A kind of preparation method with diamagnetic chain coordination polymer

A coordination polymer, diamagnetic technology, applied in chemical instruments and methods, luminescent materials, etc., can solve problems such as materials lacking magnetic properties, and achieve good thermal stability and diamagnetic stability.

Active Publication Date: 2019-08-09
LIAONING UNIVERSITY OF PETROLEUM AND CHEMICAL TECHNOLOGY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the prior art, there is a lack of research on materials whose magnetic properties can be controlled by temperature, especially the research on complex materials whose structure is not destroyed even when the temperature reaches 200°C.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method with diamagnetic chain coordination polymer
  • A kind of preparation method with diamagnetic chain coordination polymer
  • A kind of preparation method with diamagnetic chain coordination polymer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 1 mmol Zn(NO 3 ) 2 6(H 2 O), 1 mmol of isophthalic acid-5-sodium sulfonate, and 1 mmol of 4,4'-bipyridine were dissolved in a mixed solution of 20 mL of water and ethanol, the volume ratio of water and ethanol was 1:1, and encapsulated in After heating in the reactor for 3 days, the temperature was lowered to room temperature until a colorless massive single crystal was precipitated to obtain complex 1 with a yield of 92%.

Embodiment 2

[0025] 0.5 mmol Zn(NO 3 ) 2 6(H 2 O), 1 mmol isophthalic acid-5-sodium sulfonate, and 1.5 mmol 4,4'-bipyridine were dissolved in a mixed solution of 15 mL water and ethanol, the volume ratio of water and ethanol was 1:1, and encapsulated in After heating in the reactor for 4 days, the temperature was lowered to room temperature until a colorless massive single crystal was precipitated, and the yield was 90%.

Embodiment 3

[0027] 1 mmol Zn(NO 3 ) 2 6(H 2 O), 1.5 mmol isophthalic acid-5-sodium sulfonate, and 1.5 mmol 4,4'-bipyridine were dissolved in 15 mL of a mixed solution of water and ethanol, the volume ratio of water and ethanol was 1:1, and encapsulated in After heating in the reactor for 3 days, the temperature was lowered to room temperature until a colorless massive single crystal was precipitated, and the yield was 88%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
magnetic susceptibilityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a diamagnetic chain-shaped coordination polymer. The method comprises the following steps: dissolving 0.5-1.5mmol of Zn(NO3)2.6(H2O), 0.5-1.5mmol of 5-sulfoisophthalic acid monosodium salt and 0.5-1.5mmol of 4,4'-dipyridyl in 15-20mL of water and alcohol mixed liquid; and encapsulating in a reactor, heating for 2-4 days, and cooling to room temperature until colorless bulk single crystal is separated. The method preferably comprises the following steps: dissolving 1mmol of Zn(NO3)2.6(H2O), 1mmol of 5-sulfoisophthalic acid monosodium salt and 1mmol of 4,4'-dipyridyl in 20mL of water and alcohol mixed liquid; and encapsulating in the reactor, heating for 3 days, and cooling to room temperature until the colorless bulk single crystal is separated. Compared with the prior art, the coordination polymer material has excellent thermal stability and stable diamagnetic property, and has fluorescent emission property.

Description

technical field [0001] The invention relates to the field of magnetic properties and materials, in particular to a preparation method of a diamagnetic chain coordination polymer. Background technique [0002] Existing studies on the magnetic properties of complexes mainly focus on ferromagnetic and antiferromagnetic transition metals and some elements in rare earth metals, and mainly test the magnetic susceptibility curve of the complexes with temperature. When the temperature drops to the Curie temperature Finally, the complexes show ferromagnetic or antiferromagnetic coupling effects, and these aspects of research are more common. However, in the prior art, there is a lack of research on materials whose magnetic properties are controlled by temperature, especially the research on complex materials whose structures are not destroyed even when the temperature reaches 200°C. Contents of the invention [0003] The purpose of the present invention is to establish a material ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/06C08G83/00
CPCC08G83/008C09K11/06C09K2211/188
Inventor 关磊王莹
Owner LIAONING UNIVERSITY OF PETROLEUM AND CHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com