Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Technology for recycling lithium hydroxide from solution through bipolar membrane method

A lithium hydroxide, bipolar membrane technology, applied in the direction of electrolysis process and electrolysis components, can solve the problems of long production process, high operation cost, environmental pollution, etc. The effect of secondary pollution

Active Publication Date: 2015-12-16
HANGZHOU BLUETEC ENVIRONMENTAL TECH
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the lithium industrial production process, it is necessary to concentrate lithium sulfate to more than 12%, then add sodium hydroxide, and then undergo crystallization and purification to make lithium hydroxide. The production process is relatively long, which has certain pollution to the environment and high operating costs. economy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Technology for recycling lithium hydroxide from solution through bipolar membrane method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] Lithium sulfate solution is mainly derived from the by-products produced in the production of lithium iron sulfate batteries, with a concentration ranging from 5-20%. Mainly contains lithium sulfate and some Fe 3+ , enter the system for processing.

[0024] With reference to the accompanying drawings, the lithium sulfate solution entering the process of the present invention is first processed in step (1): the lithium sulfate solution is treated with an ultrafiltration system and ion exchange, mainly to remove divalent and more than divalent metal ions; after pretreatment Finally, the parameters of the purified lithium sulfate solution are as follows: control iron ions below 1mg / l, calcium and magnesium ions below 1mg / l, COD below 5mg / l, bicarbonate below 20mg / l, silicon dioxide If it is lower than 5mg / l, the concentration of lithium sulfate is 5-20% (mass percentage), the water produced in the pretreatment system enters the treatment of step (2), and the concentrated ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a technology for recycling lithium hydroxide from a solution through a bipolar membrane method. By means of the technology, the lithium sulfate solution is processed through a bipolar membrane system, and produced water produced through the bipolar membrane system is lithium hydroxide and sulfuric acid. By means of the technology, the environment pollution problem is solved, alkali and acid consumption is reduced, cleaner production, energy saving and emission reduction are achieved, and operating cost is lowered.

Description

technical field [0001] The invention relates to a technology for recovering lithium hydroxide from a solution by a bipolar membrane method. Background technique [0002] Lithium hydroxide is a white monoclinic fine crystal, with a spicy taste and strong alkalinity. It can absorb carbon dioxide and water in the air. It is soluble in water, slightly soluble in ethanol, and insoluble in ether. The pH of 1mol / L solution is about 14, the relative density is 1.51, the melting point is 471°C (anhydrous), and the boiling point is 925°C (decomposition). , corrosive. Lithium hydroxide can be used as a developing agent for spectral analysis, lubricating oil, and an additive for alkaline battery electrolytes, which can increase the capacitance by 12% to 15%, and increase the service life by 2 to 3 times. [0003] In the lithium industrial production process, it is necessary to concentrate lithium sulfate to more than 12%, then add sodium hydroxide, and then undergo crystallization and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25B1/20
Inventor 黄伟平楼永通李嘉陈良
Owner HANGZHOU BLUETEC ENVIRONMENTAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com