Production method of sunken aventurine ceramic tile

A ceramic tile and placer gold technology, which is applied in the field of preparation of sunken placer gold tiles, can solve the problems of single color, low pattern contrast, and unnatural color of glazed tiles, and achieve the effect of rich colors, natural and delicate patterns, and easy control of density

Active Publication Date: 2017-02-01
成都新西南陶瓷艺术股份公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention overcomes the deficiencies of the prior art and provides a method for preparing sunken placer gold tiles, hoping to solve the problems of unnatural color, single color and low pattern contrast of glazed tiles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The target pattern is a pastoral style pattern obtained by photography, with basic colors: 1. Cyan (#33ff38), 2. Green (#1f8a22), 3. Rose red (#f917c1), 4. True red (#fe0713), 5 , yellow-green (#81fe07).

[0035] Matt glaze formula: K 2 2.8 parts of O, Na 2 O 1.5 parts, MgO 5.8 parts, CaO 22.5 parts, ZnO 2.7 parts, Al 2 o 3 1.6 parts, B 2 o 3 1.3 parts, SiO 2 47.5 parts, Zro 2 7.9 parts, TiO 2 6.4 parts; These ingredients are ball milled and pulped to obtain a matte glaze.

[0036] Dry Powder Glaze Recipe: K 2 O 2.8, Na 2 O 1.5 parts, Fe 2 o 3 0.5 parts, V 2 o 5 3.5 parts, MnO 2 5.4 parts, CaO17.5 parts, Al 2 o 3 11.7 parts, B 2 o 3 19.3 parts, SiO 2 37.8 parts; These components are ball milled and pulped to obtain a dry powder glaze with a particle size in the range of 80-120 μm.

[0037] Clean tile blanks, set aside.

[0038] The target pattern is peeled according to the above 5 basic colors. After peeling, each basic color forms a decom...

Embodiment 2

[0042] The target pattern is the pet pattern obtained by painting, with eight basic colors: four different shades of gray-black (#121212, #030303, #5C5C5C, #8B8B7A), two different shades of brown (#8B3E2F, 8B5742) , white (#FFFFFF), light yellow (#FFEFDF).

[0043] Matt glaze formula: K 2 O 4.2 parts, Na 2 O 3.1 parts, MgO 7.9 parts, CaO 8.6 parts, ZnO 6.4 parts, Al 2 o 3 0.7 parts, B 2 o 3 2.2 parts, SiO 2 60.4 parts, Zro 2 2.9 parts, TiO 2 3.6 parts; These ingredients are ball milled and pulped to obtain a matte glaze.

[0044] Dry Powder Glaze Recipe: K 2 O 2.8, Na 2 O 2.2 parts, Fe 2 o 3 2.1 parts, V 2 o 5 2.3 parts, MnO 2 4.6 parts, CaO11.9 parts, Al 2 o 3 15.7 parts, B 2 o 3 12.1 parts, SiO 2 46.3 parts; These components are ball milled and pulped to obtain a dry powder glaze with a particle size in the range of 80-120 μm.

[0045] Clean tile blanks, set aside.

[0046] The target pattern is peeled according to the above 8 basic colors. Af...

Embodiment 3

[0050] The target pattern is a pattern composed of different shades of blue obtained by painting, with 10 basic colors: blue with different shades (#87CEFF, #87CEFA, #87CEEB, #6495ED, #63B8FF, #4876FF, #4169E1, #1E90FF, #1C86EE, #1874CD).

[0051] Matt glaze formula and dry powder glaze formula are identical with embodiment 1.

[0052] Clean tile blanks, set aside.

[0053] The target pattern is peeled according to the above 10 basic colors. After peeling, each basic color forms a decomposed pattern, and the combination of 10 decomposed patterns can form a complete target pattern. Make screens according to the decomposed pattern corresponding to each basic color. In the screen production process, when the film is released, the quality of the decomposed pattern on each screen is 175 lines and 300 resolution. When the screen is drawn, the drug side of the film is placed upwards, and the screen is drawn. The slurry is water-sensitive. Light glue, sizing 3 times inside the scre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of a sunken aventurine ceramic tile. A target pattern is peeled according to different basic colors, an exposed pattern formed by each basic color is made into a screen plate and is converted into a bitmap, the exposed patterns are all carved to a roller, mat glaze is applied to a ceramic tile biscuit , and the screen plates and the roller are subjected to plate printing and roller printing respectively, and dry powder glaze is spread out then; an obtained ceramic tile stands at normal temperature until a glaze layer dries and is glaze-fired in a kiln to obtain the sunken aventurine ceramic tile with the target pattern. Ceramic tiles with rich color and a natural and fine pattern can be produced by using the method, the suitable dry powder glaze is attached to the glaze surface of each ceramic tile, and by controlling the quantity, addition position and density of the dry powder glaze, the ceramic tile can be imparted nature imitating crystal gloss or fancy color such that the ceramic tile pattern is natural and rough.

Description

technical field [0001] The invention relates to building material tiles, and more particularly, the invention relates to a method for preparing sunken placer gold tiles. Background technique [0002] Ceramic tile is an indispensable material and product in home decoration, and ceramic products rich in ceramic art are more popular among consumers. Nowadays, there are many brands of tiles on the market, and the types are rich. For example, the common types of tiles are divided into mosaics, glazed tiles, vitrified tiles or polished tiles according to the materials and production processes used. Ceramic glazed tiles are made of ceramic tiles. The surface is composed of a layer of glaze, which is fired at high temperature and high pressure. Due to the addition of glaze, the ceramic is more beautiful and popular among consumers. However, there are disadvantages such as unnatural color, single color, and low pattern contrast. Contents of the invention [0003] The invention ove...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/89C03C8/20C03C8/14B44C1/22
CPCB44C1/225C03C8/14C03C8/20C04B41/52C04B41/89C04B2235/963C04B41/5022
Inventor 徐素容李正久
Owner 成都新西南陶瓷艺术股份公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com