High-hardness high-strength high-transparency microcrystalline glass and preparation method and application thereof

A glass-ceramic, high-transparency technology, used in telephone communications, electrical components, telephone structures, etc., can solve the problem of low melting point, high hardness, high strength, and the melting point of glass-ceramic cannot be processed to form wear-resistant glass glaze and mobile phone panels. and other problems, to achieve the effect of excellent molding processing performance, smooth glazed surface without bubbles, suitable size and uniformity

Inactive Publication Date: 2020-03-06
赵国祥
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that the glass-ceramic in the prior art cannot be processed and formed to prepare wear-resistant glass glaze and mobile phone panel due to its high melting point, and to provide a glass-ceramic with high hardness, high strength and high transparency and a low melting point. Its formulation and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A method for preparing glass ceramics with high hardness, high strength and high transparency, the specific steps are as follows:

[0032] (1) casting the mixture into glass, wherein the casting process is as follows: melting the mixture at a temperature of 1615°C for 8.5 hours and then casting; the components and contents of the mixture are shown in Table 1;

[0033](2) After the crystallization treatment, annealing treatment is carried out to obtain the high hardness, high strength and high transparency glass-ceramic, wherein the crystallization treatment is divided into two stages, the temperature of the first stage is 672°C, The time is 4.9h; the temperature of the second stage is 941°C, and the time is 2.3h; the temperature of annealing treatment is 682°C, and the time is 4.7h;

[0034] The prepared glass ceramics with high hardness, high strength and high transparency are composed of a glass matrix and spodumene crystals dispersed in dendritic distribution, spinel...

Embodiment 2

[0038] A method for preparing glass ceramics with high hardness, high strength and high transparency, the specific steps are as follows:

[0039] (1) casting the mixture into glass, wherein the casting process is as follows: melting the mixture for 9 hours at a temperature of 1600° C. and then casting; the components and contents of the mixture are shown in Table 1;

[0040] (2) After the crystallization treatment, annealing treatment is carried out to obtain the high hardness, high strength and high transparency glass-ceramic, wherein the crystallization treatment is divided into two stages, the temperature of the first stage is 680°C, The time is 3.9h; the temperature of the second stage is 947°C and the time is 2.1h; the temperature of annealing treatment is 685°C and the time is 4.3h;

[0041] The prepared glass ceramics with high hardness, high strength and high transparency are composed of a glass matrix and spodumene crystals dispersed in dendritic distribution, spinel ...

Embodiment 3

[0045] A method for preparing glass ceramics with high hardness, high strength and high transparency, the specific steps are as follows:

[0046] (1) Casting the mixture into glass, wherein the casting process is as follows: melting the mixture at a temperature of 1610°C for 8.8 hours and then casting; the components and contents of the mixture are shown in Table 1;

[0047] (2) After the crystallization treatment, annealing treatment is carried out to obtain the high hardness, high strength and high transparency glass-ceramic, wherein the crystallization treatment is divided into two stages, the temperature of the first stage is 675°C, The time is 4.8h; the temperature of the second stage is 950°C, and the time is 2h; the temperature of annealing treatment is 681°C, and the time is 4.8h;

[0048] The prepared glass ceramics with high hardness, high strength and high transparency are composed of a glass matrix and spodumene crystals dispersed in dendritic distribution, spinel ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
densityaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to high-hardness high-strength high-transparency microcrystalline glass and a preparation method and application thereof. The preparation method comprises the following steps: casting a mixture into glass, and carrying out crystallization treatment to obtain the microcrystalline glass, wherein the mixture mainly comprises Li2O, A2lO3, SiO2, CaO, SrO, ZnO, BaO, K2O, Na2O, ZrO2, Sb2O3 and NaCl; and the prepared microcrystalline glass is mainly composed of a glass matrix, spodumene crystals dispersed in the glass matrix and distributed in a dendritic manner, spinel crystalsdistributed in a granular manner and cubic zirconium oxide crystals distributed in a granular manner, and can be applied to preparation of high-strength wear-resistant transparent microcrystalline glass glaze and to preparation of mobile phone panels. The preparation method of the high-hardness high-strength high-transparency microcrystalline glass is simple and easy to implement, and has extremely high popularization value; and the prepared microcrystalline glass has the advantages of a low melting point, excellent forming processability and good application prospects.

Description

technical field [0001] The invention belongs to the technical field of glass-ceramics, and relates to a glass-ceramic with high hardness, high strength and high transparency, its preparation method and application. Background technique [0002] There are many types of glass-ceramics, and glass products with different uses can be produced by different composition ratios and different processes. Most of the glass-ceramics disclosed in the prior art are architectural decorative materials, biological materials, craft products or small heating products, etc. The glass-ceramics used in the above products in the prior art usually have high strength and hardness, but there is a common problem that the high melting point cannot be processed and formed to prepare wear-resistant glass glazes and mobile phone panels. [0003] Therefore, it is of great significance to study a glass-ceramic with high hardness, high strength and high transparency that can be processed and formed to prepar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/12C03B32/02C03B25/00C03C8/06H04M1/02H04M1/18
CPCC03B25/00C03B32/02C03C8/06C03C10/0009H04M1/026H04M1/185
Inventor 赵天佑赵国祥赵成玉吴非
Owner 赵国祥
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap