Formula of nylon composite material

A nylon composite material and formula technology, applied in the field of nylon composite material formula, can solve problems such as affecting long-term life, affecting luminous efficiency, and affecting performance of LED lamp life, so as to achieve a good effect of modifying the face shape

Inactive Publication Date: 2018-04-20
李颂
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The heat dissipation of LED lights is now more and more valued by people. This is because the light decay or life of LED lights is directly related to its junction temperature. If the heat dissipation is not good, the junction temperature will be high and the life will be short. According to the Arrhenius law Every time the temperature drops by 10°C, the life will be extended by 2 times. From the relationship between light decay and junction temperature released by Cree, it can be seen that if the junction temperature can be controlled at 65°C, then the life of light decay to 70% can be as high as 100,000 hours ; but the heat dissipation of the existing actual LED lamps is far from reaching the required temperature, so that the life of the LED lamps has become a major problem affecting its performance. Moreover, the junction temperature not only affects the long-term life, but also directly affects Short-term luminous efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] A formula of nylon composite material, the raw materials in the formula are composed by weight percentage: 5% carbon fiber, 1% carbon nanotube, 1% processing aid, 5% polyamide, 3% bifunctional toughening agent, ethyl alcohol 2% ethylene bis stearamide, 1% modified ethylene bis stearamide, 11% antioxidant, 5% hemp fiber, 3% wood fiber, 3% plastic material, 1% unsaturated polyester resin, glass fiber 5%, infrared blocking agent 1%, titanium dioxide 4%, zinc stearate 2%, at this time, the effects of nylon composite materials modifying the face shape, sunscreen and skin care are insufficient.

Embodiment 2

[0009] A kind of prescription of nylon composite material, the raw material in the prescription is composed respectively by weight percentage: carbon fiber 15%, carbon nanotube 5%, processing aid 10%, polyamide 15%, bifunctional toughening agent 9%, ethyl alcohol 3% ethylene bis stearamide, 5% modified ethylene bis stearamide, 19% antioxidant, 7% hemp fiber, 5% wood fiber, 5% plastic material, 5% unsaturated polyester resin, glass fiber 10%, infrared blocking agent 1.5%, titanium dioxide 5%, and zinc stearate 4%. At this time, the effect of modifying the face shape and sunscreen and skin care of the nylon composite material is not obvious.

Embodiment 3

[0011] A formula of nylon composite material, the raw materials in the formula are composed by weight percentage: 10% of carbon fiber, 3% of carbon nanotube, 6% of processing aid, 10% of polyamide, 6% of bifunctional toughening agent, and 2.3% ethylene bis stearamide, 1.5% modified ethylene bis stearamide, 11.9% antioxidant, 5.7% hemp fiber, 3.5% wood fiber, 3.5% plastic material, 1.5% unsaturated polyester resin, glass fiber 8%, infrared blocking agent 1.28%, titanium dioxide 4.5%, and zinc stearate 2.4%. At this time, the nylon composite material has a good effect of modifying the face shape, sunscreen and skin care.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is a formula of nylon composite material. The raw materials in the formula are composed of 5-15% of carbon fiber, 1-5% of carbon nanotube, 1-10% of processing aid, and 5-15% of polyamide. , Bifunctional toughening agent 3‑9%, ethylene bis stearamide 2‑3%, modified ethylene bis stearamide 1‑5%, antioxidant 11‑19%, hemp fiber 5‑7% , wood fiber 3‑5%, plastic material 3‑5%, unsaturated polyester resin 1‑5%, glass fiber 5‑10%, infrared blocking agent 1‑1.5%, titanium dioxide 4‑5%, zinc stearate 2‑4%, at this time, the nylon composite material has a good effect of modifying the face shape, sun protection and skin care.

Description

technical field [0001] The invention is a formula of nylon composite material. Background technique [0002] The heat dissipation of LED lights is now more and more valued by people. This is because the light decay or life of LED lights is directly related to its junction temperature. If the heat dissipation is not good, the junction temperature will be high and the life will be short. According to the Arrhenius law Every time the temperature drops by 10°C, the life will be extended by 2 times. From the relationship between light decay and junction temperature released by Cree, it can be seen that if the junction temperature can be controlled at 65°C, then the life of light decay to 70% can be as high as 100,000 hours ; but the heat dissipation of the existing actual LED lamps is far from reaching the required temperature, so that the life of the LED lamps has become a major problem affecting its performance. Moreover, the junction temperature not only affects the long-term ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08L1/02C08L97/02C08L67/06C08K13/04C08K7/06C08K7/24C08K5/20C08K7/14
CPCC08L77/00C08K2201/011C08L1/02C08L2205/035C08L2205/16C08L97/02C08L67/06C08K13/04C08K7/06C08K7/24C08K5/20C08K7/14
Inventor 李颂
Owner 李颂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products