Ultrasonic intensified leaching method for refractory gold ores and ultrasonic intensified gold leaching stirrer

A technology of ultrasonic strengthening and gold mining, applied in the field of hydrometallurgy, can solve difficult, difficult, and further improvement problems, and achieve the effects of reducing investment, convenient operation, and saving equipment space

Inactive Publication Date: 2014-11-05
KUNMING UNIV OF SCI & TECH
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is more difficult to continue to develop on this basis
The rate of leaching go...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrasonic intensified leaching method for refractory gold ores and ultrasonic intensified gold leaching stirrer
  • Ultrasonic intensified leaching method for refractory gold ores and ultrasonic intensified gold leaching stirrer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] For a refractory gold ore, the gold grade is 3.23g / t, and the leaching rate obtained by direct conventional cyanidation leaching process is 12.7%. First mix 400g of gold ore powder with a particle size of less than 200 mesh and 600ml of water in a 1L beaker, then add 20g of sodium hydroxide; turn on the mechanical stirring and adjust the stirring speed to 500 rpm, the air volume to 120L / hour, and stir After uniformity, the opening frequency is 20.0kHz, the power is 2kW, and the sound intensity is 3.3W / cm 3 Ultrasonic device carries out ultrasonic intensive pretreatment. The cycle of ultrasonic pretreatment is 5 minutes of ultrasonic pretreatment and 1 minute off. During ultrasonic pretreatment, 1ml of hydrogen peroxide is added every half hour; after 3 hours of treatment, it is filtered, washed and dried for later use. Take 150g of ore sample treated with sodium hydroxide, add 600ml of water, 1g of calcium oxide and 1.8g of sodium cyanide. cm 3 Ultrasonic equipment is...

Embodiment 2

[0028] For a refractory gold ore, the gold grade is 3.23g / t, and the leaching rate obtained by direct conventional cyanidation leaching process is 12.7%. First mix 400g of gold ore powder with a particle size of less than 200 mesh and 600ml of water in a 1L beaker, then add 60g of sodium hydroxide; turn on the mechanical stirring and adjust the stirring speed to 500 rpm, and the air volume to 180L / hour, stir After uniformity, the opening frequency is 20.0kHz, the power is 2kW, and the sound intensity is 3.3W / cm 3 Ultrasonic device for ultrasonic pretreatment. The cycle of ultrasonic pretreatment is 5 minutes of ultrasonic pretreatment and stop for 1 minute. During ultrasonic pretreatment, 1ml of hydrogen peroxide is added every half hour. After 1 hour of treatment, it is filtered, washed and dried for later use; Add 600ml of water, 1g of calcium oxide and 1.8g of sodium cyanide to 150g of the ore sample treated with sodium hydroxide. 3 Ultrasonic equipment is used for ultraso...

Embodiment 3

[0034] For a refractory gold ore, the gold grade is 3.23g / t, and the leaching rate obtained by direct conventional cyanidation leaching process is 12.7%. First mix 400g of gold ore powder with a particle size of less than 200 mesh and 600ml of water in a 1L beaker, then add 60g of sodium hydroxide; turn on the mechanical stirring and adjust the stirring speed to 500 rpm. The air flow rate is 180L / hour, and after stirring evenly, the opening frequency is 20.0kHz, the power is 2kW, and the sound intensity is 3.3W / cm 3 Ultrasonic device for ultrasonic pretreatment. The cycle of ultrasonic pretreatment is 5 minutes of ultrasonic pretreatment and stop for 1 minute. During ultrasonic pretreatment, 1ml of hydrogen peroxide is added every half hour. After 1 hour of treatment, it is filtered, washed and dried for later use; Add 600ml of water, 1g of calcium oxide and 2.7g of sodium cyanide to 150g of the ore sample treated with sodium hydroxide. 3 Ultrasonic equipment is used for ultr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Belonging to the technical field of wet metallurgy, the invention relates to an ultrasonic intensified leaching method for refractory gold ores and an ultrasonic intensified gold leaching stirrer. The method includes: firstly crushing gold ores to prepare an ore pulp, and then subjecting the ore pulp to pretreatment and leaching processes, in which ultrasonic intensified treatment is adopted. The ultrasonic intensified gold leaching stirrer includes a trough body, a feed inlet, a discharge port, a stirring structure, an ultrasonic structure and a ventilation structure. In the pretreatment and leaching processes, the method employs the ultrasonic method to perform intensified treatment on refractory gold ores, especially by adopting the ultrasonic method in the pretreatment process, the reaction time is shortened, and the leaching effect is intensified. The transmission shaft and stirring impellers of the ultrasonic intensified gold leaching stirrer deviate from the trough body center, thus effectively preventing the swirling phenomena, being beneficial to uniform mixing of solid-liquid-gas phase, and increasing the mass transfer rate.

Description

technical field [0001] The invention relates to a method for ultrasonically intensified leaching of refractory gold ore and an ultrasonically intensified gold leaching stirrer, belonging to the technical field of hydrometallurgy. Background technique [0002] Due to its excellent performance, gold has also been widely used in modern high-tech industries, such as electronics, communications, aerospace, chemical, medical and other technical fields. With the continuous increase in the mining of gold mineral resources, the reserves of high-grade and easy-to-treat gold mines are increasingly depleted, and refractory gold mines will become an important resource for the gold industry in the future. How to effectively and sustainably develop and utilize refractory gold mines is a technical problem that my country's gold industry urgently needs to solve. [0003] Among the proven gold geological reserves in my country, about 1,000 tons belong to the pyrite / arsenopyrite-wrapped refra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B3/02C22B3/12C22B11/08
CPCY02P10/20
Inventor 王仕兴张利波彭金辉崔维
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap