Preparation method for high-survival cultivation matrix of toona sinensis seedlings
A technology of survival rate and toona sinensis is applied in the field of preparation of cultivation substrates for high survival rate of toona sinensis seedlings.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] A preparation method for cultivating substrate with high survival rate of Chinese toon seedlings, comprising the following steps:
[0018] (1) In parts by weight, add 22 parts of huanghuamin, 19 parts of wood ginger, 10 parts of sunflower disc, 8 parts of cotton root, 5 parts of bamboo root seven, and 2 parts of mahogany into 120 parts of boiling water, stir well , continue to decoct with low heat for 40 minutes, filter to obtain the filtrate, and cool the filtrate to room temperature to obtain a nutrient solution;
[0019] (2) Add bentonite to 6 times its weight in water, stir evenly, and after preparing the suspension, add ammonia water with 30% volume of the suspension into it, stir evenly, heat the mixture to 85°C, and keep it warm for 2 hours Afterwards, modified bentonite is obtained;
[0020] (3) Mix the modified bentonite and the nutrient solution evenly at a mass ratio of 1:1, heat the mixture to 65°C, heat-preserve it for 12 hours, and dry it to prepare the n...
Embodiment 2
[0026] A preparation method for cultivating substrate with high survival rate of Chinese toon seedlings, comprising the following steps:
[0027] (1) In parts by weight, add 24 parts of huanghuaren, 21 parts of wood ginger, 13 parts of sunflower flower disc, 10 parts of cotton root, 7 parts of bamboo root seven, and 4 parts of mahogany into 130 parts of boiling water, stir well , continue to decoct with low heat for 45 minutes, filter to obtain the filtrate, and cool the filtrate to room temperature to obtain a nutrient solution;
[0028] (2) Add bentonite to water that is 7 times its weight, stir evenly, and after preparing the suspension, add ammonia water with 40% of the volume of the suspension, stir evenly, heat the mixture to 88°C, and heat-preserve for 2.5 hours Afterwards, modified bentonite is obtained;
[0029] (3) After mixing the modified bentonite and the nutrient solution evenly according to the mass ratio of 1:2, the mixture was heated to 68°C, heat-preserved f...
Embodiment 3
[0035] A preparation method for cultivating substrate with high survival rate of Chinese toon seedlings, comprising the following steps:
[0036] (1) In parts by weight, add 26 parts of huanghuamin, 24 parts of wood ginger, 15 parts of sunflower flower disc, 12 parts of cotton root, 9 parts of bamboo root seven, and 6 parts of mahogany into 140 parts of boiling water, stir well , continue to decoct with low heat for 50 minutes, filter to obtain the filtrate, and cool the filtrate to room temperature to obtain a nutrient solution;
[0037] (2) Add bentonite to water that is 8 times its weight, stir evenly, and after preparing a suspension, add ammonia water with 50% of the volume of the suspension, stir evenly, heat the mixture to 90°C, and heat-preserve for 3 hours Afterwards, modified bentonite is obtained;
[0038] (3) Mix the modified bentonite and the nutrient solution evenly at a mass ratio of 1:3, heat the mixture to 70°C, heat-preserve for 15 hours, and dry to obtain n...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle size (mesh) | aaaaa | aaaaa |
particle size (mesh) | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com