A kind of finishing process of moisture-absorbing and sweat-wicking aroma chemical fiber wig

A technology of moisture absorption and perspiration and chemical fiber filaments, which is applied in the field of textile fibers, can solve the problems of wigs, such as difficult odor, low application range, and poor air permeability, etc., achieve good moisture absorption and perspiration performance, solve the problem of sour odor, and enhance the finishing effect Effect

Active Publication Date: 2022-05-17
青岛华瑞美进出口有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Wigs made of real hair have better moisture absorption and air permeability than the other two, but they are expensive and have a lower scope of application
There are two kinds of wigs made of chemical fiber silk and chemical fiber silk mixed with real hair. The price is moderate and the effect is relatively realistic. However, after wearing it, it is not very breathable and has poor moisture absorption and perspiration. If worn for a long time, the scalp will heat up and the scalp metabolism will be accelerated. It makes the scalp sweat more, and it will secrete more oil, which will block the hair follicles and cause some allergic people to have rashes or even hair loss. At the same time, the wig will also produce unpleasant odors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of finishing process of moisture-absorbing and sweat-wicking aroma chemical fiber wig
  • A kind of finishing process of moisture-absorbing and sweat-wicking aroma chemical fiber wig

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] (1) Weigh 1g of polyester silk wig, wash it thoroughly with water, and let it dry naturally.

[0043] (2) Put the polyester silk wig treated in step (1) into 50ml of emulsifier MOA-7 solution (solution concentration is 5g / L) for further cleaning for 90min, after the end, fully wash with water and dry naturally.

[0044] (3) Hydrophilic finishing of polyester silk wigs with cutinase finishing solution: Soak polyester silk wigs in 100 mL of cutinase finishing solution with a concentration of 50 U / mL at 40 ° C and pH = 6, and add 200 mg of flat Add O and continue stirring for 1h.

[0045] (4) Use the dipping method to carry out moisture absorption and perspiration finishing on polyester silk wigs: at 60°C, dip the polyester silk wigs that have been hydrophilically treated in step (3) in 10g / L ZLJ-2 for 15min, and then dry them at 50°C Dry it for 30min.

[0046] (5) Add 0.2 g of rose essential oil, 1.5 g of gelatin and 0.5 g of emulsifier into a beaker, then add 50 mL of ...

Embodiment 2

[0052] (1) Weigh 2g of polyester silk wig, wash it thoroughly with water, and let it dry naturally.

[0053] (2) Put the polyester silk wig treated in step (1) into 80ml of emulsifier MOA-9 solution (concentration of solution is 3g / L) for further cleaning for 100min. After the end, fully wash with water and dry naturally.

[0054] (3) Hydrophilic finishing of polyester silk wigs with cutinase finishing solution: Soak polyester silk wigs in 100 mL of cutinase finishing solution with a concentration of 100 U / mL at 50 ° C and pH = 7, and add 200 mg of flat Add O and continue stirring for 1h.

[0055] (4) Use the dipping method to carry out moisture absorption and perspiration finishing on polyester silk wigs: at 70°C, dip the polyester silk wigs that have been hydrophilically treated in step (3) in 15g / L ZLJ-6 for 20min, and then dry them at 60°C Dry it for 20min.

[0056] (5) Add 0.4 g of rose essential oil, 1.6 g of gelatin and 0.55 g of emulsifier into a beaker, then add 80 ...

Embodiment 3

[0061] (1) Weigh 5g of polyester wig, wash it thoroughly with water, and let it dry naturally.

[0062] (2) Put the polyester silk wig treated in step (1) into 100ml of emulsifier MOA-15 ​​solution (solution concentration is 8g / L) for further cleaning for 120min, after the end, fully wash with water and dry naturally.

[0063] (3) Hydrophilic finishing of polyester silk wigs with cutinase finishing solution: Soak polyester silk wigs in 100 mL of cutinase finishing solution with a concentration of 150 U / mL at 60 ° C and pH = 8, and add 200 mg of flat Add O and continue stirring for 1h.

[0064] (4) Use the dipping method to carry out moisture absorption and perspiration finishing on polyester silk wigs: at 80°C, immerse the polyester silk wigs that have been hydrophilically treated in step (3) in 20g / L ZLJ-9 for 25min, and then dry them at 70°C Dry it for 15 minutes.

[0065] (5) Add 0.6 g of rose essential oil, 1.7 g of gelatin and 0.6 g of emulsifier into a beaker, then add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of textile fibers, and discloses a finishing process for moisture-absorbing and sweat-wicking aromatic chemical fiber wigs, which includes: cleaning the chemical fiber wigs with a detergent, washing and drying them with water, and then immersing them in a cutinase finishing solution for hydrophilic finishing , and then soaked in the moisture-wicking finishing agent for moisture-wicking finishing; adding the microcapsule fragrance to the capsule wall liquid to obtain a microcapsule suspension; finally adding a cross-linking agent to the microcapsule suspension and putting the moisture-wicking After finishing, the chemical fiber silk wig is dipped in it for aroma finishing. The chemical fiber silk wig obtained by the finishing process of the invention has excellent moisture absorption and perspiration performance and good fragrance persistence.

Description

technical field [0001] The invention relates to the field of textile fibers, in particular to a finishing process for moisture-absorbing and sweat-wicking aromatic fibrous wigs. Background technique [0002] At present, the materials of wigs mainly include chemical fiber silk, chemical fiber silk mixed with real hair, and real hair. The hygroscopicity and breathability of wigs made of real hair are better than the other two, but they are expensive and have a lower scope of application. There are two kinds of wigs made of chemical fiber silk and chemical fiber silk mixed with real hair. The price is moderate and the effect is relatively realistic. However, after wearing it, it is not very breathable and has poor moisture absorption and perspiration. If worn for a long time, the scalp will heat up and the scalp metabolism will be accelerated. It will increase the amount of scalp sweating and secrete more oil, which will block the hair follicles and cause rashes and even hair ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M16/00D06M13/256D06M13/41D06M15/55D06M23/12D06M15/03D06M13/00D06M15/15D06M15/568A41G3/00D06M101/32
CPCD06M16/003D06M13/256D06M13/41D06M15/55D06M23/12D06M15/03D06M16/00D06M13/00D06M15/15D06M15/568A41G3/0091D06M2101/32
Inventor 毛庆辉郑琳娟张毓陈春升王伟郁佳张莉
Owner 青岛华瑞美进出口有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap