Bulletproof steel plate for armor and manufacturing method thereof

A manufacturing method and steel plate technology are applied to the bulletproof steel plate for armor and its manufacturing field, which can solve the problems of low elongation and achieve the effects of uniform performance, guarantee of performance uniformity, and improvement of plastic and toughness indexes.

Active Publication Date: 2020-08-14
贝斯山钢(山东)钢板有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] CN102181795A discloses an ultra-high-strength bulletproof steel plate and its manufacturing process. The carbon content is relatively high at 0.3-0.5%, and alloying elements such as Cr, Ni, Mo, V, Ti, and B are added. After quenching treatment, due to the relatively low carbon equivalent High, the yield strength has reached more than 1350MPa, the hardness value is in the range of 480-630HBW according to different thicknesses, but the elongation is lower than 5%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bulletproof steel plate for armor and manufacturing method thereof
  • Bulletproof steel plate for armor and manufacturing method thereof
  • Bulletproof steel plate for armor and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 5

[0060] The difference between Example 5 and Example 1 is that the weight percentage of Cr is 0.7%, and the percentages of other components are the same as in Example 5, and then the steel plate is prepared by using the steel plate preparation method and process parameters provided in Example 5.

Embodiment 6

[0062] The difference between Example 6 and Example 1 is that the component Co is removed, and the percentages of other components are the same as in Example 5, and then the steel plate is prepared by using the preparation method and process parameters of the steel plate provided in Example 5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a bulletproof steel plate for armor and a manufacturing method of the bulletproof steel plate. The bulletproof steel plate for the armor is prepared from, by weight, 0.25-0.38%of C, 0.20-0.40% of Si, 0.22-0.50% of Mn, 0.015% or less of P, 0.005% or less of S, 0.010-0.050% of Alt, 0.10-0.38% of Ni, 0.80-1.50% of Cr, 0.16-0.40% of Mo, 0.010-0.035% of Ti, 0.0050% or less of N,0.00022% or less of H and the balance Fe and inevitable impurities. The manufacturing method of the steel plate comprises a steel making work procedure, a steel rolling work produce and a heat treatment work procedure. The bulletproof steel plate for the armor improves the plastic toughness index while ensuring the strength of the steel plate. The manufacturing method of the bulletproof steel plate for the armor is reasonable in design, the advantages of each control process are fully exerted, the uniformity of the performance of the steel plate is guaranteed, the influence of residual internal stress of the steel plate is effectively eliminated, and the subsequent cutting, welding and other machining properties of the steel plate are improved.

Description

technical field [0001] The invention relates to the technical field of high-strength quenched and tempered steel and its production process, in particular to a bulletproof steel plate for armor and a manufacturing method thereof. The bulletproof steel plate for armor has a Brinell hardness within the range of 480HBW-530HBW. Background technique [0002] Armor protection is the basis for tank armored vehicles to survive on the battlefield. In modern warfare, tank armored vehicles face all kinds of anti-armor weapons such as enemy tank guns, anti-tank missiles, shoulder-mounted anti-tank weapons, anti-tank grenades, improvised explosive devices, electromagnetic weapons, and high-power microwave weapons. Attacks have put forward higher requirements for the protection capabilities of tanks and armored vehicles. Therefore, strengthening armor protection has become a research hotspot in various countries. [0003] The main function of the bulletproof steel plate is to prevent bu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/44C22C38/50C21D8/02C22C33/04
Inventor 彭宾李士安周平王勇谢晖李玲许立清王旭峰姜晓军薄其伟王雅桢
Owner 贝斯山钢(山东)钢板有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products