Adhesive for iodine polarizer, preparation method of adhesive and iodine polarizer

A technology for adhesives and polarizers, applied in the direction of monocarboxylate copolymer adhesives, adhesives, polarizing elements, etc., can solve the problems that the performance of iodine-based polarizers does not meet the requirements of electronic products, so as to improve optical performance and application The effect of range extension

Active Publication Date: 2015-03-11
佛山纬达光电材料股份有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to provide an adhesive for iodine-based polarizers and its preparation method and iodine-based polarizers, aiming to solve the problem that the performance of iodine-based polarizers does not meet the requirements of electronic products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive for iodine polarizer, preparation method of adhesive and iodine polarizer
  • Adhesive for iodine polarizer, preparation method of adhesive and iodine polarizer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Formula of two adhesive layers in iodine-based polarizer:

[0050] The adhesive formulation of the first adhesive layer is (by weight): 1.9% of JV company’s J-type adhesive raw material; pure water 97%; H 3 BO 3 0.4%; Ethylene Glycol: 0.3%; Glyoxal: 0.3%; Exp 0.1%; The viscosity of the adhesive formulated according to the content of the above components is 11-14cps.

[0051] The adhesive formulation of the second adhesive layer is (by weight): 1.9% of JV company’s J-type adhesive raw material; 97% of pure water; H 3 BO 3 0.4%; Ethylene Glycol 0.3%; Glyoxal 0.3%; Exp 0.1%; The viscosity of the prepared adhesive is 11-14cps.

Embodiment 2

[0053] Formula of two adhesive layers in iodine-based polarizer:

[0054]The adhesive formulation of the first adhesive layer is (by weight): 3.5% of the J-type adhesive material of JV Company; 95% of pure water; H 3 BO 3 0.4%; ethylene glycol 0.3%; glyoxal 0.3%; Exp 0.5%, the viscosity of the prepared adhesive is 13-18cps.

[0055] The adhesive formulation of the second adhesive layer is (by weight): 3.5% of the J-type adhesive raw material of JV Company; 95% of pure water; 3 BO 3 0.4%; Ethylene Glycol 0.3%; Glyoxal 0.3%; Exp 0.5%; The viscosity of the prepared adhesive is 13-18cps.

Embodiment 3

[0057] Formula of two adhesive layers in iodine-based polarizer:

[0058] The adhesive formula of the first adhesive layer is (by weight): 7% of the J-type adhesive material of JV Company, 91% of pure water, H 3 BO 3 : 0.2%, ethylene glycol: 0.2%, glyoxal: 0.1%, Exp: 1.5%, the viscosity of the adhesive after preparation is 35-43cps.

[0059] The adhesive formula of the second adhesive layer is (by weight): 7% of the J-type adhesive material of JV Company, 91% of pure water, H 3 BO 3 : 0.2%, ethylene glycol: 0.2%, glyoxal: 0.1%, Exp: 1.5%, the viscosity after preparation is 35-43cps.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an adhesive for an iodine polarizer, a preparation method of the adhesive and the iodine polarizer. The adhesive is prepared from the following components in percentage by weight: 1.9-7 percent of an adhesive raw material, 90-97 percent of pure water, 0.2-0.5 percent of a crosslinking agent, 0.1-3.5 percent of EXP, 0.2-0.5 percent of ethylene glycol and 0.1-1 percent of glyoxal. With adoption of the adhesive, the purpose that the iodine polarizer is durable in the performance is achieved. After the adhesive is adhered to a PVA film, in the drying process, iodine ions in the PVA film can be better fixed and kept in an ordered chain state under the condition of 95 DEG C*500H and high temperature and high humidity of 65 DEG C*95 percent*1000H, so that the variation of the optical stability of the polarizer is no larger than 5 percent after and before a test under the conditions, the application range of the corresponding iodine polarizer is expanded, and the optical performance of an electronic product which applies the iodine polarizer is also improved.

Description

technical field [0001] The invention relates to the technical field of polarizer preparation, in particular to an adhesive for an iodine-based polarizer, a preparation method thereof, and an iodine-based polarizer. Background technique [0002] At present, the durability test performance of optical products for general-purpose iodine-based polarizers can only be achieved at dry temperature: 80°C*500H, high temperature and high humidity: 60°C*90%*500H, and the application range of iodine-based polarizers with this capability is relatively narrow , which can only be used on daily ordinary consumer products. [0003] However, with the increasing popularity of electronic products, polarizers used in mobile phones and car displays generally require dry temperature: 90°C*500H, high temperature and high humidity: 65°C*95%*500H, and now large Only dye-based polarizers meet the requirements, but it is difficult to achieve an optical transmittance of more than 42% and a degree of pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J201/00C09J131/04C09J11/04C09J11/06G02B5/30
Inventor 廖剑能
Owner 佛山纬达光电材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com