High-temperature additive for cold rolling of aluminum, and preparation and application thereof

A technology of high-temperature additives and aluminum rolling, applied in the direction of additives, thickeners, petroleum industry, etc., can solve problems such as insufficient lubrication of oil products, achieve the effects of reducing the probability of occurrence, improving high-temperature performance, and easy cleaning

Active Publication Date: 2016-04-27
CHINALCO LUBRICANT TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Aiming at the deficiencies of the existing technology, the purpose of the present invention is to propose a high-temperature additive for aluminum cold rolling to solve the problem of insufficient lubrication of oil products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature additive for cold rolling of aluminum, and preparation and application thereof
  • High-temperature additive for cold rolling of aluminum, and preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The present invention is used for preparing the system of high temperature additive for aluminum cold rolling such as figure 1 , including a reaction kettle 1, a feed pipe 2, the feed pipe 2 is connected with a drying room 3, and the drying room is heated with hot water at a temperature of 80°C. The feed pipe 2 is also connected with a base oil feed port 4 and an antioxidant feed port 5 .

[0045] The reaction kettle 1 has a jacket, and the inlet 6 and the outlet of the boiler return water are arranged on the jacket, and the temperature of the boiler return water is 45°C. There is a stirring device in the reaction kettle 1. According to the total mass of reactants, 1000kg is stirred for about 30-50 minutes.

[0046]The side of the reaction kettle away from the raw material inlet is connected to a vacuum pump 9 and a buffer tank 10 through a pipeline, and the vacuum pump 9 is used for vacuum suction. The bottom of the reaction kettle 1 is provided with a discharge filt...

Embodiment 2

[0049] Equipment and preparation steps are with embodiment 1. Aluminum cold rolling high-temperature additive formula: the mass percentages of low molecular weight thickener PB2400, antioxidant (composite antioxidant mixed with T501 and T534, etc.), base oil D90# are 50%, 1%, and 49% respectively .

Embodiment 3

[0054] Equipment and preparation steps are with embodiment 1. Aluminum cold rolling high-temperature additive formula: low molecular weight thickener PB1800, antioxidant is a composite antioxidant mixed with T501 and T534, and base oil D90#, the mass percentages of which are 70%, 3%, and 27% respectively .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Kinematic viscosityaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-temperature additive for rolling oil used in cold rolling of aluminum strips, which belongs to the field of lubricant compositions. The high-temperature additive is composed of a low-molecular-weight thickening agent, an anti-oxidant and base oil, wherein the anti-oxidant is one or more selected from the group consisting of a hindered phenol anti-oxidant, an aromatic amine anti-oxidant, an thiodipropionic diester anti-oxidant and a phosphite anti-oxidant, and the mass percentage contents of the low-molecular-weight thickening agent, the anti-oxidant and base oil are 4 to 80%, 0.01 to 3% and 17 to 95%, respectively. According to the invention, through reasonable adjustment of the ratio of low-molecular-weight thickening agent to anti-oxidant to base oil, integral high temperature performance of the rolling oil can be improved in cold rolling of aluminum strips without changing conventional base oil, composite additives and process; and the high-temperature additive has guaranteed high lubricity at a high temperature, is easy to clean and reduces occurrence probability of annealing oil marks.

Description

technical field [0001] The invention belongs to the field of lubricating compositions, and in particular relates to a lubricating agent composition containing aliphatic additives, a preparation method and application thereof. Background technique [0002] Cold rolling of aluminum sheet and strip is usually carried out in a 4-roll or 2-roll mill, and the raw material is hot-rolled billet or cast-rolled billet. Aluminum rolling oil is composed of base oil and compound additives. The base oil for cold rolling of aluminum plate and strip is mostly low-viscosity, light mineral oil. Moreover, the viscosity of the base oil for cold rolling of aluminum plate is slightly higher than that of aluminum foil, and the viscosity of base oil for high-speed rolling is slightly higher than that of aluminum foil. lower than low speed rolling. Products sometimes require finished annealing or intermediate annealing, which requires higher surface quality, including plate shape and surface bright...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M165/00C10M169/00C10N30/04C10N30/06C10N40/24
CPCC10M119/18C10M129/10C10M133/12C10M165/00C10M169/00C10M2207/026C10M2209/1036C10M2209/106C10M2215/06C10N2030/04C10N2030/06C10N2040/243C10N2040/245C10N2030/10C10N2030/02
Inventor 马清宇
Owner CHINALCO LUBRICANT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap