4-amino-2-sodium hydroxybenzoate synergistic polysiloxane defoaming agent

A technology of sodium hydroxybenzoate and phenylmethyl polysiloxane, which is applied in the direction of foam dispersion/prevention, chemical instruments and methods, liquid degassing, etc., and can solve the problem of complex raw material components and the amount of polysiloxane substances used Large and other problems, to achieve high economic and ecological benefits, low cost, and extend the storage period of validity

Active Publication Date: 2017-03-22
江门市冠达化工科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when preparing polysiloxane defoamers, it is usually necessary to add four basic components: active ingredient polysiloxane, emulsifier, carrier and thickener. The raw material components are more complex and polysiloxane heavy substance use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 4-amino-2-sodium hydroxybenzoate synergistic polysiloxane defoaming agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A 4-amino-2-hydroxybenzoate sodium synergistic polysiloxane defoamer, based on a total of 100 parts by weight, consists of the following parts by weight:

[0033] Polyborosiloxane: 0.1 part; Sodium 4-amino-2-hydroxybenzoate: 0.01 part;

[0034] Phenylmethyl polysiloxane: 0.6 parts; 4-methyl-2-hexanol: 10 parts;

[0035] Water: balance.

[0036] The preparation method of described defoamer is:

[0037] Add sodium 4-amino-2-hydroxybenzoate and higher aliphatic alcohol to a part of the solvent, heat up to 40°C, heat and stir for 1 minute;

[0038] Then slowly add polyborosiloxane under stirring, heat up to 60°C and then keep stirring for 3 minutes;

[0039] Continue to slowly add phenylmethyl polysiloxane under stirring, heat up to 70°C, and keep stirring for 10 minutes;

[0040] Finally, add the remaining solvent and stir slowly and cool down to room temperature to obtain a defoamer.

Embodiment 2

[0042] A 4-amino-2-hydroxybenzoate sodium synergistic polysiloxane defoamer, based on a total of 100 parts by weight, consists of the following parts by weight:

[0043] Polyborosiloxane: 1 part; Sodium 4-amino-2-hydroxybenzoate: 10 parts;

[0044] Phenylmethyl polysiloxane: 1 part; 3-heptanol: 10 parts;

[0045] Isomerized tridecanol: 15 parts; water: balance.

[0046] The preparation method of described defoamer is:

[0047] Add sodium 4-amino-2-hydroxybenzoate and higher aliphatic alcohol to a part of the solvent, heat up to 50°C, heat and stir for 2 minutes;

[0048] Then slowly add polyborosiloxane under the action of stirring, heat up to 65°C, and then heat and stir for 5 minutes;

[0049] Continue to slowly add phenylmethylpolysiloxane under stirring, heat up to 75°C, and keep stirring for 20 minutes;

[0050] Finally, add the remaining solvent and stir slowly and cool down to room temperature to obtain a defoamer.

Embodiment 3

[0052] A 4-amino-2-hydroxybenzoate sodium synergistic polysiloxane defoamer, based on a total of 100 parts by weight, consists of the following parts by weight:

[0053] Polyborosiloxane: 0.2 part; Sodium 4-amino-2-hydroxybenzoate: 1 part;

[0054] Phenylmethyl polysiloxane: 0.6 parts; 4-methyl-2-hexanol: 5 parts;

[0055] 3-heptanol: 5 parts; isomeric tridecanol: 5 parts; 2-hexyldecanol: 5 parts;

[0056] Myristyl alcohol: 5 parts; water: the balance.

[0057] The preparation method of described defoamer is:

[0058] Add sodium 4-amino-2-hydroxybenzoate and higher aliphatic alcohol to a part of the solvent, heat up to 40°C, heat and stir for 1 minute;

[0059] Then slowly add polyborosiloxane under stirring, heat up to 60°C and then keep stirring for 3 minutes;

[0060] Continue to slowly add phenylmethyl polysiloxane under stirring, heat up to 75°C, and keep stirring for 10 minutes;

[0061] Finally, add the remaining solvent and stir slowly and cool down to room temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
kinematic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of textile assistants, and discloses a 4-amino-2-sodium hydroxybenzoate synergistic polysiloxane defoaming agent. The 4-amino-2-sodium hydroxybenzoate synergistic polysiloxane defoaming agent is prepared from the following components based on 100 parts by weight: 0.1 to 1 part of polyborosiloxane, 0.01 to 10 parts of 4-amino-2-sodium hydroxybenzoate, 0.6 to 1 part of phenyl methicone, 10 to 25 parts of higher aliphatic alcohol and the balance of a solvent. By the adding of 4-amino-2-sodium hydroxybenzoate synergistic polysiloxane serving as the physical and chemical property of the defoaming agent, extremely good foam distinction and inhibition effects can be achieved with the extremely small amount of the defoaming agent, and the adding amount of polysiloxane is obviously reduced; furthermore, the stability of the defoaming agent is improved, and the storage effective period of the polysiloxane defoaming agent is prolonged; the resistance to high temperature, the resistance to acid and alkali and the resistance to shearing of the synergistic polysiloxane can be further improved.

Description

[0001] Technical field: [0002] The invention relates to the technical field of textile auxiliaries, in particular to a 4-amino-2-hydroxybenzoate sodium synergistic polysiloxane defoamer. [0003] Background technique: [0004] The surfactant is adsorbed on the gas-liquid interface, causing the surface tension of the liquid surface to decrease, thereby increasing the gas-liquid contact surface, so that the bubbles are not easy to merge. The relative density of the bubbles is much smaller than that of the liquid itself. When the rising bubbles pass through the liquid surface, they absorb a layer of surfactant molecules on the liquid surface. Therefore, the bubble film with adsorbed surfactant exposed in the air is different from the bubble film in the solution. It contains two layers of surfactant molecules to form a bimolecular film, and the adsorbed surfactant has protection for the liquid film. effect. The defoamer is to destroy and inhibit the formation of this film. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D19/04
CPCB01D19/0409
Inventor 付淑珍
Owner 江门市冠达化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com