Water-soluble nail polish and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A nail polish and water-soluble technology, which is applied in the field of water-soluble nail polish and its preparation, can solve the problems of water-resistant washing, poor adhesion and antibacterial effect, poor weather resistance, and insufficient hardness, and achieve high water resistance and excellent Quick-drying, fine particle size effect
Inactive Publication Date: 2018-07-13
JINHUA MINGSHI TECH
View PDF4 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, its water resistance to washing, adhesion and antibacterial effect are poor, and its retention time is short.
[0006] CN201510672793.6 discloses a cationic water-based acrylate-type environmentally friendly water-based nail polish and a preparation method thereof, wherein: compared with conventional water-based acrylic emulsions, the drying speed of the cationic water-based acrylate resin is slower, the hardness is not high enough, and the cost is slightly lower. High and weather resistance is not very good and so on
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] Example 1: A water-soluble nail polish according to the present invention, its components in parts by weight:
[0033]
[0034]
[0035] After weighing the above ingredients, disperse and mix them at high speed to make a rose-scented red nail polish.
[0036] The nail polish obtained by the invention has no irritating odor, and has no burning, redness and irritation after being tested on human skin and nails. Using existing technology to detect, the nail polish has excellent quick-drying, adhesion, abrasion resistance, water resistance, gloss and anti-stickiness.
Embodiment 2
[0037] Example 2: A water-soluble nail polish according to the present invention, its components in parts by weight:
[0038]
[0039]
[0040] After weighing the above ingredients, disperse and mix at high speed to make white nail polish.
[0041] The nail polish obtained by the invention has no irritating odor, and has no burning, redness and irritation after being tested on human skin and nails. Using existing technology to detect, the nail polish has excellent quick-drying, adhesion, abrasion resistance, water resistance, gloss and anti-stickiness.
Embodiment 3
[0042] Example 3: A water-soluble nail polish according to the present invention, its components in parts by weight:
[0043]
[0044]
[0045] After weighing the above ingredients, disperse and mix them evenly at high speed to make colorful sequined nail polish.
[0046] The nail polish obtained by the invention has no irritating odor, and has no burning, redness and irritation after being tested on human skin and nails. Using existing technology to detect, the nail polish has excellent quick-drying, adhesion, abrasion resistance, water resistance, gloss and anti-stickiness.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides water-soluble nail polish and a preparation method thereof. The water-soluble nail polish comprises a waterborne polyurethane-modified acrylic composite emulsion, a film formingaid, a waterborne wetting dispersant, a waterborne substrate wetting agent, a thickening agent, an adhesion promoter, a pigment, other auxiliaries and water. The preparation method comprises the following steps: adding the waterborne polyurethane-modified acrylic composite emulsion at a rotating speed of 800-900 r / min, adding the film forming aid at a speed of 6-8 L / h, dispersing for 25-30 minutes, then adding the waterborne wetting dispersant and the waterborne substrate wetting agent, continuously dispersing for 10-15 minutes, then adding the pigment, the adhesion promoter and the other auxiliaries, uniformly stirring, adjusting the viscosity with the thickening agent and the balance of water, and filtering and packaging with a 150-mesh filter screen. The water-soluble nail polish provided by the invention uses the waterborne polyurethane-modified acrylic core-shell composite emulsion with a special structure and is fine in particle size, optimal in film-forming property, strong inadhesive force, high in water resistance, high in glossiness and strong in after tackiness resistance.
Description
Technical field [0001] The invention belongs to the technical field of cosmetics, and specifically relates to a water-soluble nail polish and a preparation method thereof. Background technique [0002] Traditional nail polish uses nitrocellulose or other UV-curable resins as the film-forming base material. The former is more harmful to nails and the human body due to the existence of a large amount of organic solvents, and the latter needs to be cured by ultraviolet light to form a film. Harmful and cumbersome nail art process. There are also some patents reporting some water-based nail polish products. [0003] CN200910119825.4 discloses a water-soluble high-hardness antibacterial nail polish applied to the nail beauty industry and a preparation method thereof, and has the characteristics of high hardness, antibacterial, and strong adhesion. However, it is an externally added antibacterial agent, the base material itself is not antibacterial and the water-soluble resin as the fi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more