Black-body celadon body material, black-body celadon ware and production method of black-body celadon ware

Abstract

The invention discloses black-body celadon body material, black-body celadon ware and a production method of the black-body celadon ware. The black-body celadon body material comprises, by weight, 26-31 parts of Huangshixuan porcelain clay, 3-8 parts of Mudaikou Zijin clay, 1-6 parts of Gaojitou Zijin clay, 25-30 parts of Jindan porcelain clay and 22-27 parts of Baogeng porcelain clay. The black-body celadon ware using the body material is high in yield during firing and stable in quality and has the cinnabar color of pure Longquan porcelain. The black-body celadon ware is stable in quality, attractive and pure in color and high in yield.

Description

technical field [0001] The invention relates to a celadon base material, porcelain using the base material and a manufacturing method thereof, in particular to a black-bodied celadon base material, black-bodied celadon porcelain and a manufacturing method thereof. Background technique [0002] Black-bodied celadon is caused by the high iron content in the clay body. The amount of iron causes the color of the body to vary from gray to dark black; the glaze color is blue, with rich changes from light to dark; There are all lines; there are also the characteristics of purple mouth and iron feet. Historically, there are only a handful of kiln sites that produced this type of porcelain on a certain scale, mainly including the official kiln site in the suburbs of Hangzhou, the Laohudong kiln site, and the kiln sites in Longquan Dayao, Xikou, and Xiaomei. The prior art of porcelain glazes, such as the Chinese invention patent with the authorized announcement number CN103803949B, d...

AI Technical Summary

Problems solved by technology

A Yaozhou kiln tea foam glazed porcelain, the tea foam glazed porcelain includes a base material and a glaze, and the base material is composed of the following raw materials in parts by weight: 40-50 parts of Yucai crucible soil, 20-30 parts of Dongshan crucible soil , 15-30 parts of sand beam crucible; the glaze is composed of the following raw materials in parts by weight: 70-80 parts of black medicine soil, 5-10 parts of potassium feldspar, and 10-20 parts of kaolin. The technical content of the material configuration is high, the glaze is refined, the production process is difficult, and the firing range is extremely narrow. Folk kilns dare not easily lose money and try it.