A kind of preparation method of helical columnar polypyrrole

A polypyrrole and columnar technology is applied in the field of preparation of polypyrrole, which can solve the problems of unfavorable polypyrrole product performance improvement, promotion and application, increased synthesis process complexity, mechanical or chemical damage, etc., so as to avoid mechanical or chemical damage, manufacture Low cost and stable product performance

Inactive Publication Date: 2017-06-09
SOUTHWEST JIAOTONG UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The synthesis method of this helical polypyrrole product needs to make a hard template in advance, which increases the complexity of the synthesis process. Or chemical damage, these are not conducive to the performance improvement and application of polypyrrole products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of helical columnar polypyrrole
  • A kind of preparation method of helical columnar polypyrrole
  • A kind of preparation method of helical columnar polypyrrole

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of preparation method of helical columnar polypyrrole, its concrete practice is:

[0027] A, preparation of hydrosol: add sodium indigo disulfonate into distilled water, stir to fully dissolve sodium indigo disulfonate, obtain sodium indigo disulfonate hydrosol, and the molar concentration of sodium indigo disulfonate in the hydrosol is 0.0050 mol / L;

[0028] B. Preparation of the reaction mixture: take 180ml of the hydrosol obtained in step a, then add 1.38ml of pyrrole, and then magnetically stir for 15min in an ice bath until the temperature of the mixture drops to 0°C to obtain the reaction mixture;

[0029] C, the preparation of initiator solution: FeCl 3 ·6H 2 O was added to distilled water and stirred well until the FeCl 3 ·6H 2 O is completely dissolved, and the initiator solution is obtained, in which FeCl 3 The molar concentration is 0.05mol / L;

[0030] D. Pyrrole polymerization reaction: 20 ml of the initiator solution prepared in step c was adde...

Embodiment 2

[0033] A kind of preparation method of helical columnar polypyrrole, its concrete practice is:

[0034] A, preparation of hydrosol: add sodium indigo disulfonate into distilled water, stir to fully dissolve sodium indigo disulfonate, obtain sodium indigo disulfonate hydrosol, and the molar concentration of sodium indigo disulfonate in the hydrosol is 0.0025 mol / L;

[0035] B. Preparation of the reaction mixture: take 180ml of the hydrosol obtained in step a, then add 1.38ml of pyrrole, and then magnetically stir for 25min in an ice bath until the temperature of the mixture drops to 5°C to obtain the reaction mixture;

[0036] C, the preparation of initiator solution: FeCl 3 ·6H 2 O was added to distilled water and stirred well until the FeCl 3 ·6H 2 O is completely dissolved, and the initiator solution is obtained, in which FeCl 3 The molar concentration is 0.05mol / L;

[0037] D. Polymerization of pyrrole: 20 ml of the initiator solution prepared in step c was added drop...

Embodiment 3

[0040] A kind of preparation method of helical columnar polypyrrole, its concrete practice is:

[0041] A, preparation of hydrosol: add sodium indigo disulfonate into distilled water, stir to fully dissolve sodium indigo disulfonate, obtain sodium indigo disulfonate hydrosol, and the molar concentration of sodium indigo disulfonate in the hydrosol is 0.0050 mol / L;

[0042]B. Preparation of the reaction mixture: take 180ml of the hydrosol obtained in step a, then add 1.38ml of pyrrole, and then magnetically stir for 20min in an ice bath until the temperature of the mixture drops to 3°C to obtain the reaction mixture;

[0043] C, the preparation of initiator solution: FeCl 3 ·6H 2 O was added to distilled water and stirred well until the FeCl 3 ·6H 2 O is completely dissolved, and the initiator solution is obtained, in which FeCl 3 The molar concentration is 0.07mol / L;

[0044] D. Polymerization of pyrrole: 20 ml of the initiator solution prepared in step c was added dropw...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A kind of preparation method of helical columnar polypyrrole, its practice mainly is: the molar concentration of A, preparation sodium indigo disulfonate is the hydrosol of 0.0025-0.0075mol / L; B, get hydrosol 180ml, then add 1.38ml pyrrole, in 0-7 DEG C of magnetic stirring under ice bath conditions for 15-25min to obtain a reaction mixture; C, preparation of FeCl Molar concentration is 0.03-0.15mol / L initiator solution; D, 20ml of initiator solution is added dropwise in the reaction mixture, Under the condition of 0-7°C in an ice bath, magnetically stirred and reacted for 4.5-9 hours, and the solid was obtained by suction filtration; E, washed and dried, and obtained. The helical columnar polypyrrole prepared by the method has a diameter of micrometer to nanometer order, has better magnetic loss effect and nanometer loss effect on electromagnetic waves, and has simple preparation process, low manufacturing cost and stable product performance.

Description

technical field [0001] The invention relates to a preparation method of polypyrrole, in particular to a preparation method of polypyrrole with helical columnar microscopic morphology. Background technique [0002] In the last 20 to 30 years, conductive polymers have gradually developed into a research field with great research value and much attention. Among them, polypyrrole is a conductive polymer with a π-conjugated structure. It has high practical application value due to its good thermal and chemical stability, high electrical conductivity, and easy synthesis. , can be widely used in the development of sensor materials, metal anti-corrosion materials, absorbing materials and other functional materials. The popularization and application effect of polypyrrole in the above functional materials field is directly affected by its physical properties, while the physical properties of polypyrrole are mainly affected by its chemical structure factors such as its doping degree,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G73/06
Inventor 胡书春李燕斌韩洪川屈圆圆蒋彦嫚肖达张玲玲翟晶
Owner SOUTHWEST JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com