Fiber preheating device for pultrusion of composite material products and pultrusion preheating method thereof

A composite material and heating method technology, which is applied in the field of fiber heating devices, can solve problems such as product defects, uneven speed fiber heating, etc., and achieve the effects of convenient operation, reasonable structure design, and improved mechanical properties

Active Publication Date: 2019-08-09
ZHONGFU CARBON FIBER CORE CABLE TECH
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adopting the device and preheating method of the present invention can improve production efficiency and solve the problem that in the existing pultrusion molding process, the speed is too fast and the fibers are heated unevenly, which leads to product defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber preheating device for pultrusion of composite material products and pultrusion preheating method thereof
  • Fiber preheating device for pultrusion of composite material products and pultrusion preheating method thereof
  • Fiber preheating device for pultrusion of composite material products and pultrusion preheating method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Such as Figure 1 to Figure 4 , a fiber preheating device for pultruded composite products, which includes a PTFE extruded sheet 1, an electric heating aluminum plate 2 fixed to the PTFE extruded sheet 1 by bolts, and a power plug connected to the electric heating aluminum sheet 2 3. Both the PTFE extruded rubber plate 1 and the electric heating aluminum plate 2 are provided with 50 counterbore holes 7 of equal size, and the small mouth 4 passes through the counterbore holes on the PTFE extruded rubber plate 1 and the electric heating aluminum plate 2; The outer periphery of the PTFE extrusion board 1 is provided with a through hole 5 matched with the pre-cured mold tooling,

[0029] The two sides of the electric heating aluminum plate 2 are respectively provided with temperature measuring holes 6 .

[0030] The pre-curing mold is composed of PTFE extrusion board, small nozzle and electric heating aluminum plate, in which the small nozzle is installed on the correspond...

Embodiment 2

[0032] A fiber heating method for a pultruded composite product, comprising the steps of:

[0033] Step a: Tightly connect the PTFE extrusion board 1 and the electric heating aluminum board 2 with bolts through the screw holes;

[0034] Step b: install small nozzles 4 in sequence on the counterbore corresponding to the PTFE extrusion board 1 and the electric heating aluminum board 2;

[0035] Step c: through the through hole 5 reserved on the PTFE extruded sheet 1, fix the spliced ​​PTFE extruded sheet 1, the electric heating aluminum plate 2 and the small nozzle 4 on the pre-cured mold;

[0036] Step d: Pass the glass fiber through the PTFE extrusion board 1 and the small nozzle 4 on the electric heating aluminum plate 2, plug in the power plug 3 above the electric heating aluminum plate 2 and heat it to 80-140°C;

[0037] Step e: Under the traction of the tractor, the glass fiber passes through the resin glue tank, and then passes through the PTFE extrusion board 1 for extr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a fiber preheating device for pultrusion of composite material products and a pultrusion method thereof. The fiber preheating device for pultrusion of the composite material products comprises a tetrafluoroethylene glue-extruding plate (1), an electrical heating aluminium plate (2) which is connected and fixed to the tetrafluoroethylene glue-extruding plate (1) through bolts and a power supply plug (3) connected with the upper portion of the electrical heating aluminum plate (2). Counter bores of the same number and size are formed in the tetrafluoroethylene glue-extruding plate (1) and the electrical heating aluminum plate (2) correspondingly. Little spouts (4) penetrate through the counter bores in the tetrafluoroethylene glue-extruding plate (1) and the electrical heating aluminum plate (2). Through holes (5) matched with pre-solidifying mold tools are formed in the outer periphery of the tetrafluoroethylene glue-extruding plate (1). Temperature measuring holes are formed in two side faces of the electrical heating aluminum plate (2) respectively. By means of the fiber preheating device for pultrusion of the composite material products, the pultrusion speed in the pultrusion production process can be effectively improved; the device has a great preheating effect on glass fiber pre-impregnated with resin; and meanwhile, the mechanical property of pultrusion composite material products can be improved, and efficiency and benefits of pultrusion production are improved.

Description

technical field [0001] The invention relates to a fiber heating device in the pultrusion process of composite materials and a pultrusion preheating method thereof. [0002] technical background [0003] There are various molding processes for glass fiber reinforced plastics, among which the pultrusion molding process is a process with a high degree of automation. This molding process is continuous production and has high efficiency. It is an important one in the current glass fiber reinforced plastics molding technology. The pultrusion molding process generally uses continuous glass fiber yarns to impregnate the resin, and the cross-sectional shape of the product is formed through the yarn splitting plate and the preformed plate, and then enters the heating mold for curing and molding. The traditional pultrusion method mainly uses molds or pre-curing molds for curing and molding. Because it takes a certain amount of time for the heat of the curing mold to transfer to the fibe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/54B29C70/52
CPCB29C70/52B29C70/528
Inventor 任桂芳徐俊王志伟张春颖王赵雨刘传瑞
Owner ZHONGFU CARBON FIBER CORE CABLE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap