Grinding wheel applied to liquid crystal glass chamfering and manufacturing method thereof

A technology of liquid crystal glass and grinding wheel, which is applied in the field of ultra-precision processing of substrate substrates, can solve the problems of large chipping, product scrapping, fragmentation, etc., and achieve the effect of reducing strength and good holding force

Active Publication Date: 2018-02-27
ZHENGZHOU RES INST FOR ABRASIVES & GRINDING CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And it is easy to break during processing, especially when processing its corners, it is prone to chipping and fragmentation, so that the entire product is scrapped
Low prod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Grinding wheel applied to liquid crystal glass chamfering and manufacturing method thereof
  • Grinding wheel applied to liquid crystal glass chamfering and manufacturing method thereof
  • Grinding wheel applied to liquid crystal glass chamfering and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0036] Example 1

[0037] A preparation method of a grinding wheel applied to liquid crystal glass chamfering, comprising the following steps:

[0038] (1) Coarse grinding layer binder configuration: the binder consists of 10wt% Sn-Cu alloy powder (the mass ratio of Sn and Cu is 34.5:65.5), and 80wt% Ag-Ni alloy powder (the mass ratio of Ag and Ni is 34.5:65.5). 37:63), 10wt% paraffin composition. Weigh the raw materials of the binder in proportion, mix well, and then weigh the 80-mesh diamond and the mixed binder according to the mass ratio of diamond and binder of 1:5. Mix the mixture of diamond and binder with absolute ethanol according to the mass ratio of 1:8, stir for 30 minutes, the stirring speed is 1200rpm / min, and finally put it in an oven at 90 ° C for 4 hours to dry, and pass through a 140-mesh sieve Get a mix.

[0039] (2) Put the mixture in step (1) into a graphite mold of the corresponding size, and press it into a rough grinding layer under the pressure of 2MP...

Example Embodiment

[0043] Example 2

[0044] A preparation method of a grinding wheel applied to liquid crystal glass chamfering, comprising the following steps:

[0045] (1) Coarse grinding layer binder configuration: the binder consists of 30wt% Sn-Cu alloy powder (the mass ratio of Sn and Cu is 42:58), and 60wt% Ag-Ni alloy powder (the mass ratio of Ag and Ni is 42:58). 22:78), 10wt% paraffin composition. Weigh the raw materials of the binder in proportion, mix well, and then weigh the 120-mesh diamond and the mixed binder according to the mass ratio of diamond and binder of 1:10. Put the diamond and binder into the mixture of diamond and binder and anhydrous ethanol according to the mass ratio of 1:9, stir for 50 minutes, the stirring speed is 1200rpm / min, and finally put it in an oven at 120 ℃ Dry for 2 hours, and sieve through 140 mesh to obtain a mixture.

[0046] (2) Put the mixture in step (1) into a graphite mold of corresponding size, and press it into a rough grinding layer under ...

Example Embodiment

[0050] Example 3

[0051] A preparation method of a grinding wheel applied to liquid crystal glass chamfering, comprising the following steps:

[0052] (1) Coarse grinding layer binder configuration: the binder is composed of 15wt% Sn-Cu alloy powder (the mass ratio of Sn and Cu is 33:67), and 60wt% Ag-Ni alloy powder (the mass ratio of Ag-Ni is 33:67). 20:80), 25wt% paraffin composition. Weigh the raw materials of the binder in proportion, mix well, and then weigh the diamond and the mixed binder according to the mass ratio of 140 mesh diamond and binder of 1:8. Put the diamond and the binder into absolute ethanol, stir for 40 minutes at a stirring speed of 1200 rpm / min, and finally put them in an oven at 100 ° C for 3 hours to dry, and sieve 120 mesh to obtain a mixture.

[0053] (2) Put the mixture into a graphite mold of the corresponding size, under the pressure of 6MPa, keep it at 45℃ for 30min, 200℃ for 20min, 400℃ for 15min, 650℃ for 20min, and press it into a rough ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a grinding wheel applied to liquid crystal glass chamfering and a manufacturing method thereof, and belongs to the technical field of substrate ultra-precise machining. The grinding wheel applied to liquid crystal glass chamfering comprises a grinding wheel base body and a grinding wheel grinding layer. The grinding wheel base body can be processed from stainless steel, hard alloy, aviation aluminum and the like according to certain shape dimension. The grinding wheel grinding layer is divided into two parts, wherein one part is a coarse grinding layer and the other part is a fine grinding layer. The coarse grinding layer is used for removing chamfering margin, is sharp, is high in processing efficiency, and can achieve the processing dimension which meets the requirements; and the fine grinding layer is used for removing and polishing coarsely grinded grains and cracks after the coarse grinding layer works, so that the purposes of being free of cracks and freeof macroscopic grains are achieved.

Description

technical field [0001] The invention belongs to the field of ultra-precision processing of substrates, and in particular relates to a grinding wheel applied to liquid crystal glass chamfering and a preparation method thereof. Background technique [0002] Liquid crystal glass is a high-tech optoelectronic glass product made of liquid crystal film through high temperature and high pressure, interlayer packaging. Users can control the arrangement of liquid crystal molecules through the current energization or not, so as to control the transparent and opaque state of the glass. ultimate purpose. The liquid crystal film in the middle layer is used as the functional material of the dimming glass. The application principle is: the liquid crystal molecules are arranged in a straight line when the power is on, and the liquid crystal glass is light-transmitting and transparent; when the power is off, the liquid crystal molecules are in a scattering state, and the liquid crystal film...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B24D3/06B24D3/28B24D3/34B24D7/14B24D18/00
CPCB24D3/06B24D3/28B24D3/342B24D3/344B24D7/14B24D18/0009
Inventor 叶腾飞
Owner ZHENGZHOU RES INST FOR ABRASIVES & GRINDING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap