Quantum dot optical thin film without barrier film and preparation method thereof

An optical film and quantum dot technology, applied in instruments, identification devices, etc., can solve the problems of poor waterproof and oxygen resistance, increase the cost of optical films, low light transmittance, etc., achieve excellent waterproof and anti-oxidation performance, and reduce material costs. , The effect of improving light transmittance

Inactive Publication Date: 2018-02-23
HUIZHOU KINGBALI TECH
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current backlight display quantum dot optical film uses two layers of barrier film to coat the quantum dot colloid solution, which increases the cost of the optical film, and its light transmittance is low, and its waterproof and oxygen performance is not excellent. a difficulty of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quantum dot optical thin film without barrier film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A number of implementations of the present application will be disclosed below, and for the sake of clarity, many practical details will be described together in the following description. It should be understood, however, that these practical details should not be used to limit the application. That is to say, in some embodiments of the present application, these practical details are unnecessary.

[0021] In addition, the technical solutions of the various embodiments can be combined with each other, but it must be based on the realization of those skilled in the art. When the combination of technical solutions is contradictory or cannot be realized, it should be considered that the combination of technical solutions does not exist , nor within the scope of protection required by the present invention.

[0022] The quantum dot optical film without a barrier film of the present application includes a body, the body is solidified into a film by a quantum dot colloid so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a quantum dot optical thin film without a barrier film and a preparation method thereof. The quantum dot optical thin film comprises a body which prepared by curing a quantumdot colloid solution to form a film. The quantum dot colloid solution comprises, by weight, 0.5 part of a quantum dot solution and a resin solution, wherein the quantum dot solution has a concentration of 15 mg / L; the resin solution comprises, by weight, 10 parts of organic resin, 100 to 400 parts of a diluent and 0.1 part of an auxiliary agent; and the above components are mixed in proportion toprepare the quantum dot colloid solution which is then naturally dried in the air for film formation. According to the quantum dot optical thin film of the invention, quantum dots are wrapped by organic resin in virtue of the film forming property of the organic resin, and supporting with a substrate and protection via a barrier film are not needed; after the quantum dot optical thin film is formed after curing, the quantum dot optical thin film can be directly used and has excellent water and oxidation resistance and improved light transmittance; and the preparation method is simplified and material cost is reduced.

Description

technical field [0001] The invention relates to the technical field of quantum dot optical films, in particular to a quantum dot optical film without a barrier film and a preparation method thereof. Background technique [0002] Display technology has developed to today, from monochrome to color, from fuzzy to clear, from small to large, after countless changes, the production technology of the display is constantly improving and perfecting, so that its products can adapt to the ever-changing consumption of consumers Psychology and consumer behavior. [0003] At present, quantum dot optical films are applied in display technology. Quantum dots are semiconductor nanocrystals, which can accurately transport light when used in display technology, have an efficient display color gamut value, make the color more pure and vivid, and make the color performance more tense. [0004] Quantum dot optical film is prepared by making quantum dot colloidal solution. The preparation of q...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J5/18C08L33/12C08L69/00C08L27/06G09F9/00
CPCC08J5/18C08J2327/06C08J2333/12C08J2369/00G09F9/00
Inventor 张彦兵张立强张力广
Owner HUIZHOU KINGBALI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com