patterns, luxurious style, safety and environmental protection, convenient construction, reasonable price and many other incomparable characteristics of other interior decoration materials. It is a widely used interior decoration material. In environmental assessment, the concentration of negative ions in the air is listed as an important parameter to measure air quality. An appropriate concentration of negative ions in the air can eliminate dust and toxic and harmful gases suspended in the air, inhibit the growth of bacteria and molds, and purify the air. I...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/80D06M11/79D06M15/263D06M101/32
Inventor 钟明峰苏达根朱锦辉殷文清
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap