A kind of antioxidant binder composition with ultraviolet absorbing function

A binder and composition technology, applied in the direction of non-polymer organic compound adhesives, adhesives, non-polymer adhesive additives, etc., to improve the ability to absorb ultraviolet rays, excellent resistance to ultraviolet radiation, and modified adhesion Effect

Active Publication Date: 2017-03-08
威海博浪游艇有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are still many problems in the temperature control effect and oxidation resistance of the existing anti-oxidation binders, which still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] An anti-oxidation binder composition, the binder composition is made up of the following raw materials in parts by weight:

[0043] Styrene-acrylic acid copolymer emulsion 10 parts

[0044] 4 parts PVC resin

[0045] Alkyd resin 5 parts

[0046] Distyrylphenol polyoxyethylene ether 1 part

[0047] 1 part asiaticoside

[0048] 1,8-dihydroxy-3-hydroxymethylanthraquinone 6 parts

[0049] 5 parts of 3-phenyl-2-propyl acrylate

[0050] 1 part of 2-thiophenethanol

[0051] 0.2 parts of 3-nonen-2-one

[0052] Phthalocyanine blue 0.1 parts

[0053] Zirconia powder 1 part

[0054] Chitin 0.8 parts

[0055] 1 part phenyl phthalate

[0056] 1 part dispersant

[0057] 40 parts of deionized water.

Embodiment 2

[0059] An anti-oxidation binder composition, the binder composition is made up of the following raw materials in parts by weight:

[0060] Styrene-acrylic copolymer emulsion 15 parts

[0061] 12 parts of PVC resin

[0062] Alkyd resin 10 parts

[0063] Distyrylphenol polyoxyethylene ether 3 parts

[0064] 4 parts asiaticoside

[0065] 12 parts of 1,8-dihydroxy-3-hydroxymethylanthraquinone

[0066] 3-phenyl-2-propyl acrylate 10 parts

[0067] 2 parts of 2-thiophenethanol

[0068] 1 part of 3-nonen-2-one

[0069] Phthalocyanine blue 0.5 parts

[0070] 3 parts zirconia powder

[0071] Chitin 5 parts

[0072] Phenyl o-hydroxybenzoate 3 parts

[0073] Dispersant 5 parts

[0074] 50 parts of deionized water.

Embodiment 3

[0076] An anti-oxidation binder composition, the binder composition is made up of the following raw materials in parts by weight:

[0077] Styrene-acrylic copolymer emulsion 12 parts

[0078] PVC resin 8 parts

[0079] 8 parts alkyd resin

[0080] Distyrylphenol polyoxyethylene ether 2 parts

[0081] 3 parts asiaticoside

[0082] 1,8-dihydroxy-3-hydroxymethylanthraquinone 8 parts

[0083] 3-Phenyl-2-Propyl Acrylate 7 parts

[0084] 1.5 parts of 2-thiophenethanol

[0085] 0.6 parts of 3-nonen-2-one

[0086] Phthalocyanine blue 0.3 parts

[0087] Zirconia powder 2 parts

[0088] Chitin 2 parts

[0089] Phenyl o-hydroxybenzoate 2 parts

[0090] dispersant 3 parts

[0091] 45 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an antioxidative binding agent combination with an ultraviolet absorption function. The antioxidative binding agent combination comprises resin of different types and additives of different types, and by means of combining all the components, the binding agent combination has the good performance of resisting ultraviolet radiation and changes of temperature difference.

Description

technical field [0001] The invention relates to an anti-oxidation adhesive composition with ultraviolet absorbing function. Background technique [0002] With the rapid development of my country's material field, a large number of new composite materials with excellent properties are widely used in infrastructure such as buildings, railways, and highways, aerospace, medical, home appliances, and other fields. Numerous functional binders have also emerged as the times require. Among many functional adhesives, the anti-oxidation and anti-ultraviolet adhesive is an important functional adhesive. Its function is to control the temperature change and oxidation of the adhesive caused by the ultraviolet radiation of sunlight in the external environment. The binder provides anti-aging and oxidation protection. There are still many problems in the temperature control effect and oxidation resistance of the existing anti-oxidation binders, which still need to be improved. Contents ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J4/02C09J4/06C09J11/06C09J11/04
Inventor 杜懿芳阎新东张伟志
Owner 威海博浪游艇有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap