A kind of antistatic environment-friendly coated fabric and preparation method thereof

A coated fabric, an environmentally friendly technology, applied in the field of antistatic and environmentally friendly coated fabrics and their preparation, can solve the problems of coated fabrics without flame retardancy, antistatic and wear resistance, poor functionality, and no preparation methods, etc., to achieve Avoid oven contact, good color fastness and good product quality

Active Publication Date: 2017-05-17
苏州格洛博纺织有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the coated fabric disclosed in this patent has good transparency, good gloss, soft hand feeling, and excellent fastness, which improves the aesthetic feeling and performance of the fabric, the coated fabric has no properties such as flame retardancy, antistatic and wear resistance. It can only be used in a simple environment, has poor functionality, and has no preparation method. Therefore, it is necessary to design an antistatic environmentally friendly coated fabric and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antistatic environment-friendly coated fabric and preparation method thereof
  • A kind of antistatic environment-friendly coated fabric and preparation method thereof
  • A kind of antistatic environment-friendly coated fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The preparation method of the antistatic environment-friendly coated fabric comprises the following steps:

[0051] a. Take the required raw materials by the mass parts of the above components;

[0052] b. Add polyurethane resin, silicone resin, fluororubber and toluene to an ordinary mixer, the stirring time is 10min, and the stirring speed is 300r / min;

[0053] c. Add the cross-linking agent, antistatic agent, magnesium oxide and dyes to the ordinary mixer, the stirring time is 3min, the stirring speed is 100r / min, and the coating liquid is obtained;

[0054] d. Spray the coating liquid evenly on the release paper through an ordinary spray gun, and the spray thickness is 0.12mm;

[0055] e. Put the release paper sprayed with the coating liquid into the ordinary drying equipment to dry, the drying temperature is 90 ℃, and the drying time is 8 minutes, and the reinforcement layer can be obtained;

[0056] f. The base fabric layer and the reinforcing layer are laminate...

Embodiment 2

[0064] The preparation method of the antistatic environment-friendly coated fabric comprises the following steps:

[0065] a. Take the required raw materials by the mass parts of the above components;

[0066] b. Add polyurethane resin, silicone resin, fluororubber and toluene to an ordinary mixer, the stirring time is 12min, and the stirring speed is 350r / min;

[0067] c. Add the cross-linking agent, antistatic agent, magnesium oxide and dyes to the common mixer, the stirring time is 4min, the stirring speed is 120r / min, and the coating liquid is obtained;

[0068] d. Spray the coating liquid evenly on the release paper through an ordinary spray gun, and the spray thickness is 0.126mm;

[0069] e. Put the release paper sprayed with the coating liquid into the ordinary drying equipment to dry, the drying temperature is 100 ℃, and the drying time is 10 minutes, and the reinforcement layer can be obtained;

[0070] f. The base fabric layer and the reinforcing layer are laminat...

Embodiment 3

[0078] The preparation method of the antistatic environment-friendly coated fabric comprises the following steps:

[0079] a. Take the required raw materials by the mass parts of the above components;

[0080] b. Add polyurethane resin, silicone resin, fluororubber and toluene to an ordinary mixer, the stirring time is 15min, and the stirring speed is 400r / min;

[0081] c. Add the cross-linking agent, antistatic agent, magnesium oxide and dyes to the common mixer, the stirring time is 5min, the stirring speed is 150r / min, and the coating liquid is obtained;

[0082] d. Spray the coating liquid evenly on the release paper through an ordinary spray gun, and the spray thickness is 0.18mm;

[0083] e. Put the release paper sprayed with the coating liquid into the ordinary drying equipment for drying, the drying temperature is 110°C, and the drying time is 12 minutes, and the reinforcement layer can be obtained;

[0084] f. The base fabric layer and the reinforcing layer are lami...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides anti-static environment-friendly coating fabric and a preparing method thereof. The technical problems that existing coating fabric does not have flame-retardant, anti-static and wear-resisting properties, can be only applied to simple environment and is poor in functionality, and a preparing method does not exist are solved. The anti-static environment-friendly coating fabric comprises a base cloth layer. A reinforcing layer is fixed to the base cloth layer. The reinforcing layer is prepared from, by mass, 85-100 parts of polyurethane resin, 30-40 parts of organic silicon resin, 10-15 parts of fluorous rubber, 2-4 parts of cross-linking agents, 6-10 parts of anti-static agents, 6-8 parts of magnesium oxide, 25-30 parts of methylbenzene and 3-5 parts of dyestuff. The coating fabric has the advantages of being high in functionality and good in quality.

Description

technical field [0001] The invention relates to a coated fabric, in particular to an antistatic and environment-friendly coated fabric and a preparation method thereof. Background technique [0002] Fabric is a product made of textile fibers and yarns, which is soft and has certain mechanical properties and thickness, which is what people usually call textiles. There are also changes in the thickness direction of the fabric, which is a typical three-dimensional structure, but the fabric is generally regarded as two-dimensional, such as the usual woven, knitted, knitted, and non-woven fabrics. The coating on the surface of the fabric is called coated fabric. Coated fabric is a kind of textile. The coating adhesive material forms a single-layer or multi-layer coating in situ on one side of the fabric or on the front and back sides. It consists of two or more layers. Composition of materials in which at least one layer is a textile and the other layer is a fully continuous pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/02B32B27/08B32B27/40B32B27/18B32B37/10B32B37/00B32B38/00B32B38/16C08L75/04C08L83/04C08L27/12C08K13/02C08K3/22
CPCB32B5/02B32B27/40B32B37/00B32B37/10B32B38/00B32B38/16B32B2262/0261B32B2262/0292B32B2307/21C08L75/04C08L2201/02C08L2201/04C08L2205/03C08L83/04C08L27/12C08K13/02C08K2003/222
Inventor 马耀祥吴新初
Owner 苏州格洛博纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap