Oxidation-resistant binder composition

A binder and composition technology, applied in the direction of adhesives, adhesive types, hydrocarbon copolymer adhesives, etc., to achieve the effects of modifying adhesion, improving the ability to absorb ultraviolet rays, and improving temperature resistance

Active Publication Date: 2015-09-09
永清霍尔茨门业有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are still many problems in the temperature control effect and oxidation re

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] An anti-oxidation binder composition, the binder composition is made up of the following raw materials in parts by weight:

[0043] Styrene-acrylic copolymer emulsion 15 parts

[0044] Fluorine resin 8 parts

[0045] Alkyd resin 10 parts

[0046] Distyrylphenol polyoxyethylene ether 3 parts

[0047] Glycerin Triglyceride 5 parts

[0048] Organic fluorosilicone resin 10 parts

[0049] 3-phenyl-2-propyl acrylate 10 parts

[0050] Diethylene glycol butyl ether 2 parts

[0051] 1 part of 3-nonen-2-one

[0052] Phthalocyanine blue 0.5 parts

[0053] 3 parts zirconia powder

[0054] Silica powder 5 parts

[0055] Phenyl o-hydroxybenzoate 1-3 parts

[0056] Dispersant 1-5 parts

[0057] 40-50 parts of deionized water.

Embodiment 2

[0059] An anti-oxidation binder composition, the binder composition is made up of the following raw materials in parts by weight:

[0060] Styrene-acrylic acid copolymer emulsion 10 parts

[0061] Fluorine resin 4 parts

[0062] Alkyd resin 5 parts

[0063] Distyrylphenol polyoxyethylene ether 1 part

[0064] Glycerin Triglyceride 2 parts

[0065] Organic fluorosilicone resin 5 parts

[0066] 5 parts of 3-phenyl-2-propyl acrylate

[0067] Diethylene glycol butyl ether 1 part

[0068] 0.2 parts of 3-nonen-2-one

[0069] Phthalocyanine blue 0.1 parts

[0070] Zirconia powder 1 part

[0071] Silica powder 1 part

[0072] 1 part phenyl phthalate

[0073] 1 part dispersant

[0074] 40 parts of deionized water.

Embodiment 3

[0076] An anti-oxidation binder composition, the binder composition is made up of the following raw materials in parts by weight:

[0077] Styrene-acrylic copolymer emulsion 12 parts

[0078] Fluorine resin 6 parts

[0079] 8 parts alkyd resin

[0080] Distyrylphenol polyoxyethylene ether 2 parts

[0081] Glycerin Triglyceride 3 parts

[0082] Organic fluorosilicone resin 8 parts

[0083] 3-Phenyl-2-Propyl Acrylate 7 parts

[0084] Diethylene glycol butyl ether 1.5 parts

[0085] 0.6 parts of 3-nonen-2-one

[0086] Phthalocyanine blue 0.3 parts

[0087] Zirconia powder 2 parts

[0088] Silica powder 3 parts

[0089] Phenyl o-hydroxybenzoate 2 parts

[0090] dispersant 3 parts

[0091] 45 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an oxidation-resistant binder composition. The oxidation-resistant binder composition comprises different types of resin and auxiliaries. The oxidation-resistant binder composition with various components which are combined with one another has the advantages of excellent ultraviolet radiation resistance and temperature difference change resistance.

Description

technical field [0001] The invention relates to an anti-oxidation binder composition. Background technique [0002] With the rapid development of my country's material field, a large number of new composite materials with excellent properties are widely used in infrastructure such as buildings, railways, and highways, aerospace, medical, home appliances, and other fields. Numerous functional binders have also emerged as the times require. Among many functional adhesives, the anti-oxidation and anti-ultraviolet adhesive is an important functional adhesive. Its function is to control the temperature change and oxidation of the adhesive caused by the ultraviolet radiation of sunlight in the external environment. The binder provides anti-aging and oxidation protection. There are still many problems in the temperature control effect and oxidation resistance of the existing anti-oxidation binders, which still need to be improved. Contents of the invention [0003] In order to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J125/14C09J127/12C09J167/08C09J183/08C09J11/08C09J11/04C09J11/06
Inventor 周美琴
Owner 永清霍尔茨门业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap