Refining deoxidizing method of low-carbon low-silicon welding wire steel

A low-carbon, low-silicon, welding wire steel technology, applied in the refining field, can solve the problems of continuous casting nozzle blockage, and achieve the effect of solving blockage and reducing subcutaneous bubbles

Active Publication Date: 2020-01-03
SGIS SONGSHAN CO LTD
View PDF10 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the above-mentioned shortcomings of the prior art, the present invention provides a method for refining and deoxidizing low-carbon and low-silicon welding wire steel. By

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The specific steps are: add 2.5kg / t of low-carbon ferromanganese, 2.6kg / t of ferro-aluminum, 1kg / t of silicon-manganese, and 0.004% of Als in the argon station during the tapping process of the converter. According to the content of Als in the argon station sample 0.004%≤0.005%, 1.6-2kg / t of high-alumina refining slag is added to the refining station, and 1.7kg / t of high-alumina refining slag is actually added. The actual silicon content of sample 1 in subsequent refining is 0.017%. When the silicon content of sample 1 is between 0.01-0.02%, 0.15-0.25kg / t of ferrosilicon powder is added, and 0.2kg / t of ferrosilicon powder is actually added. The actual silicon content of refined sample 2 is 0.011%. When the silicon content of sample 2 is between 0.01-0.02%, 0.6-0.8m / t of silicon-barium wire is fed, and 0.8m / t of silicon-barium wire is actually fed. Calcium treatment feeds pure calcium line 1.2-1.5m / t, and actual calcium treatment feeds pure calcium line 1.3m / t. The outg...

Embodiment 2

[0022] The specific steps are as follows: 2.5kg / t of low-carbon ferromanganese, 2.7kg / t of ferro-aluminum, 1kg / t of silicon-manganese, and 0.013% Als content in the argon station are added during the tapping process of the converter. According to the Als content of 0.013% in the argon station sample is between 0.005-0.015%, 1-1.6kg / t of high-alumina refining slag is added to the refining station, and 1.2kg / t of high-alumina refining slag is actually added. The actual silicon content of subsequent refining sample 1 is 0.022%, and no ferrosilicon powder is added when the silicon content of sample 1 is ≥0.02%. The actual silicon content of refining sample 2 is 0.015%. When the silicon content of sample 2 is between 0.01-0.02%, the silicon-barium wire is fed at 0.6-0.8m / t, and the actual silicon-barium wire is fed at 0.6m / t. Calcium treatment feeds pure calcium line 1.2-1.5m / t, and actual calcium treatment feeds pure calcium line 1.3m / t. The outgoing Als content of the molten ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a refining deoxidizing method for low-carbon low-silicon welding wire steel. The method comprises the following specific steps that (1) deoxidizing and alloying are carried out on molten steel in a converter tapping process; and (2) high-aluminum refining slag is added into an LF refining furnace to perform deoxidation on the slag surface according to the content of argonstation Als, and silicon iron powder is add for deoxidation. By optimizing the refining deoxidizing method, the problem that a continuous casting gate is blocked is solved, and skin blowholes of continuous casting blanks are reduced.

Description

technical field [0001] The invention belongs to the technical field of refining methods, and relates to a method for refining and deoxidizing low-carbon and low-silicon welding wire steel. Background technique [0002] When smelting low-carbon and low-silicon welding wire steel, the deoxidation of molten steel is the key to refining control. If the deoxidation is not good during the refining process, water blocking will easily occur during continuous casting and pouring, and serious subcutaneous air bubbles will occur in the billet. [0003] The first is "A Method for LF Refining and Deoxidation of Low Carbon Welding Wire Steel" with the patent application number CN201710197468.8. The molten steel is smelted in a converter and then refined in an LF furnace; a mixture of ferrosilicon powder and carbon powder is used in the LF furnace. Bubble deoxidizer, realize the whole process of small batches and multi-batches to add to the slag surface for diffusion deoxidation through th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21C7/06C21C7/00
CPCC21C7/0006C21C7/0056C21C7/06
Inventor 刘志龙万翔曾令宇刘志明任世岗胡现锋余衍丰余大华赵科邓长付韦乾永王冠
Owner SGIS SONGSHAN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap