Preparation method of high-performance, low-halogen, environment-friendly and flame-retardant steel wire rope core conveyer belt

A steel cord core and high-performance technology, which is applied in the field of rubber conveyor belts, can solve problems such as unevenness, rough appearance, and uneven thickness of cover rubber, and achieve the effects of less time consumption, reduced personnel demand, and time saving

Inactive Publication Date: 2018-07-27
XIAN ZHONGZHUANG WEINAN RUBBER PROD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The thickness of the extruded cover rubber is uneven and the appearance is not smooth, uneven, which may cause quality problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-performance, low-halogen, environment-friendly and flame-retardant steel wire rope core conveyer belt
  • Preparation method of high-performance, low-halogen, environment-friendly and flame-retardant steel wire rope core conveyer belt
  • Preparation method of high-performance, low-halogen, environment-friendly and flame-retardant steel wire rope core conveyer belt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The preparation method of a high-performance low-halogen environment-friendly flame-retardant steel cord conveyor belt of the present invention will be specifically described below in conjunction with specific examples.

[0020] The formula of the preparation method of the high-performance low-halogen environment-friendly flame-retardant steel cord conveyor belt consists of the following raw materials in parts by weight: 60.0 parts of styrene-butadiene rubber, 20.0 parts of butadiene rubber, 20.0 parts of standard rubber, 6.0 parts of indirect zinc oxide, 0.8 parts of anti-aging agent RD, 1.5 parts of anti-aging agent 4010NA, 1.5 parts of paraffin, 18.0 parts of 70# chlorinated paraffin, 7.0 parts of antimony trioxide (grade 0), 8.0 parts of ammonium polyphosphate, 30.0 parts of flame retardant WX-01, 12.0 parts of flame retardant WX-02, 15.0 parts of flame retardant WX-03, 1.2 parts of accelerator CZ, 0.6 parts of accelerator DM, 45.0 parts of carbon black N234, 3.0 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a formula of a high-performance, low-halogen, environment-friendly and flame-retardant steel wire rope core conveyer belt. The conveyer belt is prepared from raw materials in parts by weight as follows: 60.0 parts of styrene-butadiene rubber, 20.0 parts of butadiene rubber, 20.0 parts of standard rubber, 6.0 parts of indirect zinc oxide, 0.8 parts of an anti-aging agent RD,1.5 parts of an anti-aging agent 4010NA, 1.5 parts of paraffin, 18.0 parts of 70# chlorinated paraffin, 7.0 parts of antimony trioxide (0 level), 8.0 parts of ammonium polyphosphate, 30.0 parts of aflame retardant WX-01, 12.0 parts of a flame retardant WX-02, 15.0 parts of a flame retardant WX-03, 1.2 parts of an accelerant CZ, 0.6 parts of an accelerant DM, 45.0 parts of carbon black N234 and 3.0 parts of sulfur powder. Cover rubber pressed with the formula has no rubber breakage, rubber rotting or rubber scorching phenomena, discharge cover rubber sheets have flat and smooth surfaces, a good foundation is laid for vulcanization of good finished products in a vulcanization process, manual rubber holding is not required, the labor intensity is greatly reduced, and the worker demand is reduced.

Description

technical field [0001] The invention relates to a rubber conveyor belt, in particular to a preparation method of a high-performance low-halogen environment-friendly flame-retardant steel cord conveyor belt. Background technique [0002] Steel cord flame retardant conveyor belt has good flame retardancy, and is widely used in various industries such as coal mines, power plants, and chemicals. Since neoprene contains a large amount of harmful organic substances, the solvent in neoprene is often emitted into the air during use, and the excessively released harmful gas seriously pollutes the environment. In recent years, many measures have been put forward for environmental protection at home and abroad, and many polluting enterprises have even been shut down because of environmental pollution. Therefore, low-carbon environmental protection and personal health have attracted the attention of all walks of life. Safety, environmental protection and energy saving are inevitable tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L9/00C08L7/00C08L91/06C08K13/02C08K3/22C08K3/32C08K5/47C08K3/04B29B7/00
CPCB29B7/005C08K2003/2296C08K2003/323C08L9/06C08L2201/02C08L2205/035C08L9/00C08L7/00C08L91/06C08K13/02C08K3/22C08K3/32C08K5/47C08K3/04
Inventor 杨化民姜丽马新尚宋洁王军龙杨晓晓
Owner XIAN ZHONGZHUANG WEINAN RUBBER PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com