A method for improving the quality and yield of flaky barium titanate template

A technology of flaky barium titanate and barium titanate, which is applied in the direction of titanate, alkaline earth metal titanate, chemical instruments and methods, etc., can solve the problems of low product quality and low output, achieve short reaction time, improve The effect of quality and yield, slight degree of corrosion

Active Publication Date: 2021-09-07
SHAANXI COAL & CHEM TECH INST
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a method for improving the quality and yield of the flaky barium titanate template, which solves the defects of low quality and low yield of the products produced by the existing flaky barium titanate powder preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for improving the quality and yield of flaky barium titanate template
  • A method for improving the quality and yield of flaky barium titanate template
  • A method for improving the quality and yield of flaky barium titanate template

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] A method for improving the quality and yield of a sheet barium titanate template provided by the present embodiment comprises the following steps:

[0061] Step 1: Weigh a certain mass of Bi according to the stoichiometric ratio 2 O 3 (99.9% purity) and TiO 2 (purity 99.99%), in addition, take a certain amount of NaCl (purity 99.9%) and KCl (purity 99.9%), wherein the molar ratio of NaCl and KCl is 1:1, and the mass ratio of molten salt and reactant is 2: 1.

[0062] Step 2, using anhydrous ethanol as a medium, the material is placed in a nylon ball milling tank equipped with zirconia balls for ball milling for 8 hours, wherein the mass specific gravity of the ball material is 2:1, and the ball-milled material is dried at 100 ° C for use.

[0063] In step 3, the dried material is placed in a corundum crucible, and is kept in a high temperature environment of 1150 ° C for 4 hours to carry out the synthesis reaction, and finally Bi is synthesized. 4 Ti 3 O 12 .

[...

Embodiment 2

[0073] A method for improving the quality and yield of a sheet barium titanate template provided by the present embodiment comprises the following steps:

[0074] Step 1: Weigh a certain mass of Bi according to the stoichiometric ratio 2 O 3 (99.9% purity) and TiO 2 (purity 99.99%), in addition weigh a certain amount of NaCl (99.9%) and KCl (purity 99.9%), wherein the molar ratio of NaCl to KCl is 1:1, and the mass ratio of molten salt to reactant is 2:1 .

[0075] Step 2, using anhydrous ethanol as the medium, the material is ball-milled for 8h in a nylon ball-milling tank equipped with zirconia balls, wherein the mass specific gravity of the ball material is 2:1, and the ball-milled material is dried in an oven at 100°C spare.

[0076] In step 3, the dried material is placed in a corundum crucible, and is kept in a high temperature environment of 1150 ° C for 4 hours to carry out the synthesis reaction, and finally Bi is synthesized. 4 Ti 3 O 12 .

[0077] Step 4. We...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to View More

Abstract

A method for improving the quality and output of sheet-shaped barium titanate templates provided by the present invention comprises the following steps: step 1, weighing Bi according to the molar ratio of 1:(3-15) 4 Ti 3 o 12 Powder and BaCO 3 The powders are mixed to prepare a mixture containing barium titanate products; step 2, the obtained mixture containing barium titanate products is sequentially washed with deionized water, dilute hydrochloric acid, concentrated ammonium salt, and deionized water until the obtained No Ba in the product 2+ ; Step 3, drying the product obtained in step 2, then adding organic reagents to carry out stirring and cleaning to remove bismuth salts, then drying to finally obtain pure flaky BaTiO 3 powder; the method of the present invention can not only ensure that the flaky barium titanate powder is not subject to corrosion and maintain the original shape, but also can effectively increase the output of the barium titanate powder.

Description

technical field [0001] The invention belongs to the field of electronic materials and devices, and particularly relates to a preparation method for improving the quality and yield of flake barium titanate powder. Background technique [0002] In recent years, in order to meet the development needs of equipment miniaturization and light weight, it has become an inevitable development trend to improve the piezoelectric properties of ceramics by textured ceramics. The methods of piezoelectric ceramic texture generally include heat treatment technology, template grain growth method and reaction template grain growth method, multilayer grain growth method, directional solidification method and non-equiaxed particle orientation solidification method. At present, the more mature method of ceramic texture is the template grain growth method. Barium titanate is recognized as an ideal texture template because of its obvious advantages. [0003] The current method for preparing flaky...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G23/00
CPCC01G23/006C01P2002/72C01P2004/03C01P2004/20
Inventor 王明文李飞杨帅周文龙李景雷徐卓
Owner SHAANXI COAL & CHEM TECH INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com